RESUMO
OBJECTIVES: To synthesize casein enzymatic hydrolysate (CEH)-laden gelatin methacryloyl (GelMA) fibrous scaffolds and evaluate the cytocompatibility and anti-inflammatory effects on dental pulp stem cells (DPSCs). MATERIALS AND METHODS: GelMA fibrous scaffolds with 10%, 20%, and 30% CEH (w/w) and without CEH (control) were obtained via electrospinning. Chemo-morphological, degradation, and mechanical analyses were conducted to evaluate the morphology and composition of the fibers, mass loss, and mechanical properties, respectively. Adhesion/spreading and viability of DPSCs seeded on the scaffolds were also assessed. The anti-inflammatory potential on DPSCs was tested after the chronic challenge of cells with lipopolysaccharides (LPS), followed by treatment with extracts obtained after immersing the scaffolds in α-MEM. The synthesis of the pro-inflammatory cytokines IL-6, IL-1α, and TNF-α was measured by ELISA. Data were analyzed by ANOVA/post-hoc tests (α = 5%). RESULTS: CEH-laden electrospun fibers had a larger diameter than pure GelMA (p ≤ 0.036). GelMA scaffolds laden with 20% and 30% CEH had a greater mass loss. Tensile strength was reduced for the 10% CEH fibers (p = 0.0052), whereas no difference was observed for the 20% and 30% fibers (p ≥ 0.6736) compared to the control. Young's modulus decreased with CEH (p < 0.0001). Elongation at break increased for the 20% and 30% CEH scaffolds (p ≤ 0.0038). Over time, DPSCs viability increased across all groups, indicating cytocompatibility, with CEH-laden scaffolds exhibiting greater cell viability after seven days (p ≤ 0.0166). Also, 10% CEH-GelMA scaffolds decreased the IL-6, IL-1α, and TNF-α synthesis (p ≤ 0.035). CONCLUSION: CEH-laden GelMA scaffolds facilitated both adhesion and proliferation of DPSCs, and 10% CEH provided anti-inflammatory potential after chronic LPS challenge. CLINICAL RELEVANCE: CEH incorporated in GelMA fibrous scaffolds demonstrated the potential to be used as a cytocompatible and anti-inflammatory biomaterial for vital pulp therapy.
Assuntos
Anti-Inflamatórios , Caseínas , Sobrevivência Celular , Polpa Dentária , Gelatina , Alicerces Teciduais , Gelatina/química , Polpa Dentária/citologia , Polpa Dentária/efeitos dos fármacos , Alicerces Teciduais/química , Humanos , Anti-Inflamatórios/farmacologia , Sobrevivência Celular/efeitos dos fármacos , Metacrilatos/química , Teste de Materiais , Ensaio de Imunoadsorção Enzimática , Resistência à Tração , Células Cultivadas , Células-Tronco/efeitos dos fármacos , Adesão Celular/efeitos dos fármacos , Materiais Biocompatíveis/farmacologia , Materiais Biocompatíveis/química , Citocinas/metabolismo , Propriedades de SuperfícieRESUMO
INTRODUCTION: Recognizing the necessity of novel disinfection strategies for improved bacterial control to ultimately favor tissue regeneration, this study developed and characterized antibiotics-laden silk fibroin methacrylated (SilkMA) scaffolds for regenerative endodontics. METHODS: SilkMA-based solutions (10% w/v) containing clindamycin (CLI) or tinidazole (TIN) (0 - control; 5, 10, or 15% w/w) or the combination of both drugs (BiMix CLI/TIN 10%) were electrospun and photocrosslinked. Morphology and composition were assessed using scanning electron microscopy (SEM) and Fourier-transform infrared spectroscopy (FTIR). Additionally, swelling and degradation profiles were also determined. Cytotoxicity was evaluated in stem cells from apical papilla (SCAPs). Antibacterial efficacy was tested using direct and indirect contact assays against Aggregatibacter actinomycetemcomitans/Aa, Actinomyces naeslundii/An, Enterococcus faecalis/Ef, and Fusobacterium nucleatum/Fn. E. faecalis biofilm inhibition on dentin discs was specifically evaluated for BiMix-laden scaffolds. Data were statistically analyzed with a significance level of 5%. RESULTS: SEM revealed that all scaffolds had similar characteristics, including fiber morphology and bead absence. FTIR showed the incorporation of CLI and TIN into the fibers and in BiMix scaffolds. Antibiotic-laden scaffolds exhibited lower swelling capacity than the control and were degraded entirely after 45 days. Scaffolds laden with CLI, TIN, or BiMix throughout all time points did not reduce SCAPs' viability. CLI-laden scaffolds inhibited the growth of Aa, An, and Ef, while TIN-laden scaffolds inhibited Fn growth. BiMix-laden scaffolds significantly inhibited Aa, An, Ef, and Fn in direct contact, and their aliquots inhibited An and Fn through indirect contact, with additional biofilm inhibition against Ef. CONCLUSIONS: BiMix-laden SilkMA scaffolds are cytocompatible and exhibit antimicrobial effects against endodontic pathogens, indicating their therapeutic potential as a drug delivery system for regenerative endodontics.
