Pure &crystallized 2D Boron Nitride sheets synthesized via a novel process coupling both PDCs and SPS methods.

Within the context of emergent researches linked to graphene, it is well known that h-BN nanosheets (BNNSs), also referred as 2D BN, are considered as the best candidate for replacing SiO2 as dielectric support or capping layers for graphene. As a consequence, the development of a novel alternative source for highly crystallized h-BN crystals, suitable for a further exfoliation, is a prime scientific issue. This paper proposes a promising approach to synthesize pure and well-crystallized h-BN flakes, which can be easily exfoliated into BNNSs. This new accessible production process represents a relevant alternative source of supply in response to the increasing need of high quality BNNSs. The synthesis strategy to prepare pure h-BN is based on a unique combination of the Polymer Derived Ceramics (PDCs) route with the Spark Plasma Sintering (SPS) process. Through a multi-scale chemical and structural investigation, it is clearly shown that obtained flakes are large (up to 30 µm), defect-free and well crystallized, which are key-characteristics for a subsequent exfoliation into relevant BNNSs.

A convenient and quantitative route to Sn(IV)-M [M = Ti(IV), Nb(V), Ta(V)] heterobimetallic precursors for dense mixed-metal oxide ceramics.

The strategy of reacting SnCl4 with M(OR)x provided a convenient and quantitative approach to new heterobimetallics with a simple addition formula, [SnCl4M(OR)x(HOR)y] (M = Ti, Nb, Ta; R = Et, Pr(i), x = 4, 5; y = 0-2) or sometimes an oxo complex [SnCl3(O)Ti2(OPr(i))7(HOPr(i))2]. The alcoholysis reactions of these heterometallics afforded mixed alkoxo complexes [SnCl4(µ-OEt)2M(Pr(i)O)x(Pr(i)OH)y] [M = Ti (x = y = 2), Nb, Ta (x = 3, y = 1)] under mild conditions, or a planar rectangular oxo product [SnCl3(µ-OEt)2Nb(OEt)2(EtOH)(µ-O)]2 at refluxing/extended stirring time. DFT calculations shed light on the stability and reactivity of these complexes. The use of these thoroughly characterized heterometallics as sol-gel precursors suppresses the formation of the undesired SnO2 grains, which are difficult to be sintered to a high density. The combined approach of using bottom-up synthesis of mixed Ti0.5Sn0.5O2 nanoparticles and Spark Plasma Sintering allowed the successful densification of chloride-free mixed-metal oxide ceramics. The influence of thermal treatment before sintering on the density and spinodal decomposition of the TiO2-SnO2 pellets is reported.