RESUMO
A lanthanum oxide (La2O3)-ZnO nanostructured material was synthesized in the proposed study with different La2O3 concentrations, 0.001 g to 5 g (named So to S7), using the combustion method. X-ray diffraction (XRD), scanning electron microscopy (SEM), and Fourier transformation infrared spectroscopy (FT-IR) were utilized for investigating the structure, morphology, and spectral studies of the La2O3- ZnO nanomaterials, respectively. The results obtained from previous techniques support ZnO's growth from crystalline to nanoparticles' fine structure by changing the concentrations of lanthanum oxide (La2O3) dopants in the host matrix. The percentage of ZnO doped with La- influences the ZnO photocatalytic activity. SEM analysis confirmed the grain size ranged between 81 and 138 nm. Furthermore, UV-Vis diffuse reflectance spectroscopy was performed to verify the effects of La2O3 dopants on the linear optical properties of the nano-composite oxides. There was a variation in the energy bandgaps of La2O3-ZnO nanocomposites, increasing the weight concentrations of lanthanum dopants. The AC electrical conductivity, dielectric properties, and current-voltage properties support the enactment of the electrical characteristics of the ZnO nanoparticles by adding La2O3. All the samples under investigation were used for photodegradation with Rhodamine B (RhB) and Methylene Blue (MB). In less than 30 min of visible light irradiation, S4 (0.5 g) La2O3-ZnO reached 99% of RhB and MB degradation activity. This study showed the best photocatalytic effect for RhB and MB degradation of 0.13 and 0.11 min-1 by 0.5 g La2O3-ZnO. Recycling was performed five times for the nanocatalysts that displayed up to 98 percent catalytic efficiency for RhB and MB degradation in 30 min. The prepared La2O3-ZnO nanostructured composites are considered novel candidates for various applications in biomedical and photocatalytic studies.
RESUMO
An efficient and environmentally friendly combustion technique was employed to produce ZnO nanopowders with different Eu concentrations (from 0.001 g to 5 g). The structural morphology of the Eu2O3-ZnO nanocomposites was examined using XRD, SEM, and infrared spectroscopy (FT-IR). In addition, UV-Vis diffuse reflectance spectroscopy was also used to investigate the effects of europium (Eu) dopant on the optical behaviors and energy bandgaps of nano-complex oxides. The photocatalytic degradation efficiency of phenol and methylene blue was investigated using all the prepared Eu2O3-ZnO nanostructured samples. Photocatalytic effectiveness increased when europium (Eu) doping ratios increased. After adding moderate Eu, more hydroxyl radicals were generated over ZnO. The best photocatalyst for phenol degradation was 1 percent Eu2O3-ZnO, while it was 0.5 percent Eu2O3-ZnO for methylene blue solutions. The obtained Eu2O3-doped ZnO nanostructured materials are considered innovative, promising candidates for a wide range of nano-applications, including biomedical and photocatalytic degradation of organic dyes and phenol.
RESUMO
The incorporation of tungsten trioxide (WO3) by various concentrations of graphitic carbon nitride (g-C3N4) was successfully studied. X-ray diffraction (XRD), Scanning Electron Microscope (SEM), and Diffused Reflectance UV-Vis techniques were applied to investigate morphological and microstructure analysis, diffused reflectance optical properties, and photocatalysis measurements of WO3/g-C3N4 photocatalyst composite organic compounds. The photocatalytic activity of incorporating WO3 into g-C3N4 composite organic compounds was evaluated by the photodegradation of both Methylene Blue (MB) dye and phenol under visible-light irradiation. Due to the high purity of the studied heterojunction composite series, no observed diffraction peaks appeared when incorporating WO3 into g-C3N4 composite organic compounds. The particle size of the prepared composite organic compound photocatalysts revealed no evident influence through the increase in WO3 atoms from the SEM characteristic. The direct and indirect bandgap were recorded for different mole ratios of WO3/g-C3N4, and indicated no apparent impact on bandgap energy with increasing WO3 content in the composite photocatalyst. The composite photocatalysts' properties better understand their photocatalytic activity degradations. The pseudo-first-order reaction constants (K) can be calculated by examining the kinetic photocatalytic activity.