RESUMO
BACKGROUND: Assessing the biocompatibility of materials is crucial for ensuring the safety and well-being of patients by preventing undesirable, toxic, immune, or allergic reactions, and ensuring that materials remain functional over time without triggering adverse reactions. To ensure a comprehensive assessment, planning tests that carefully consider the intended application and potential exposure scenarios for selecting relevant assays, cell types, and testing parameters is essential. Moreover, characterizing the composition and properties of biomaterials allows for a more accurate understanding of test outcomes and the identification of factors contributing to cytotoxicity. Precise reporting of methodology and results facilitates research reproducibility and understanding of the findings by the scientific community, regulatory agencies, healthcare providers, and the general public. AIMS: This article aims to provide an overview of the key concepts associated with evaluating the biocompatibility of biomaterials while also offering practical guidance on cellular principles, testing methodologies, and biological assays that can support in the planning, execution, and reporting of biocompatibility testing.
RESUMO
BACKGROUND: Bibliometric analysis is a critical indicator of the influence and relevance of scientific papers, whilst also highlighting key contributors and gaps in knowledge in a scientific field. OBJECTIVES: To update and analyse the 100 most-cited papers in regenerative endodontics from 2019 to 2023. METHODS: A search of the most-cited recent papers focusing on regenerative endodontics using journals included in the category, 'Dentistry, Oral Surgery & Medicine', in the Clarivate Web of Science database from 2019 to 2023 was performed. Three researchers conducted the study selection and data extraction. Data extraction included publication title and year, authors, number and mean number of citations, institution, country and continent, study design, journal title, keywords and research topic. Citation counts were also collected in Google Scholar and Scopus databases. Graphical bibliometric networks were created using VOSviewer software. RESULTS: The number of citations of the 100 most-cited articles ranged from 6 to 85. Most were published in 2020 (n = 48), principally in the Journal of Endodontics (47%), followed by International Endodontic Journal (13%), Journal of Dental Research (6%) and Dental Materials (6%). Laboratory study was the most common study design amongst the included papers (n = 47), followed by narrative reviews (n = 17) and observational studies (n = 16). The most frequent first author on the top three most-cited papers was Hacer Aksel, whilst Adham A. Azim (n = 6; 89 citations) contributed most to the top 100 articles. The institution from which most articles originated was the University of Hong Kong (China) (n = 5; 81 citations), whereas the corresponding authors were predominantly from the United States of America (USA) (n = 31; 560 citations). The VOSviewer map of co-authorship demonstrated research collaborative clusters. 'Regenerative endodontics' and 'stem-cells' were the most employed keywords (37 and 36 occurrences respectively). DISCUSSION: The current study was designed not only to showcase the most influential papers in regenerative endodontics since 2019 but also to provide a better understanding of global research in this area over the last five years. CONCLUSIONS: This bibliometric analysis highlighted papers, authors, institutions and keywords in regenerative endodontics. The 100 most-cited papers primarily consisted of laboratory studies published in the USA, focusing on evaluating biomaterials and scaffold design strategies in contact with stem cells. Clinical studies and systematic reviews representing higher levels of scientific evidence are currently not the most influential in the regenerative endodontic field.
RESUMO
Apical periodontitis (AP) is a dental-driven condition caused by pathogens and their toxins infecting the inner portion of the tooth (i.e., dental pulp tissue), resulting in inflammation and apical bone resorption affecting 50% of the worldwide population, with more than 15 million root canals performed annually in the United States. Current treatment involves cleaning and decontaminating the infected tissue with chemo-mechanical approaches and materials introduced years ago, such as calcium hydroxide, zinc oxide-eugenol, or even formalin products. Here, we present, for the first time, a nanotherapeutics based on using synthetic high-density lipoprotein (sHDL) as an innovative and safe strategy to manage dental bone inflammation. sHDL application in concentrations ranging from 25 µg to 100 µg/mL decreases nuclear factor Kappa B (NF-κB) activation promoted by an inflammatory stimulus (lipopolysaccharide, LPS). Moreover, sHDL at 500 µg/mL concentration markedly decreases in vitro osteoclastogenesis (P < 0.001), and inhibits IL-1α (P = 0.027), TNF-α (P = 0.004), and IL-6 (P < 0.001) production in an inflammatory state. Notably, sHDL strongly dampens the Toll-Like Receptor signaling pathway facing LPS stimulation, mainly by downregulating at least 3-fold the pro-inflammatory genes, such as Il1b, Il1a, Il6, Ptgs2, and Tnf. In vivo, the lipoprotein nanoparticle applied after NaOCl reduced bone resorption volume to (1.3 ± 0.05) mm3 and attenuated the inflammatory reaction after treatment to (1 090 ± 184) cells compared to non-treated animals that had (2.9 ± 0.6) mm3 (P = 0.012 3) and (2 443 ± 931) cells (P = 0.004), thus highlighting its promising clinical potential as an alternative therapeutic for managing dental bone inflammation.
