Enhanced Photodynamic Selectivity of Nano-Silica-Attached Porphyrins Against Breast Cancer Cells.

The synthesis and characterization of bare silica (4 nm in diameter) nanoparticle-attached meso-tetra(N-methyl-4-pyridyl)porphine (SiO(2)-TMPyP, 6 nm in diameter) are described for pH-controllable photosensitization. Distinguished from organosilanes, SiO(2) nanoparticles were functionalized as a potential quencher of triplet TMPyP and/or singlet oxygen ((1)O(2)) at alkaline pH, thereby turning off sensitizer photoactivity. In weak acidic solutions, TMPyP was released from SiO(2) surface for efficient production of (1)O(2). By monitoring (1)O(2) luminescence at 1270 nm, quantum yields of (1)O(2) production were found to be pH-dependent, dropping from ~ 0.45 in a pH range of 3-6 to 0.08 at pH 8-9, which is consistent with pH-dependent adsorption behavior of TMPyP on SiO(2) surface. These features make bare SiO(2)-attached cationic porphyrin a promising candidate for use in PDT for cancer treatment in which efficient (1)O(2) production at acidic pH and sensitizer deactivation at physiological pH are desirable. The enhanced therapeutic selectivity was confirmed by 3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide (MTT) tests and trypan blue exclusion tests of cell viability in breast cancer cell lines. Bimolecular quenching rate constants of (1)O(2) by free TMPyP, SiO(2) and SiO(2)-TMPyP nanoparticles were also determined.

pH-responsive, TiO2-attached porphyrin for singlet oxygen production in an aqueous solution.

A pH-responsive, TiO2-attached sensitizer was prepared based on the adsorption of 5,10,15,20-tetrakis(4-carboxyphenyl)porphyrin (TCPP) onto TiO2 nanoparticles. This colloidally dispersed TiO2-attached TCPP behaves as a single-phase colloidal sensitizer at pH 1.0-3.3 with quantum yields of singlet oxygen production (Phi(Delta)) between 0.20 and 0.25, as a heterogeneous particle sensitizer at pH 3.5-6.0 with Phi(Delta) between 0.25 and 0.50, and as homogeneous free TCPP molecules in alkaline solutions with Phi(Delta) = 0.53. The changes in Phi(Delta) are fully consistent with pH-dependent adsorption of TCPP onto the TiO2 surface. Recovery yields of 99.8% for TCPP and 98.8% for TiO2 were obtained from 1.4 mM TiO2-attached TCPP. We attribute its photosensitization ability to retaining TCPP solubility on the TiO2 surface and, hence, activity. This novel system shows a potential to bridge the gap between easily recoverable and highly efficient sensitizers.