RESUMO
The effect of primary amino acid sequence in recombinant spidroins on their spatial organization is crucial for the fabrication of artificial fibers and fibrous materials. This study focuses on the rheological properties of aqueous and alcoholic solutions of recombinant analogs of natural spidroins (rS1/9 and rS2/12), as well as the structure of their films and nanofibrous materials. Non-Newtonian flow behavior of aqueous solutions of these proteins was observed at certain concentrations in contrast to their solutions in hexafluoroisopropanol. The secondary structure of recombinant spidroins was addressed by IR spectroscopy, whereas their self-organization in various solvents was studied by AFM and cryo-TEM. The influence of the solvent on the structure and properties of the films and nanofibrous materials produced by electrospinning has been established.
RESUMO
Magnetic levitational bioassembly of three-dimensional (3D) tissue constructs represents a rapidly emerging scaffold- and label-free approach and alternative conceptual advance in tissue engineering. The magnetic bioassembler has been designed, developed, and certified for life space research. To the best of our knowledge, 3D tissue constructs have been biofabricated for the first time in space under microgravity from tissue spheroids consisting of human chondrocytes. Bioassembly and sequential tissue spheroid fusion presented a good agreement with developed predictive mathematical models and computer simulations. Tissue constructs demonstrated good viability and advanced stages of tissue spheroid fusion process. Thus, our data strongly suggest that scaffold-free formative biofabrication using magnetic fields is a feasible alternative to traditional scaffold-based approaches, hinting a new perspective avenue of research that could significantly advance tissue engineering. Magnetic levitational bioassembly in space can also advance space life science and space regenerative medicine.
RESUMO
Collagen is one of the most promising materials for 3D bioprinting because of its distinguished biocompatibility. Cell-laden constructs made of pure collagen with or without incorporated growth supplements support engineered constructs persistence in culture and are perfectly suitable for grafting. The limiting factor for direct 3D collagen printing was poor printability of collagen solutions, especially admixed with cells or tissue spheroids. In our study, we showed that concentrated solutions of native collagen branded Viscoll were effective as bioinks with high fidelity performance. Viscoll containing 20, 30, or 40 mg/ml collagen were used for direct extrusion 3D bioprinting to form scaffolds appropriate to support spatial arrangement of tissue spheroids into rigid patterns with resolution of 0.5 mm in details. Incorporated cells demonstrated sufficient viability. Associated rheological study showed that good printability of the collagen solutions correlates with their increased storage modulus value, notably exceeding the loss modulus value. The proper combination of these physical parameters could become technological criteria for manufacturing various collagen bioinks for 3D bioprinting.