Assuntos
Lipoproteínas HDL , NF-kappa B , Periodontite Periapical , Animais , Periodontite Periapical/terapia , Camundongos , Lipopolissacarídeos , Osteogênese/efeitos dos fármacos , Humanos , Osteoclastos/efeitos dos fármacos , NanopartículasRESUMO
Management of skin injuries imposes a substantial financial burden on patients and hospitals, leading to diminished quality of life. Periostin (rhOSF), an extracellular matrix component, regulates cell function, including a proliferative healing phase, representing a key protein to promote wound healing. Despite its proven efficacy in vitro, there is a lack of scaffolds that facilitate the in situ delivery of rhOSF. In addition, there is a need for a scaffold to not only support cell growth, but also to resist the mechanical forces involved in wound healing. In this work, we synthesized rhOSF-loaded mesoporous nanoparticles (MSNs) and incorporated them into a cell-laden gelatin methacryloyl (GelMA) ink that was bioprinted into melt electrowritten poly(ε-caprolactone) (PCL) microfibrous (MF-PCL) meshes to develop mechanically competent constructs. Diffraction light scattering (DLS) analysis showed a narrow nanoparticle size distribution with an average size of 82.7 ± 13.2 nm. The rhOSF-loaded hydrogels showed a steady and controlled release of rhOSF over 16 days at a daily dose of â¼40 ng/mL. Compared with blank MSNs, the incorporation of rhOSF markedly augmented cell proliferation, underscoring its contribution to cellular performance. Our findings suggest a promising approach to address challenges such as prolonged healing, offering a potential solution for developing robust, biocompatible, and cell-laden grafts for burn wound healing applications.
Assuntos
Moléculas de Adesão Celular , Gelatina , Metacrilatos , Nanopartículas , Poliésteres , Alicerces Teciduais , Cicatrização , Humanos , Cicatrização/efeitos dos fármacos , Nanopartículas/química , Gelatina/química , Poliésteres/química , Metacrilatos/química , Alicerces Teciduais/química , Moléculas de Adesão Celular/administração & dosagem , Proliferação de Células/efeitos dos fármacos , Bioimpressão/métodos , Hidrogéis/química , Porosidade , PeriostinaRESUMO
OBJECTIVE: This study examined how range concentrations of Fibroblast Growth Factor-2 (FGF-2) influence the differentiation and activity of human-derived periodontal ligament (hPDLSCs) and alveolar bone-derived stem cells (haBMSCs). DESIGN: hPDLSCs and haBMSCs were cultured with varying concentrations of FGF-2 (0, 1, 2.5, 5, 10, 20 ng/mL) and monitored for osteogenic differentiation through alkaline phosphatase (ALP) activity and quantification of gene expression (qRT-PCR) for osteogenesis markers. Additionally, alizarin red staining and a hydroxyproline colorimetric assay evaluated and quantified osteogenic matrix mineralization and collagen deposition. Statistical analyses were performed using one-way ANOVA or two-way ANOVA for multiple comparisons between groups. RESULTS: At low FGF-2 concentrations, hPDLSCs differentiated toward an osteogenic lineage, whereas higher concentrations of FGF-2 inhibited osteogenesis and promoted fibroblastic differentiation. The effect of FGF-2 at the lowest concentration tested (1 ng/mL) led to significantly higher ALP activity than osteogenically induced positive controls at early time points and equivalent RUNX2 expression at early and later time points. FGF-2 supplementation of haBMSC cultures was sufficient, at all concentrations, to increase ALP activity at an earlier time point. Mineralization of haBMSC cultures increased significantly within 5-20 ng/mL FGF-2 concentrations under basal growth media conditions (α-minimal essential medium supplemented with 15 % fetal bovine serum and 1 % penicillin/streptomycin). CONCLUSIONS: FGF-2 has a dual capacity in promoting osteogenic and fibroblastic differentiation within hPDLSCs contingent upon the dosage and timing of administration, alongside supporting osteogenic differentiation in haBMSCs. These findings underscore the need for precision growth factors dosing when considering the design of biomaterials for periodontal regeneration.
