RESUMO
The improved synthesis of thieno[3,4-c]pyrrole-4,6-dione (TPD) monomers, including Gewald thiophene ring formation, a Sandmeyer-type reaction, and neat condensation with an amine, is presented. This protocol enables faster, cheaper, and more efficient preparation of TPD units in comparison to traditional methods. Furthermore, a series of TPD homo- and pseudohomopolymers bearing various alkyl chains was synthesized via a direct heteroarylation polymerization (DHAP) procedure. UV-visible absorption and powder X-ray diffraction measurements revealed the relationship between the ratio of branched to linear alkyl chains and the optoelectronic properties of the polymers as well as their packing in the solid state.
RESUMO
An efficient route for the synthesis of 1-iodo-5-octyl-4H-thieno[3,4-c]pyrrole-4,6(5H)-dione as a key intermediate to build new electron-deficient monomers and related conjugated polymers is reported. Along these lines, two new low bandgap copolymers were synthesized from Stille or Suzuki coupling. These polymers were characterized and their properties compared to those of analogous conjugated polymers.
RESUMO
A new low-band-gap thieno[3,4-c]pyrrole-4,6-dione-based copolymer, PBDTTPD, has been designed and synthesized. PBDTTPD is soluble in chloroform or o-dichlorobenzene upon heating and shows a broad absorption in the visible region. The HOMO and LUMO energy levels were estimated to be at -5.56 and -3.75 eV, respectively. These electrochemical measurements fit well with an optical bandgap of 1.8 eV. When blended with PC(71)BM, this polymer demonstrated a power conversion efficiency of 5.5% in a bulk-heterojunction photovoltaic device having an active area of 1.0 cm(2).