The effect of nano hydroxyapatite coating implant surfaces on gene expression and osseointegration.

BACKGROUND: Hierarchical micro-nano structured topography along with surface chemistry modifications of dental implants have been suggested to positively contribute to the osseointegration process. However, the effect of such surface modifications on the molecular response as well as bone formation rate and quality are still unclear, especially in the early healing period. This study aimed to evaluate the effect of coating a double acid etched (DAE) implant surface with nano-sized (20 nm) hydroxyapatite (Nano) with respect to gene expression, histologic parameters, and nanomechanical properties when compared to DAE control at 1 and 2 weeks after implant placement in a rodent femur model. MATERIAL AND METHODS: Expression of bone-related genes was determined by qRT-PCR (Col-I, Runx-2, Osx, Opn, Ocn, Alp). Histomorphometric evaluation of bone-to-implant contact (BIC) and bone area fraction occupancy (BAFO) within implant threads was performed using photomicrographs after histologic processing. Mechanical properties, reduced elastic modulus and hardness, were determined through nanoindentation. RESULTS: At 1 week, the Nano group demonstrated significantly higher expression of Col-I and Ocn compared to the DAE group, indicating upregulation of osteoprogenitor and osteoblast differentiation genes. At 2 weeks, Nano surface further exhibited enhanced gene expression of Col-I and Osx in comparison to the DAE surface, suggesting an increased mineralization of the newly formed bone. Nanoindentation analysis revealed that the Nano group presented no significant difference on the ranks of reduced elastic modulus and hardness compared to DAE for both timepoints. Histomorphometric analysis yielded no significant difference in the percentage of BIC and BAFO between the Nano and DAE surfaces at 1 and 2 weeks. However, Nano implants did present a higher mean value, ~50%, of BIC compared to DAE, ~30%, after 2 weeks in vivo. CONCLUSIONS: While no significant differences were observed in the amount and mechanical properties of newly formed bone, Nano surface positively and significantly increased the expression osteogenic genes compared to DAE surface at early healing periods.

Influence of straight versus angulated screw channel titanium bases on failure loads of two-piece ceramic and titanium implants restored with screw-retained monolithic crowns: An in-vitro study.

OBJECTIVE: To analyze the influence of titanium-base (straight [SSC]/angulated-screw-channel [ASC]) on failure-loads and bending-moments of two-piece ceramic and titanium-zirconium implants restored with monolithic-zirconia crowns after fatigue. MATERIALS AND METHODS: Thirty-two anterior monolithic-screw-retained zirconia crowns were divided into four groups (n = 8/group) according to the factors: (1) type of implant material: two-piece titanium-zirconium implant (Ti-Zr; control-group) versus two-piece ceramic implant (CI; test-group) and (2) type of titanium-base: SSC (0° angle) versus ASC (25°). An intact implant was used for field emission gun-scanning electronic microscopy (FEG-SEM) characterization and Raman spectroscopy for phase analyses and residual stress quantification. All samples were exposed to fatigue with thermodynamic loading (1.2-million-cycles, 49 N, 1.6 Hz, 5-55°C) at a 30° angle. Surviving specimens were loaded until failure (SLF) and bending moments were recorded. Failed samples were examined using light microscope and SEM. Statistical analyses included ANOVA and Mann-Whitney U-test. RESULTS: Raman-spectroscopy revealed the presence of residual compressive stresses. FEG-SEM revealed a roughened surface between threads and polished surface at the cervical-collar of the ceramic implant. All samples survived fatigue and were free of complications. Mean bending-moments (±SD) were: Ti-Zr-0: 241 ± 45 N cm, Ti-Zr-25: 303 ± 86 N cm, CI-0: 326 ± 58 N cm, CI-25: 434 ± 71 N cm. Titanium-base and implant-material had significant effects in favor of ASC titanium bases (p = .001) and ceramic-implants (p < .001). Failure analysis after SLF revealed severe fractures in ceramic implants, whereas titanium implants were restricted to plastic deformation. CONCLUSIONS: Ceramic and titanium implants exhibited high reliability after fatigue, with no failures. From a mechanical perspective, titanium bases with ASC can be recommended for both ceramic and titanium implants and are safe for clinical application.

Immediate placement of extra-short implants in refined scapula tip microvascular free flaps: In house virtual planning and surgical technique - Proof of concept.

