RESUMO
Nuclear resonant reflectivity (NRR) from an Fe60Al40 film was measured using synchrotron radiation at several grazing angles near the critical angle of total external reflection. Using laterally resolved measurements after irradiation with 20â keV Ne+ ions of gradually varying fluence of 0-3.0â ×â 1014â ionsâ cm-2, the progressive creation of the ferromagnetic A2 phase with increasing ion fluence was confirmed. The observed depth selectivity of the method has been explained by application of the standing wave approach. From the time spectra of the nuclear resonant scattering in several reflection directions the depth profiles for different hyperfine fields were extracted. The results show that the highest magnetic hyperfine fields (â¼18-23â T) are initially created in the central part of the film and partially at the bottom interface with the SiO2 substrate. The evolution of the ferromagnetic onset, commencing at a fixed depth within the film and propagating towards the interfaces, has been directly observed. At higher fluence (3.0â ×â 1014â ionsâ cm-2) the depth distribution of the ferromagnetic fractions became more homogeneous across the film depth, in accordance with previous results.
RESUMO
Mössbauer reflectivity spectra and nuclear resonance reflectivity (NRR) curves have been measured using the Synchrotron Mössbauer Source (SMS) for a [57Fe/Cr]30 periodic multilayer, characterized by the antiferromagnetic interlayer coupling between adjacent 57Fe layers. Specific features of the Mössbauer reflectivity spectra measured with π-polarized radiation of the SMS near the critical angle and at the `magnetic' maximum on the NRR curve are analyzed. The variation of the ratio of lines in the Mössbauer reflectivity spectra and the change of the intensity of the `magnetic' maximum under an applied external field has been used to reveal the transformation of the magnetic alignment in the investigated multilayer.