RESUMO
Self-assembled monolayers of corrosion inhibitors of the mercaptobenzimidazole family, SH-BimH, SH-BimH-5NH2, and SH-BimH-5OMe, were formed on template-stripped ultraflat Au surfaces using microcontact printing, and subsequently analyzed using X-ray photoelectron spectroscopy (XPS), atomic force microscopy (AFM), and AFM-force spectroscopy (AFM-FS) using a quantitative imaging (QI) mode. Printing of all used inhibitor molecules resulted in clear patterns and in slightly more compact films compared to immersion. The stability of the monolayers is further probed by AFM-FS. Adhesion values of laterally heterogeneous inhibitor-modified surfaces compared to bare Au surfaces, nonpatterned areas, and fully covered surfaces are analyzed and discussed. Microcontact printing confers a superior nanomechanical stability to imidazole-modified films of the printed surface patches as compared to homogeneously covered surfaces by immersion into the inhibitor solution.
RESUMO
By ultrasonic spray deposition of precursors, conformal deposition on 3D surfaces of tungsten oxide (WO3) negative electrode and amorphous lithium lanthanum titanium oxide (LLT) solid-electrolyte has been achieved as well as an all-solid-state half-cell. Electrochemical activity was achieved of the WO3 layers, annealed at temperatures of 500 °C. Galvanostatic measurements show a volumetric capacity (415 mAh·cm-3) of the deposited electrode material. In addition, electrochemical activity was shown for half-cells, created by coating WO3 with LLT as the solid-state electrolyte. The electron blocking properties of the LLT solid-electrolyte was shown by ferrocene reduction. 3D depositions were done on various micro-sized Si template structures, showing fully covering coatings of both WO3 and LLT. Finally, the thermal budget required for WO3 layer deposition was minimized, which enabled attaining active WO3 on 3D TiN/Si micro-cylinders. A 2.6-fold capacity increase for the 3D-structured WO3 was shown, with the same current density per coated area.
RESUMO
The identification, fine-tuning, and process optimization of appropriate hole transporting layers (HTLs) for organic solar cells is indispensable for the production of efficient and sustainable functional devices. In this study, the optimization of a solution-processed molybdenum oxide (MoOx) layer fabricated from a combustion precursor is carried out via the introduction of zirconium and tin additives. The evaluation of the output characteristics of both organic photovoltaic (OPV) and organic light emitting diode (OLED) devices demonstrates the beneficial influence upon the addition of the Zr and Sn ions compared to the generic MoOx precursor. A dopant effect in which the heteroatoms and the molybdenum oxide form a chemical identity with fundamentally different structural properties could not be observed, as the additives do not affect the molybdenum oxide composition or electronic band structure. An improved surface roughness due to a reduced crystallinity was found to be a key parameter leading to the superior performance of the devices employing modified HTLs.