Scapula tip flaps have been introduced in the literature as an ideal surgical treatment option for large defects in the horizontal plane of the maxilla. This article aims to present a unique step by step protocol for a near total maxillectomy with a pterygoid bone resection and consecutive microvascular reconstruction with a harvested scapula tip flap. The protocol includes immediate placement of extra-short implants in donor bone with the aid of Virtual Surgical Planning (VSP), and an in-house 3D printing of medical 3D models and surgical guides. So far, there has been no presented surgical technique combining immediate implant placement in the scapula region with simultaneous microvascular repair. This technique allows: tumour resection; flap harvesting; extra-short implant placements and reconstruction to be performed in one simultaneous procedure. The technique is presented with illustrations, VSP (presented on videos), radiographs, and surgical findings. We discovered that this refinement of the scapula tip surgery has enabled reconstructive procedures to be performed at the same time as implant placements, providing expedited functional and aesthetic outcomes in selected cases. Moreover, modification of the surgical technique could enhance the competence of the oropharyngeal edge. In conclusion, this new surgical protocol utilizing VSP, 3D models and simultaneous extra-short implant placement provides indispensable advantages for such a complicated surgical procedures, while significantly shortening the duration of surgery.

Impact of implant thread design on insertion torque and osseointegration: a preclinical model.

BACKGROUND: Successful osseointegration of endosteal dental implants has been attributed to implant design, including the macro-, micro- and nano- geometric properties. Based on current literature pertaining to implant design, the resultant cellular and bone healing response is unknown when the thread thickness of the implants is increased, resulting in an increased contact area in implants designed with healing chambers. The aim of this study was to evaluate the effect of two implant designs with different thread profiles on the osseointegration parameters and implant stability at 3- and 6-weeks in vivo using a well-established preclinical dog model. MATERIAL AND METHODS: A total of 48 type V Ti alloy implants were divided in two groups according to their thread design (D1= +0.1x/mm and D2= +0.15x/mm) and placed in an interpolated fashion into the radii of six beagles. Insertion torque was measured at time of placement, radii were extracted for histological processing following 3- and 6-week healing intervals. Histologic and histomorphometric analyses were performed in terms of bone to implant contact (%BIC) and bone area fraction occupancy within implant threads (%BAFO). Statistical analyses were performed through a linear mixed model with fixed factors of time and implant thread design. RESULTS: Surface roughness analysis demonstrated no significant differences in Sa and Sq between D1 and D2 implant designs, which confirmed that both implant designs were homogenous except for their respective thread profiles. For insertion torque, statistically significant lower values were recorded for D1 in comparison to D2 (59.6 ± 11.1 and 78.9 ± 10.1 N⋅cm, respectively). Furthermore, there were no significant differences with respect to histological analysis and histomorphometric parameters, between D1 and D2 at both time points. CONCLUSIONS: Both thread profiles presented equivalent potential to successfully osseointegrate in the osteotomies, with D2 yielding higher mechanical retention upon placement without detrimental bone resorption.

Marginal and Internal Misfit of Occlusal Veneers Made in Resin-matrix Ceramics.

OBJECTIVE: Considering that misfit is a significant predictor of the clinical success of indirect restorations, the objective of this study was to evaluate the marginal and internal misfit of two computer-aided design and manufacturing (CAD/CAM) RMC ceramic materials used as occlusal veneers (OVs) of different thicknesses. METHODS AND MATERIALS: A CAD model of a mandibular first molar was obtained and OV preparations 0.5-, 1.0-, and 1.5-mm thick were modeled and milled in two different materials (n=10/group): resin nanoceramic (RNC) and polymer-infiltrated ceramic network (PICN). Using the same CAD model, tooth preparations were milled in fiber-reinforced epoxy resin (n=20/thickness). The marginal and internal misfit of the restorations was assessed by X-ray microtomography. The measurements of the marginal gap (MG) and absolute marginal discrepancy were performed in two locations on each slice, whereas internal gap (IG) measurements were performed at ten locations on each slice. The data obtained were analyzed using two-way analysis of variance and Tukey post-hoc tests (α=0.05). RESULTS: No significant effect was attributable to the material type or material-thickness interaction for the MG, absolute marginal discrepancy (AMD), or IG (p>0.05). However, the thickness significantly affected the IG of the restorations (p<0.05). CAD/CAM RNC and PICN systems presented similar MG and AMD for OVs 0.5-, 1.0-, and 1.5-mm thick. However, the IG varied between thicknesses.

Bone regeneration at extraction sockets filled with leukocyte-platelet-rich fibrin: An experimental pre-clinical study.