Assuntos
Fator 2 de Crescimento de Fibroblastos , Ligamento Periodontal , Humanos , Fosfatase Alcalina/metabolismo , Processo Alveolar/citologia , Processo Alveolar/efeitos dos fármacos , Diferenciação Celular/efeitos dos fármacos , Células Cultivadas , Subunidade alfa 1 de Fator de Ligação ao Core/metabolismo , Fator 2 de Crescimento de Fibroblastos/farmacologia , Osteogênese/efeitos dos fármacos , Osteogênese/fisiologia , Ligamento Periodontal/citologia , Ligamento Periodontal/efeitos dos fármacos , Reação em Cadeia da Polimerase em Tempo Real , Células-Tronco/efeitos dos fármacosRESUMO
OBJECTIVE: To fabricate and characterize an innovative gelatin methacryloyl/GelMA electrospun scaffold containing the citrus flavonoid naringenin/NA with osteogenic and anti-inflammatory properties. METHODS: GelMA scaffolds (15 % w/v) containing 0/Control, 5, 10, or 20 % of NA w/w were obtained via electrospinning. The chemical composition, fiber morphology/diameter, swelling/degradation profile, and NA release were investigated. Cytotoxicity, cell proliferation, adhesion and spreading, total protein/TP production, alkaline phosphatase/ALP activity, osteogenic genes expression (OCN, OPN, RUNX2), and mineralized nodules deposition/MND with human alveolar bone-derived mesenchymal stem cells (aBMSCs) seeded on the scaffolds were assessed. Moreover, aBMSCs seeded on the scaffolds and stimulated with tumor necrosis factor-alpha/TNF-α were submitted to collagen, nitric oxide/NO, interleukin/IL-1α, and IL-6 production assessment. Data were analyzed using ANOVA and t-student/post-hoc tests (α = 5 %). RESULTS: NA-laden scaffolds presented increased fiber diameter, lower swelling capacity, and faster degradation profile over 28 days (p < 0.05). NA release was detected over time. Cell adhesion and spreading, and TP production were similar between GelMA and GelMA+NA5 % scaffolds, while cell proliferation, ALP activity, OCN/OPN/RUNX2 gene expression, and MND were higher for GelMA+NA5 % scaffolds (p < 0.05). Cells seeded on control scaffolds and TNF-α-stimulated presented higher levels of NO, IL-1α/IL-6, and lower levels of collagen (p < 0.05). In contrast, cells seeded on GelMA+NA5 % scaffolds showed downregulation of inflammatory markers and higher collagen synthesis (p < 0.05). SIGNIFICANCE: GelMA+NA5 % scaffold was cytocompatible, stimulated aBMSCs proliferation and differentiation, and downregulated inflammatory mediators' synthesis, suggesting its therapeutic effect as a multi-target bifunctional scaffold with osteogenic and anti-inflammatory properties for bone tissue engineering.
Assuntos
Proliferação de Células , Flavanonas , Gelatina , Metacrilatos , Osteogênese , Alicerces Teciduais , Alicerces Teciduais/química , Gelatina/química , Humanos , Flavanonas/farmacologia , Flavanonas/química , Osteogênese/efeitos dos fármacos , Proliferação de Células/efeitos dos fármacos , Metacrilatos/química , Células-Tronco Mesenquimais/efeitos dos fármacos , Anti-Inflamatórios/farmacologia , Fosfatase Alcalina/metabolismo , Adesão Celular/efeitos dos fármacos , Células Cultivadas , Fator de Necrose Tumoral alfa , Engenharia Tecidual , Subunidade alfa 1 de Fator de Ligação ao CoreRESUMO
This study investigated the incorporation of sources of calcium, phosphate, or both into electrospun scaffolds and evaluated their bioactivity on human dental pulp cells (HDPCs). Additionally, scaffolds incorporated with calcium hydroxide (CH) were characterized for degradation, calcium release, and odontogenic differentiation by HDPCs. Polycaprolactone (PCL) was electrospun with or without 0.5% w/v of calcium hydroxide (PCL + CH), nano-hydroxyapatite (PCL + nHA), or ß-glycerophosphate (PCL + ßGP). SEM/EDS analysis confirmed fibrillar morphology and particle incorporation. HDPCs were cultured on the scaffolds to assess cell viability, adhesion, spreading, and mineralized matrix formation. PCL + CH was also evaluated for gene expression of odontogenic markers (RT-qPCR). Data were submitted to ANOVA and Student's t-test (α = 5%). Added CH increased fiber diameter and interfibrillar spacing, whereas ßGP decreased both. PCL + CH and PCL + nHA improved HDPC viability, adhesion, and proliferation. Mineralization was increased eightfold with PCL + CH. Scaffolds containing CH gradually degraded over six months, with calcium release within the first 140 days. CH incorporation upregulated DSPP and DMP1 expression after 7 and 14 days. In conclusion, CH- and nHA-laden PCL fiber scaffolds were cytocompatible and promoted HDPC adhesion, proliferation, and mineralized matrix deposition. PCL + CH scaffolds exhibit a slow degradation profile, providing sustained calcium release and stimulating HDPCs to upregulate odontogenesis marker genes.
