On Curie temperature of B20-MnSi films.

B20-type MnSi is the prototype magnetic skyrmion material. Thin films of MnSi show a higher Curie temperature than their bulk counterpart. However, it is not yet clear what mechanism leads to the increase of the Curie temperature. In this work, we grow MnSi films on Si(100) and Si(111) substrates with a broad variation in their structures. By controlling the Mn thickness and annealing parameters, the pure MnSi phase of polycrystalline and textured nature as well as the mixed phase of MnSi and MnSi1.7 are obtained. Surprisingly, all these MnSi films show an increased Curie temperature of up to around 43 K. The Curie temperature is likely independent of the structural parameters within our accessibility including the film thickness above a threshold, strain, cell volume and the mixture with MnSi1.7. However, a pronounced phonon softening is observed for all samples, which can tentatively be attributed to slight Mn excess from stoichiometry, leading to the increased Curie temperature.

Formation of Thin NiGe Films by Magnetron Sputtering and Flash Lamp Annealing.

The nickel monogermanide (NiGe) phase is known for its electrical properties such as low ohmic and low contact resistance in group-IV-based electronics. In this work, thin films of nickel germanides (Ni-Ge) were formed by magnetron sputtering followed by flash lamp annealing (FLA). The formation of NiGe was investigated on three types of substrates: on amorphous (a-Ge) as well as polycrystalline Ge (poly-Ge) and on monocrystalline (100)-Ge (c-Ge) wafers. Substrate and NiGe structure characterization was performed by Raman, TEM, and XRD analyses. Hall Effect and four-point-probe measurements were used to characterize the films electrically. NiGe layers were successfully formed on different Ge substrates using 3-ms FLA. Electrical as well as XRD and TEM measurements are revealing the formation of Ni-rich hexagonal and cubic phases at lower temperatures accompanied by the formation of the low-resistivity orthorhombic NiGe phase. At higher annealing temperatures, Ni-rich phases are transforming into NiGe, as long as the supply of Ge is ensured. NiGe layer formation on a-Ge is accompanied by metal-induced crystallization and its elevated electrical resistivity compared with that of poly-Ge and c-Ge substrates. Specific resistivities for 30 nm Ni on Ge were determined to be 13.5 µΩ·cm for poly-Ge, 14.6 µΩ·cm for c-Ge, and 20.1 µΩ·cm for a-Ge.