BACKGROUND: We aimed to histomorphometrically evaluate the effects of Leucocyte-Platelet-Rich Fibrin (L-PRF), with and without the combination of a bone grafting material, for alveolar ridge preservation using an in vivo canine model. MATERIAL AND METHODS: Seven dogs (Female Beagles, ~18-month-old) were acquired for the study. L-PRF was prepared from each individual animal by drawing venous blood and spinning them through a centrifuge at 408 RCF-clot (IntrasSpin, Intra-Lock, Boca Raton, FL). L-PRF membranes were obtained from XPression fabrication kit (Biohorizons Implant Systems, Inc., AL, USA). A split mouth approach was adopted with the first molar mesial and distal socket defects treated in an interpolated fashion of the following study groups: 1) Empty socket (negative control); 2) OSS filled defect 3) L-PRF membrane; and 4) Mix of Bio-Oss® with L-PRF. After six weeks, samples were harvested, histologically processed, and evaluated for bone area fraction occupancy (BAFO), vertical/horizontal ridge dimensions (VRD and HRD, respectively), and area of coronal soft tissue infiltration. RESULTS: BAFO was statistically lower for the control group in comparison to all treatment groups. Defects treated with Bio-Oss® were not statistically different then defects treated solely with L-PRF. Collapsed across all groups, L-PRF exhibited higher degrees of BAFO than groups without L-PRF. Defects filled with Bio-Oss® and Bio-Oss® with L-PRF demonstrated greater maintenance of VRD relative to the control group. Collapsed across all groups, Bio-Oss® maintained the VRD and resulted in less area of coronal soft tissue infiltration compared to the empty defect. Soft tissue infiltration observed at the coronal area was not statistically different among defects filled with L-PRF, Bio-Oss®, and Bio-Oss® with L-PRF. CONCLUSIONS: Inclusion of L-PRF to particulate xenograft did not promote additional bone heading at 6 weeks in vivo. However, we noted that L-PRF alone promoted alveolar socket regeneration to levels comparable to particulate xenografts, suggesting its potential utilization for socket preservation.

Failure Load of Monolithic Lithium Disilicate Implant-Supported Single Crowns Bonded to Ti-base Abutments versus to Customized Ceramic Abutments after Fatigue.

PURPOSE: This laboratory study analyzed the influence of retention mode (screw- vs cement retained) and fatigue application on the failure load of monolithic lithium-disilicate (LDS) implant-supported single crowns (ISSC). MATERIAL AND METHODS: A total of 72 samples of monolithic LDS (*Ivoclar Vivadent) ISSC were divided into three groups (n = 24) according to their type of retention mode: Group Ti-CAD: Titanium base (SICvantage CAD/CAM Abutment red (SIC invent AG), screw-retained milled monolithic LDS (IPS e.max CAD*); Group Ti-P: Titanium base (SICvantage CAD/CAM Abutment red), screw-retained pressed monolithic LDS (IPS e.max Press*) and Group Ti-Cust: Titanium base with cemented press LDS (IPS e.max Press*) crown on a LDS (IPS e.max Press*) custom abutment. A mandibular first molar implant-supported single crown model was investigated (Titanium implant: SICvantage-max, SIC invent AG, diameter: 4.2 mm, length: 11.5 mm). Half of each group (n = 12) w​ere exposed to fatigue with cyclic mechanical loading (F = 198 N, 1.2 million cycles) and simultaneous thermocycling (5-55°C). Single load to failure testing was performed, before (Subgroups Ti-CAD, Ti-P, and Ti-Cust) and after (Subgroups Ti-CAD-F, Ti-P-F, and Ti-Cust-F) fatigue. Weibull distribution was used to determine the characteristic strength and Weibull modulus differences between groups. Probability of survival at 900N load was calculated. RESULTS: No samples failed during fatigue. Characteristic strength values were as follow: Ti-CAD: 3259.5N, Ti-CAD-F: 2926N, Ti-P: 2763N, Ti-P-F: 2841N, Ti-Cust: 2789N, Ti-Cust-F: 2194N. Whereas no difference was observed between pressed or milled monolithic crowns cemented to Ti-base, regardless of loading condition, fatigue decreased the characteristic strength of crowns cemented to custom abutments. Probability of survival at 900 N was not significantly different between groups. CONCLUSIONS: Screw-retained pressed or milled monolithic LDS ISSC, cemented directly to Ti-base abutments or LDS crowns cemented to custom ceramic abutments resist physiological chewing forces after simulated 5-year aging in the artificial mouth and presented equally high probability of survival. However, a significant decrease in load to failure was observed in LDS crowns cemented to custom ceramic abutments after fatigue. Prospective clinical trials are needed to confirm the results of this laboratory investigation.

Nanoscale physico-mechanical properties of an aging resistant ZTA composite.