RESUMO
This study aimed to develop gelatin methacryloyl (GelMA)-injectable hydrogels incorporated with 58S bioactive glass/BG-doped with strontium for vital pulp therapy applications. GelMA hydrogels containing 0% (control), 5%, 10%, and 20% BG (w/v) were prepared. Their morphological and chemical properties were evaluated by scanning electron microscopy/SEM, energy dispersive spectroscopy/EDS, and Fourier transform infrared spectroscopy/FTIR (n = 3). Their swelling capacity and degradation ratio were also measured (n = 4). Cell viability (n = 8), mineralized matrix formation, cell adhesion, and spreading (n = 6) on DPSCs were evaluated. Data were analyzed using ANOVA/post hoc tests (α = 5%). SEM and EDS characterization confirmed the incorporation of BG particles into the hydrogel matrix, showing GelMA's (C, O) and BG's (Si, Cl, Na, Sr) chemical elements. FTIR revealed the main chemical groups of GelMA and BG, as ~1000 cm-1 corresponds to Si-O and ~1440 cm-1 to C-H. All the formulations were degraded by day 12, with a lower degradation ratio observed for GelMA+BG20%. Increasing the concentration of BG resulted in a lower mass swelling ratio. Biologically, all the groups were compatible with cells (p > 0.6196), and cell adhesion increased over time, irrespective of BG concentration, indicating great biocompatibility. GelMA+BG5% demonstrated a higher deposition of mineral nodules over 21 days (p < 0.0001), evidencing the osteogenic potential of hydrogels. GelMA hydrogels incorporated with BG present great cytocompatibility, support cell adhesion, and have a clinically relevant degradation profile and suitable mineralization potential, supporting their therapeutic potential as promising biomaterials for pulp capping.
RESUMO
The field of tissue engineering has witnessed significant advancements in recent years, driven by the pursuit of innovative solutions to address the challenges of bone regeneration. In this study, we developed an electrospun composite scaffold for bone tissue engineering. The composite scaffold is made of a blend of poly(L-lactide-co-ε-caprolactone) (PLCL) and polyethylene glycol (PEG), with the incorporation of calcined and lyophilized silicate-chlorinated bioactive glass (BG) particles. Our investigation involved a comprehensive characterization of the scaffold's physical, chemical, and mechanical properties, alongside an evaluation of its biological efficacy employing alveolar bone-derived mesenchymal stem cells. The incorporation of PEG and BG resulted in elevated swelling ratios, consequently enhancing hydrophilicity. Thermal gravimetric analysis confirmed the efficient incorporation of BG, with the scaffolds demonstrating thermal stability up to 250°C. Mechanical testing revealed enhanced tensile strength and Young's modulus in the presence of BG; however, the elongation at break decreased. Cell viability assays demonstrated improved cytocompatibility, especially in the PLCL/PEG+BG group. Alizarin red staining indicated enhanced osteoinductive potential, and fluorescence analysis confirmed increased cell adhesion in the PLCL/PEG+BG group. Our findings suggest that the PLCL/PEG/BG composite scaffold holds promise as an advanced biomaterial for bone tissue engineering.
Assuntos
Células-Tronco Mesenquimais , Poliésteres , Polietilenoglicóis , Engenharia Tecidual , Alicerces Teciduais , Polietilenoglicóis/química , Poliésteres/química , Alicerces Teciduais/química , Células-Tronco Mesenquimais/citologia , Células-Tronco Mesenquimais/metabolismo , Humanos , Vidro/química , Teste de MateriaisRESUMO
Gingival recession, a prevalent condition affecting the gum tissues, is characterized by the exposure of tooth root surfaces due to the displacement of the gingival margin. This review explores conventional treatments, highlighting their limitations and the quest for innovative alternatives. Importantly, it emphasizes the critical considerations in gingival tissue engineering leveraging on cells, biomaterials, and signaling factors. Successful tissue-engineered gingival constructs hinge on strategic choices such as cell sources, scaffold design, mechanical properties, and growth factor delivery. Unveiling advancements in recent biofabrication technologies like 3D bioprinting, electrospinning, and microfluidic organ-on-chip systems, this review elucidates their precise control over cell arrangement, biomaterials, and signaling cues. These technologies empower the recapitulation of microphysiological features, enabling the development of gingival constructs that closely emulate the anatomical, physiological, and functional characteristics of native gingival tissues. The review explores diverse engineering strategies aiming at the biofabrication of realistic tissue-engineered gingival grafts. Further, the parallels between the skin and gingival tissues are highlighted, exploring the potential transfer of biofabrication approaches from skin tissue regeneration to gingival tissue engineering. To conclude, the exploration of innovative biofabrication technologies for gingival tissues and inspiration drawn from skin tissue engineering look forward to a transformative era in regenerative dentistry with improved clinical outcomes.