OBJECTIVE: To characterize the effects of aging on the nanomechanical properties and 3D surface topographical parameters of an experimental Zirconia Toughened Alumina (ZTA) composite compared to its respective individual counterpart materials. METHODS: Disk-shaped specimens comprised of three material groups were processed: 1) ZTA 70/30 (70% alumina reinforced with 30% second-generation 3Y-TZP); 2) Zpex (Second-generation 3Y-TZP), and; 3) Al2O3 (High purity Alumina) (n = 10/material, 12 × 1 mm). After synthesis, ceramic powders were pressed, the green-body samples were sintered and polished. Nanoindentation testing was performed to record elastic modulus (E) and hardness (H). Interferometry was utilized to assess 3D surface roughness parameters (Sa, Sq), while X-ray diffraction (XRD) and scanning electron microscope (SEM) assessed the crystalline content and microstructure. All tests were performed before and after simulated aging (134°C, 2.2 bar, 20 h). Statistical analyses were performed using linear mixed-model and least square difference pos-hoc tests (α = 5%). RESULTS: XRD spectra indicated increase of monoclinic peaks for Zpex (~18%) relative to ZTA 70/30 (~2.5%) after aging. Additionally, aging did not affect the surface roughness parameters of ZTA 70/30 and Al2O3, although a significant increase in Sa was recorded for Zpex following aging (~90 nm) (p < 0.001). Al2O3 yielded the highest H and E values (H:21 GPa, E: 254 GPa), followed by ZTA 70/30 (H: 13 GPa, E: 214 GPa) and Zpex (H:11 GPa, E: 167 GPa), all significantly different (p < 0.03). CONCLUSION: ZTA 70/30 and Al2O3 presented high hydrothermal stability with respect to all evaluated variables, where artificial aging significantly increased the monoclinic content and surface roughness of Zpex.

Microstructural, mechanical, and optical characterization of an experimental aging-resistant zirconia-toughened alumina (ZTA) composite.

OBJECTIVE: To evaluate the effect of aging on the microstructural, mechanical, and optical properties of an experimental zirconia-toughened alumina composite with 80%Al2O3 and 20%ZrO2 (ZTA Zpex) compared to a translucent zirconia (Zpex) and Alumina. METHODS: Disc-shaped specimens were obtained by uniaxial and isostatic pressing the synthesized powders (n = 70/material). After sintering and polishing, half of the specimens underwent aging (20 h, 134 °C, 2.2 bar). Crystalline content and microstructure were evaluated using X-ray diffraction and scanning electron microscopy, respectively. Specimens underwent biaxial flexural strength testing to determine the characteristic stress, Weibull modulus, and reliability. Translucency parameter (TP) and Contrast ratio (CR) were calculated to characterize optical properties. RESULTS: ZTA Zpex demonstrated a compact surface with a uniform dispersion of zirconia particles within the alumina matrix, and typical alumina and zirconia crystalline content. ZTA Zpex and alumina exhibited higher CR and lower TP than Zpex. ZTA Zpex and Zpex showed significantly higher characteristic stress relative to alumina. While aging did not affect optical and mechanical properties of ZTA Zpex and alumina, Zpex demonstrated a significant increase in translucency, as well as a in characteristic stress. Alumina reliability was significantly lower than others at 300 MPa, ZTA Zpex and Zpex reliability decreased at 800 MPa, except for aged Zpex. SIGNIFICANCE: While aging did not affect the mechanical nor the optical properties of ZTA Zpex and alumina, it did alter both properties of Zpex. The results encourage further investigations to engineer ZTA as a framework material for long span fixed dental prostheses specially where darkened substrates, such as titanium implant abutments or endodontically treated teeth, demand masking.

Aging resistance of an experimental zirconia-toughened alumina composite for large span dental prostheses: Optical and mechanical characterization.

PURPOSE: To synthesize a zirconia-toughened alumina (ZTA) composite with 85% alumina matrix reinforced by 15% zirconia and to characterize its optical and mechanical properties before and after artificial aging, to be compared with a conventional dental zirconia (3Y-TZP). MATERIAL AND METHODS: After syntheses, ZTA and 3Y-TZP powders were uniaxially and isostatically pressed. Green-body samples were sintered and polished to obtain 80 disc-shaped specimens per group (12 × 1 mm, ISO 6872:2015). The crystalline content and microstructure were characterized by X-ray diffraction (XRD) and scanning electron microscope (SEM). Optical properties were determined by the calculation of contrast ratio (CR) and translucency parameter (TP) using reflectance data. Mechanical properties were assessed by Vickers hardness, fracture toughness and biaxial flexural strength test (BFS). All analyses were conducted before and after artificial aging (20h, 134 °C, 0.22 MPa). Optical parameters and microhardness differences were evaluated through repeated-measures analysis of variance (p < 0.05). BFS data were analyzed using Weibull statistics (95% CI). RESULTS: The synthesis of the experimental ZTA composite was successful, with 98% of theoretical density, as shown in the SEM images. XRD patterns revealed typical zirconia and alumina crystalline phases. ZTA optical properties parameters showed no effect of aging, with a high CR and low TP values denoting a high masking-ability. 3Y-TZP presented lower masking-ability and aging significantly affected its optical properties. ZTA Vickers hardness, fracture toughness and Weibull parameters, including characteristic stress and Weibull modulus were not influenced by aging, while 3Y-TZP presented a significant decrease in characteristic stress and increase in fracture toughness after aging. The ZTA probability of survival for missions of 300 and 500 MPa was estimated at ~99% validating its use for 3-unit posterior fixed dental prostheses (FDP), and no different from conventional 3Y-TZP. At high-stress mission (800 MPa) a significant decrease in probability of survival was observed for aged 3Y-TZP (84%) and for immediate and aged ZTA (73 and 82% respectively). CONCLUSION: The ZTA composite presented a dense microstructure, with preservation of the crystalline content, optical and mechanical properties after artificial aging, which encourages future research to validate its potential use for large span FDP.