Assuntos
Regeneração , Engenharia Tecidual , Alicerces Teciduais , Humanos , Engenharia Tecidual/métodos , Regeneração/fisiologia , Alicerces Teciduais/química , Gengiva , Animais , Materiais Biocompatíveis/química , Impressão Tridimensional , Retração Gengival/terapia , Bioimpressão/métodosRESUMO
OBJECTIVES: Customization and the production of patient-specific devices, tailoring the unique anatomy of each patient's jaw and facial structures, are the new frontiers in dentistry and maxillofacial surgery. As a technological advancement, additive manufacturing has been applied to produce customized objects based on 3D computerized models. Therefore, this paper presents advances in additive manufacturing strategies for patient-specific devices in diverse dental specialties. METHODS: This paper overviews current 3D printing techniques to fabricate dental and maxillofacial devices. Then, the most recent literature (2018-2023) available in scientific databases reporting advances in 3D-printed patient-specific devices for dental and maxillofacial applications is critically discussed, focusing on the major outcomes, material-related details, and potential clinical advantages. RESULTS: The recent application of 3D-printed customized devices in oral prosthodontics, implantology and maxillofacial surgery, periodontics, orthodontics, and endodontics are presented. Moreover, the potential application of 4D printing as an advanced manufacturing technology and the challenges and future perspectives for additive manufacturing in the dental and maxillofacial area are reported. SIGNIFICANCE: Additive manufacturing techniques have been designed to benefit several areas of dentistry, and the technologies, materials, and devices continue to be optimized. Image-based and accurately printed patient-specific devices to replace, repair, and regenerate dental and maxillofacial structures hold significant potential to maximize the standard of care in dentistry.
Assuntos
Impressão Tridimensional , Prostodontia , HumanosRESUMO
The evolutionary establishment of an internal biological clock is a primordial event tightly associated with a 24-h period. Changes in the circadian rhythm can affect cellular functions, including proliferation, DNA repair and redox state. Even isolated organs, tissues and cells can maintain an autonomous circadian rhythm. These cell-autonomous molecular mechanisms are driven by intracellular clock genes, such as BMAL1. Little is known about the role of core clock genes and epigenetic modifications in the skin. Our focus was to identify BMAL1-driven epigenetic modifications associated with gene transcription by mapping the acetylation landscape of histones in epithelial cells responding to injury. We explored the role of BMAL1 in epidermal wound and tissue regeneration using a loss-of-function approach in vivo. We worked with BMAL1 knockout mice and a contraction-resistance wound healing protocol, determining the histone modifications using specific antibodies to detect the acetylation levels of histones H3 and H4. We found significant differences in the acetylation levels of histones in both homeostatic and injured skin with deregulated BMAL1. The intact skin displayed varied acetylation levels of histones H3 and H4, including hyperacetylation of H3 Lys 9 (H3K9). The most pronounced changes were observed at the repair site, with notable alterations in the acetylation pattern of histone H4. These findings reveal the importance of histone modifications in response to injury and indicate that modulation of BMAL1 and its associated epigenetic events could be therapeutically harnessed to improve skin regeneration.
Assuntos
Fatores de Transcrição ARNTL , Histonas , Camundongos , Animais , Histonas/metabolismo , Fatores de Transcrição ARNTL/genética , Fatores de Transcrição ARNTL/metabolismo , Ritmo Circadiano , Epigênese Genética , Camundongos KnockoutRESUMO
Pulp capping is a necessary procedure for preserving the vitality and health of the dental pulp, playing a crucial role in preventing the need for root canal treatment or tooth extraction. Here, we developed an electrospun gelatin methacryloyl (GelMA) fibrous scaffold incorporating beta-tricalcium phosphate (TCP) particles for pulp capping. A comprehensive morphological, physical-chemical, and mechanical characterization of the engineered fibrous scaffolds was performed. In vitro bioactivity, cell compatibility, and odontogenic differentiation potential of the scaffolds in dental pulp stem cells (DPSCs) were also evaluated. A pre-clinical in vivo model was used to determine the therapeutic role of the GelMA/TCP scaffolds in promoting hard tissue formation. Morphological, chemical, and thermal analyses confirmed effective TCP incorporation in the GelMA nanofibers. The GelMA+20%TCP nanofibrous scaffold exhibited bead-free morphology and suitable mechanical and degradation properties. In vitro, GelMA+20%TCP scaffolds supported apatite-like formation, improved cell spreading, and increased deposition of mineralization nodules. Gene expression analysis revealed upregulation of ALPL, RUNX2, COL1A1, and DMP1 in the presence of TCP-laden scaffolds. In vivo, analyses showed mild inflammatory reaction upon scaffolds' contact while supporting mineralized tissue formation. Although the levels of Nestin and DMP1 proteins did not exceed those associated with the clinical reference treatment (i.e., mineral trioxide aggregate), the GelMA+20%TCP scaffold exhibited comparable levels, thus suggesting the emergence of differentiated odontoblast-like cells capable of dentin matrix secretion. Our innovative GelMA/TCP scaffold represents a simplified and efficient alternative to conventional pulp-capping biomaterials. STATEMENT OF SIGNIFICANCE: Vital pulp therapy (VPT) aims to preserve dental pulp vitality and avoid root canal treatment. Biomaterials that bolster mineralized tissue regeneration with ease of use are still lacking. We successfully engineered gelatin methacryloyl (GelMA) electrospun scaffolds incorporated with beta-tricalcium phosphate (TCP) for VPT. Notably, electrospun GelMA-based scaffolds containing 20% (w/v) of TCP exhibited favorable mechanical properties and degradation, cytocompatibility, and mineralization potential indicated by apatite-like structures in vitro and mineralized tissue deposition in vivo, although not surpassing those associated with the standard of care. Collectively, our innovative GelMA/TCP scaffold represents a simplified alternative to conventional pulp capping materials such as MTA and Biodentine™ since it is a ready-to-use biomaterial, requires no setting time, and is therapeutically effective.