Mechanical Behavior of Ceramic Monolithic Systems With Different Thicknesses.

OBJECTIVES: This study assessed the fully stabilized zirconia (FSZ) Prettau Anterior, the partially stabilized zirconia (PSZ) Prettau, and the lithium disilicate IPS e.max CAD (LD) through microstructural and mechanical characterization and effect of thickness on fracture load of the ceramics. METHODS AND MATERIALS: Disk-shaped specimens (12 mm diameter and 1.2 mm thickness) were prepared for biaxial flexural strength (BFS) and Weibull statistics (n=30). For the fracture load static test (FLST) and Weibull statistics (n=30), disk-shaped specimens 12 mm in diameter and thicknesses of 0.5 mm, 1 mm, and 1.5 mm were cemented on an epoxy-resin substrate. RESULTS: BFS (MPa) results were PSZ: 683.0 ± 70.23; FSZ: 438.6 ± 64.1; and LD: 248.6 ± 37.3. One-way analysis of variance (ANOVA) for BFS was significant (p<0.001), and the Tukey post hoc test showed differences among all ceramics. There was difference in characteristic strength, but there was no difference in Weibull modulus. Two-way ANOVA for FLST was significant for ceramic (p<0001), thickness (p<0001), and interaction (p<0001). There was no difference among all ceramics at the 0.5 mm thickness. PSZ had higher values for the 1.0 mm and 1.5 mm thicknesses. LD of 1.5 mm thickness exhibited a higher FLST than FSZ. CONCLUSIONS: PSZ had the highest BFS, but when cemented on a substrate, all ceramics with 0.5 mm thickness behaved similarly. Despite the lower BFS, LD had a fracture load similar or superior to FSZ when cemented on a substrate.

Effect of Thermocycling on Biaxial Flexural Strength of CAD/CAM, Bulk Fill, and Conventional Resin Composite Materials.

New resin-based restorative materials have been developed, such as computer-aided design/computer-aided manufacturing (CAD/CAM) and bulk-fill composites, as an alternative to traditional layering techniques. This study evaluated the biaxial flexural strength (BFS) before and after thermocycling of five different resin composites: one hybrid resin/ceramic CAD/CAM indirect material, Lava Ultimate CAD-CAM Restorative (LU, 3M Oral Care); a conventional composite, Filtek Z350 XT (Z350, 3M Oral Care); two bulk-fill composites, Tetric N-Ceram Bulk Fill (TBF, Ivoclar Vivadent) and Filtek Bulk Fill (FBF, 3M Oral Care); and one bulk-fill flow resin composite, Filtek Bulk Fill Flow (FBFF, 3M Oral Care). Three hundred disc-shaped specimens (6.5 mm in diameter and 0.5 mm thick) were fabricated and divided into five groups (n=30 for each composite and condition). The BFS test was performed in a universal testing machine at a crosshead speed of 0.5 mm/min immediately (i, 24 hours) and after thermocycling (a, 500 thermal cycles of 5°C to 55°C with a 30-second dwell time). The Weibull modulus (m) and characteristic stress (η) were calculated, and a contour plot was used (m vs η) to detect differences between groups (95% two-sided confidence intervals). Significantly higher characteristic stress was observed for LUi (286.6 MPa) and Z350i (248.8 MPa) compared to the bulk-fill groups (FBFi=187.9 MPa, FBFFi=175.9 MPa, TBFi=149.9 MPa), with no differences between LUi and Z350i. Thermocycling significantly decreased the characteristic stress of all groups with the highest values observed for LUa (186.7 MPa) and Z350a (188.9 MPa) and the lowest for FBFFa (90.3 MPa). Intermediate values were observed for FBFa (151.6 MPa) and TBFa (122.8 MPa). The Weibull modulus decreased only for FBFa compared to FBFi. Composition and thermocycling significantly influenced the biaxial flexural strength of resin composite materials.

Cone-beam computed tomography compared to X-ray in diagnosis of extremities bone fractures: A study of 198 cases.

CBCT is an imaging technique consisting of X-ray computed tomography, in which the x-rays are divergent, forming a cone. During 2015, a new model of CBCT, New Tom 5G XL (Verona), was used in the Radiology Department of The University of Verona, in collaboration with the Orthopaedics Department. Our study was carried out from October 2015 to October 2016 (198 patients). We compared CBCT with standard x-ray in the diagnosis of foot and anke fractures (and Lisfranc lesions), tibial plateau fractures, wrist and scaphoid fractures, elbow fractures. All patients were analyzed, of which 143 were positive or had documented bone lesions, while 55 were with no fractures seen. Of the 55 negative patients, 19 were considered positive at Standard RX, thus in 34.5% of cases the X-ray Standard examination overestimated the disease (false positive cases). Similarly, of the 143 positive patients, 21 were negative at RX, resulting in 14.6% of false negatives. We can say that if compared to standard X-ray, CBCT has higher sensitivity and specificity in the proper identification and typing of these kind of lesions, with low exposition dose if compared to MDCT. The most common rx-unrecognized fractures were in small bones of carpus and tarsus.

Effect of undigested neutral detergent fiber content of alfalfa hay on lactating dairy cows: Feeding behavior, fiber digestibility, and lactation performance.

The objective of this study was to investigate the effects of 2 alfalfa hays differing in undigested neutral detergent fiber content and digestibility used as the main forage source in diets fed to high producing cows for Parmigiano-Reggiano cheese production. Diets were designed to have 2 different amounts of undigestible NDF [high (Hu) and low (Lu)], as determined by 240-h in vitro analysis (uNDF240). Alfalfa hay in vitro digestibility [% of amylase- and sodium sulfite-treated NDF with ash correction (aNDFom)] at 24 and 240 h was 40.2 and 31.2% and 53.6 and 45.7% for low- (LD) and high-digestibility (HD) hays, respectively. The 4 experimental diets (Hu-HD, Lu-HD, Hu-LD, and Lu-LD) contained 46.8, 36.8, 38.8, and 30.1% of alfalfa hay, respectively, 8.6% wheat straw, and 35.3% corn (50% flake and 50% meal; DM basis). Soy hulls and soybean meal were used to replace hay to balance protein and energy among diets. Eight multiparous Holstein cows (average milk production = 46.0 ± 5.2 kg/d, 101 ± 38 d in milk, and 662 ± 42 kg of average body weight) were assigned to a 4 × 4 Latin square design, with 2 wk of adaptation and a 1-wk collection period. Dry matter and water intake, rumination time, ruminal pH, and milk production and composition were measured. Diets and feces were analyzed for NDF on an organic matter basis (aNDFom), acid detergent fiber, acid detergent lignin, and uNDF240 to estimate total-tract fiber digestibility. Dry matter intake and rumination times were higher in HD diets compared with LD diets, regardless of forage amount. Rumination time was constant per unit of dry matter intake but differed when expressed as a function of uNDF240, aNDFom, or physically effective NDF intake. No differences were found among treatments on average ruminal pH, but the amount of time with pH <5.8 was lower in Hu-HD diets. Milk production and components were not different among diets. Total-tract aNDFom and potentially digestible neutral detergent fiber fraction digestibility was higher for the LD diets (88.3 versus 85.8% aNDFom in HD), for which lower feed intakes were also observed. The Hu-HD diet allowed greater dry matter intake, longer rumination time, and higher ruminal pH, suggesting that the limiting factor for dry matter intake is neutral detergent fiber digestibility and its relative rumen retention time.

Technical note: In vitro digestibility of amylase-treated, ash-corrected neutral detergent fiber, with addition of sodium sulfite, at 240 hours with or without rumen fluid reinoculation.

Long-term in vitro fermentation (240 h) evaluating amylase-treated, ash-corrected neutral detergent fiber, with addition of sodium sulfite (aNDFom) digestibility is required to quantify the indigestible fiber fraction. It is commonly accepted to inoculate rumen fluid more than one time during such fermentations, every 96 h or at 120 h. However, no studies have been conducted to verify if the reinoculation is actually required to properly carry out the fermentation process. The current study aims to evaluate the effects of these procedures on aNDFom digestibility at 240 h. The study was conducted on a total of 24 forage samples (8 alfalfa hays, 8 grass hays, and 8 corn silages). Samples were digested in triplicate at 240 h in vitro. Rumen fluid was added twice (at 96 and 192 h) in treatment 1, after 120 h in treatment 2, whereas no addition was made in treatment 3. At the end of the fermentations, residual aNDFom was quantified to calculate digestibility. Among treatments, no difference was found in digestibility of aNDFom. Moreover, treatment 1 resulted in higher variability compared with other treatments. Results obtained in the current study show that subsequent addition of rumen fluid is not necessary for a proper estimation of aNDFom digestibility, and can be avoided.