Assuntos
Materiais Biocompatíveis , Alicerces Teciduais , Alicerces Teciduais/química , Células Cultivadas , Materiais Biocompatíveis/química , Diferenciação Celular , Apatitas/farmacologia , Polpa DentáriaRESUMO
This study aimed to evaluate the effect of dentin hypersensitivity treatments on immediate and long-term shear bond strength (SBS) of composite restorations. Ninety non-carious extracted human molars were cut to expose dentin, which was embedded in acrylic resin, and randomly divided into three groups (n = 30/group) according to surface treatment: 1) no treatment (C and C*; control); 2) silver diamine fluoride with potassium iodide (SDF/KI and SDF/KI*; Riva Star); and 3) nano-hydroxyapatite (nHAp and nHAp*; PrevDent). The specimens were etched through the etch-and-rinse technique, followed by universal adhesive application and resin composite cylinders (2.38 mm in diameter × 3.5 mm high). The SBS was tested immediately (24 h after the restoration) and after thermocycling (*) (5000 cycles, 5 °C to 55 °C) at a 0.5 mm/min crosshead speed using a universal testing machine. A stereomicroscope was used to evaluate the mode of failure, and representative scanning electron microscopy (SEM) images were also acquired. Data normality was verified, and two-way ANOVA and Tukey's post hoc tests were performed for multiple comparisons (α = 0.05). The control group presented the highest SBS (27.10 MPa), while SDF/KI* had the lowest values (6.87 MPa). nHAp-based desensitizer exhibited higher SBS than SDF/KI for both immediate (22.6 MPa) and thermocycled (19.03 MPa) conditions. No intragroup difference was evidenced between immediate and thermocycled samples for any group. Most specimens for the C and nHAp groups presented mixed failure, while the SDF/KI groups presented comparable adhesive and mixed failures. The SBS of adhesive restorations after the application of desensitizing agents is material dependent, where SDF/KI reduces SBS values below the acceptable minimum bond strength, while the nHAp application meets the minimally required bond strength.
Assuntos
Colagem Dentária , Adesivos Dentinários , Humanos , Adesivos Dentinários/química , Colagem Dentária/métodos , Dentina , Pirenos , Teste de Materiais , Cimentos de Resina/química , Resistência ao CisalhamentoRESUMO
Keeping sodium hypochlorite (NaOCl) within the root canal is challenging in regenerative endodontics. In this study, we developed a drug delivery system using a gelatin methacryloyl (GelMA) hydrogel incorporated with aluminosilicate clay nanotubes (HNTs) loaded with NaOCl. Pure GelMA, pure HNTs, and NaOCl-loaded HNTs carrying varying concentrations were assessed for chemo-mechanical properties, degradability, swelling capacity, cytocompatibility, antimicrobial and antibiofilm activities, and in vivo for inflammatory response and degradation. SEM images revealed consistent pore sizes of 70-80 µm for all samples, irrespective of the HNT and NaOCl concentration, while HNT-loaded hydrogels exhibited rougher surfaces. The hydrogel's compressive modulus remained between 100 and 200 kPa, with no significant variations. All hydrogels demonstrated a 6-7-fold mass increase and complete degradation by the seventh day. Despite an initial decrease in cell viability, all groups recovered to 65-80% compared to the control. Regarding antibacterial and antibiofilm properties, 12.5 HNT(Double) showed the highest inhibition zone on agar plates and the most significant reduction in biofilm compared to other groups. In vivo, the 12.5 HNT(Double) group displayed partial degradation after 21 days, with mild localized inflammatory responses but no tissue necrosis. In conclusion, the HNT-NaOCl-loaded GelMA hydrogel retains the disinfectant properties, providing a safer option for endodontic procedures without harmful potential.