Microcomputed Tomography Evaluation of Polymerization Shrinkage of Class I Flowable Resin Composite Restorations.

The present study aimed to characterize the pattern and volume of polymerization shrinkage of flowable resin composites, including one conventional, two bulk fill, and one self-adhesive. Standardized class I preparations (2.5 mm depth × 4 mm length × 4 mm wide) were performed in 24 caries-free human third molars that were randomly divided in four groups, according to the resin composite and adhesive system used: group 1 = Permaflo + Peak Universal Bond (PP); group 2 = Filtek Bulk Fill + Scotchbond Universal (FS); group 3 = Surefil SDR + XP Bond (SX); and group 4 = Vertise flow self-adhering (VE) (n=6). Each tooth was scanned three times using a microcomputed tomography (µCT) apparatus. The first scan was done after the cavity preparation, the second after cavity filling with the flowable resin composite before curing, and the third after it was cured. The µCT images were imported into three-dimensional rendering software, and volumetric polymerization shrinkage percentage was calculated for each sample. Data were submitted to one-way analysis of variance and post hoc comparisons. No significant difference was observed among PP, FS, and VE. SX bulk fill resin composite presented the lowest values of volumetric shrinkage. Shrinkage was mostly observed along the occlusal surface and part of the pulpal floor. In conclusion, polymerization shrinkage outcomes in a 2.5-mm deep class I cavity were material dependent, although most materials did not differ. The location of shrinkage was mainly at the occlusal surface.

Imágenes del depósito de gadolinio en el sistema nervioso central / Images of gadolinio deposit in the central nervous system Abstract

Magnetic resonance imaging has been shown to be very useful in the diagnosis and monitoring of multiple diseases affecting the central nervous system. Gadolinium has been used extensively worldwide. It has been estimated that since its introduction more than two hundred million doses of GBCA have been administered globally. Gadolinium-based contrast agents (GBCAs) were long considered medicines with a high safety profile, the literature reports incidences of immediate adverse effects such as headache, dizziness, and altered sense of taste. Studies performed a few years after the introduction of GBCA showed that there were gadolinium deposits in the tissues but their clinical significance was not known. It wasn’t until 2006 when the first reports were published that associated the gadolinium ion tissue deposits from GBCA with a systemic inflammatory entity of the connective tissue similar to scleroderma known as Nephrogenic Systemic Fibrosis (NSF), in patients with chronic renal failure. In 2013, the association between the use of GBCAs and the progressive increase in the signal intensity of the dentate nucleus and the globus pallidus in T1-weighted MRI images without contrast medium, was described for the first time. This review describes the most relevant aspects of the pathophysiology of these findings taking into account their differential diagnosis.

Las imágenes por resonancia magnética han mostrado ser de gran utilidad en el diagnóstico y seguimiento de múltiples enfermedades que afectan el sistema nervioso central. El gadolinio se ha utilizado ampliamente a nivel mundial. Se estima que desde su introducción se han administrado más de doscientos millones de dosis de MCBG en el mundo. Los medios de contraste basados en Gadolinio (MCBG) fueron considerados por mucho tiempo medicamentos con un alto perfil de seguridad, la literatura reporta incidencia de efectos adversos inmediatos como cefalea, mareo y alteración del sentido del gusto. Estudios realizados pocos años después de la introducción de los MCBG mostraron que había depósitos de gadolinio en los tejidos, pero no se conocía su significancia clínica Fue hasta 2006 cuando se publicaron los primeros reportes que asociaban el depósito tisular del ion gadolinio proveniente de los MCBG con una entidad inflamatoria sistémica del tejido conectivo similar a la escleroderma conocida como Fibrosis Sistémica Nefrogénica (FSN) en pacientes con falla renal crónica. En 2013 se describió por primera vez la asociación entre el uso de los MCBG y el aumento progresivo de la intensidad de señal del núcleo dentado y los globos pálidos en las imágenes de RM ponderadas en T1 sin medio de contraste. En esta revisión se describen los aspectos más relevantes de la fisiopatología de estos hallazgos considerando su diagnóstico diferencial.

Using single or multiple liquor-donor cows for in vitro digestibility of amylase- and sodium sulfite-treated neutral detergent fiber with ash correction.

In vitro methods requiring ruminal microorganisms to ferment and digest feeds have been used for decades. Though commonly accepted, collecting and pooling rumen fluid from different donor animals to avoid individual characteristics could affect in vitro fermentations. The current study evaluated the effects of individual or pooled liquors on in vitro digestibility of amylase- and sodium sulfite-treated NDF with ash correction (aNDFom). The study was conducted on 24 samples (8 alfalfa hays, 8 grass hays, and 8 corn silages). The 3 donor animals (treatment 1, 2, and 3) were selected based on similar body weights, parity, days in milk, milk production, and milk composition. Samples were digested in vitro via inoculation of different rumen fluid at different time points (12, 24, 72, and 120h). An equal amount of each liquor collected was sampled and equally mixed with the others to obtain treatment 4. For the alfalfa hay group, differences were observed at 12 (29.95, 27.07, 29.02, and 32.55% aNDFom for treatments 1, 2, 3, and 4, respectively) and 24h (37.35, 35.54, 36.44, and 40.56% aNDFom for treatments 1, 2, 3, and 4, respectively). The inoculum source did not affect in vitro digestibility over longer time periods (72 and 120 h). Similar results were observed in the grass hay group, in which the mixed inoculum had greater digestibility values at both 12 (28.86, 26.89, 27.88, and 30.92% aNDFom for treatments 1, 2, 3, and 4, respectively) and 24h (37.35, 35.54, 36.44, and 40.56% aNDFom for treatment 1, 2, 3, and 4, respectively), but not over longer time periods. For the corn silage group, we observed differences for treatment 4 only at 12h (35.78, 33.87, 34.83, and 37.80% aNDFom for treatment 1, 2, 3, and 4, respectively). These results underline the differences among donor animals, especially when evaluating short incubation time points, and that pooling rumen contents is not equal to averaging across individual animals. Reported data require a deeper investigation on whether or not the method of inoculating a pool of rumen contents represents the actual ability of the animal to digest fiber.

Effects of a completely pelleted diet on growth performance in Holstein heifers.

Forage neutral detergent fiber (NDF) content and particle size are important factors that affect rumen function. The aim of the current study was to evaluate the effects on rumen health, NDF digestibility, and animal performance of pelleting a forage-based diet. Eight Holstein heifers (age 336±30d, body weight 346±35kg) were randomly assigned to a repeated crossover design. Animals were housed in tie-stalls and fed for ad libitum intake. The study included 4 periods of 3 wk, the first 2 wk for adaptation to the diet and the last wk for data collection. Diets had the same ingredients but had a different physical form: total mixed ration (TMR) and pellet (diameter=8mm). The physically effective NDF (peNDF) differed between the 2 treatments (39.8 and 11.8% of NDF in the TMR and pellet diets, respectively). During the trial, dry matter intake (DMI), water intake, rumination time, rumen temperature, and pH were evaluated daily. Fecal samples were collected in wk3 of each period to determine total-tract digestibility of the potential digestible (pd)NDF. Average daily gain and feed conversion ratio were calculated at the end of each period. With the pellet diet, DMI, DMI/body weight, and water consumption were higher. We observed no significant difference in average daily gain or feed conversion ratio. Rumination time was lower for the pellet diet than for the TMR diet (241 vs. 507min/d, respectively). Diet had no effect on rumen temperature or rumen pH. The total-tract digestibility of the pdNDF was greater with the TMR diet than with the pellet diet (90.25 vs. 86.82% pdNDF, respectively). The results of the current study suggest that a complete-feed pellet diet was well accepted by the animals, as demonstrated by higher DMI. Rumination time was reduced with the pellet diet, but rumen pH was not different. The pdNDF digestibility was high for both diets, but significantly higher for the TMR diet. Given that animal performance was similar between the 2 diets, although they differed with respect to DMI and fiber digestion, we hypothesize that the 2 diets had different retention times, related to their physical form. A complete-feed pellet diet formulated to provide a sufficient level of NDF from forages could be fed to growing ruminants without apparent negative effects on rumen health and animal productivity, at least for a short period. More research over a longer growing period is needed before recommending this feeding strategy for growing heifers.

A Critical Perspective on Mechanical Testing of Implants and Prostheses.

The degree of interplay among variables in dental implant treatment presents a challenge to randomized clinical trials attempting to answer questions in a timely, unbiased, and economically feasible fashion. Further adding complexity to the different scenarios is the varied implant designs and related bone response, area of implantation, implant bulk material, restoration, abutments and related screws, fixation mode (screwed, fixed, or a combination), and horizontal implant-abutment matching geometry. This article critically appraises the most common mechanical testing methods used to characterize the implant-prostheses complex. It attempts to provide insight into the process of construction of an informed database of clinically relevant questions regarding preclinical evaluation of implant biomechanics and failure mechanisms. The use of single load to failure, fatigue life, fatigue limit, and step-stress accelerated life testing is discussed with emphasis on their deliverables, weaknesses, and strengths. Fractographic analysis and challenges in the correlation between laboratory- and in-service-produced failures of dental ceramics, resin composites, and titanium are introduced. In addition, examples are presented of mechanical characterization studies used in our laboratory to assess some implant-supported rehabilitation variables.