RESUMO
Objectives: The goal of this systematic review was to analyze, in randomized controlled clinical trials (RCTs), regenerative techniques used to treat peri-implantitis (PI). Methods: Three databases (PubMed/Medline, EMBASE, and On-Line Knowledge Library) were accessed, applying the PICO strategy (Population [P], Intervention [I], Comparison [C], and Outcomes [O]), with the following focused questions: (i) "In patients who received regenerative treatments for peri-implantitis (P), is the regenerative surgical treatment (I) clinically effective and predictable compared to non-regenerative (C) to treat PI (O)?"; and (ii) "In patients who received regenerative treatments for peri-implantitis (P), the regenerative approach (I), compared to non-regenerative (C), significantly increase the prognosis and implant survival rate in the mid- and long-term (O)?" The inclusion criteria were RCTs published in English between 2012 and 2022, with at least a one-year follow-up, which applied regenerative techniques to treat peri-implantitis. Cochrane's collaboration tool for assessing the risk of bias was used. Main results: Nine articles were included with 404 patients (225 females and 179 males; mean age of 60.44 years). One study evaluated patients after 48 months and another after 88 months. The techniques and devices used were: (i) implantoplasty with Er:YAG laser, (ii) blood concentrate (growth factors), and (iii) EMD, with no statistically significant outcome. Two studies considered the use of titanium granules with a significant increase in radiographic bone identification, whereas regenerative techniques with bone graft (autogenous, alloplastic, and xenograft) were the majority chosen, associated or not, with a collagen membrane. Xenograft had better results radiographically when compared to the autogenous bone graft and presented better results for bone level. There was an overall decrease in bleeding on probing, independent of the control or test group, and a reduction in pocket depth in the groups analyzed. Titanium granules, EMD, Er:YAG laser, and CGF had non-significant results; better results were observed when using bone grafts. The RoB showed a low risk in four studies (44.44%), three with moderate (33.33%), and two with high risk (22.23%). Conclusion: Surgical regenerative treatment was a predictable option in the management of PI and in improving the clinical parameters of peri-implant tissues in the short term, mainly when using porous titanium granules, alloplastic bone grafts, and xenografts.
RESUMO
The objective of this research was to create and appraise biodegradable polymer-based nanofibers containing distinct concentrations of calcium trimetaphosphate (Ca-TMP) for periodontal tissue engineering. Poly(ester urea) (PEU) (5% w/v) solutions containing Ca-TMP (15%, 30%, 45% w/w) were electrospun into fibrous scaffolds. The fibers were evaluated using SEM, EDS, TGA, FTIR, XRD, and mechanical tests. Degradation rate, swelling ratio, and calcium release were also evaluated. Cell/Ca-TMP and cell/scaffold interaction were assessed using stem cells from human exfoliated deciduous teeth (SHEDs) for cell viability, adhesion, and alkaline phosphatase (ALP) activity. Analysis of variance (ANOVA) and post-hoc tests were used (α = 0.05). The PEU and PEU/Ca-TMP-based membranes presented fiber diameters at 469 nm and 414-672 nm, respectively. Chemical characterization attested to the Ca-TMP incorporation into the fibers. Adding Ca-TMP led to higher degradation stability and lower dimensional variation than the pure PEU fibers; however, similar mechanical characteristics were observed. Minimal calcium was released after 21 days of incubation in a lipase-enriched solution. Ca-TMP extracts enhanced cell viability and ALP activity, although no differences were found between the scaffold groups. Overall, Ca-TMP was effectively incorporated into the PEU fibers without compromising the morphological properties but did not promote significant cell function.
RESUMO
Major advances in the field of periodontal tissue engineering have favored the fabrication of biodegradable membranes with tunable physical and biological properties for guided bone regeneration (GBR). Herein, we engineered innovative nanoscale beta-tricalcium phosphate (ß-TCP)-laden gelatin methacryloyl/polycaprolactone (GelMA/PCL-TCP) photocrosslinkable composite fibrous membranes via electrospinning. Chemo-morphological findings showed that the composite microfibers had a uniform porous network and ß-TCP particles successfully integrated within the fibers. Compared with pure PCL and GelMA/PCL, GelMA/PCL-TCP membranes led to increased cell attachment, proliferation, mineralization, and osteogenic gene expression in alveolar bone-derived mesenchymal stem cells (aBMSCs). Moreover, our GelMA/PCL-TCP membrane was able to promote robust bone regeneration in rat calvarial critical-size defects, showing remarkable osteogenesis compared to PCL and GelMA/PCL groups. Altogether, the GelMA/PCL-TCP composite fibrous membrane promoted osteogenic differentiation of aBMSCs in vitro and pronounced bone formation in vivo. Our data confirmed that the electrospun GelMA/PCL-TCP composite has a strong potential as a promising membrane for guided bone regeneration.