Correlation between fluoride release, surface hardness and diametral tensile strength of restorative glass ionomer cements.

Background: The aim of this study was to determine if there is a correlation between fluoride release, surface hardness, and diametral tensile strength of restorative glass ionomer cements (GICs). Material and Methods: Conventional (Riva Self Cure) and resin-modified (Riva Light Cure) GICs were used. Thirty-four samples (ø 6 x 3 mm) were prepared for each cement. The kinetics of fluoride release (n=4) was evaluated over 28 days using a fluoride-selective electrode (ISE 4010-C00). The analysis of surface hardness (n=10) was performed using a microhardness tester (Shimadzu HMV-2000, Japan) with a Knoop indenter and a load of 25 gf for 30 seconds. The diametral tensile strength test (n=10) was conducted on a universal testing machine at a speed of 0.75 mm/min. Fluoride release data were analyzed by two-way repeated measures ANOVA and Bonferroni post hoc test, while independent t-test was used for other analyses (α=0.05). Results: Overall, the groups showed higher fluoride release until day 7 and a progressive decrease until day 28. On day 1 and day 21, Riva Self Cure showed a higher level of release than Riva Light Cure (p=0.026). Riva Light Cure showed higher diametral tensile strength (p<0.0001) and surface hardness (p=0.034) than Riva Self Cure. A negative correlation was found, indicating that higher fluoride release is associated with lower surface hardness and diametral tensile strength. Conclusion: Fluoride release and mechanical performance are related properties of GICs, and these properties exhibit different values depending on the type of material. Resin-modified GIC release less fluoride but exhibit better mechanical performance compared to conventional GIC. Key words:Diametral Tensile Strength, Fluoride, Glass Ionomer Cement, Surface Hardness.

Er,Cr:YSGG and 980nm diode lasers influence dentin surface volume after cariogenic challenge: in vitro study.

This study aimed to evaluate the influence of the Er,Cr:YSGG irradiation and 980-nm diode lasers on the surface roughness (SR) and volume loss (VL) of dentin subjected to cariogenic challenge. Subsequently, 130 specimens of bovine dentin were divided into the following 13 groups: NT: no treatment; FG: fluoride gel; FV: fluoride varnish; Di: 980-nm diode; Di + FG; Di + FV; FG + D; FV + Di; Er: Er,Cr:YSGG; Er + FG; Er + FV; FG + Er and FV + Er. Er,Cr:YSGG laser parameters were as follows: 0.25 W; 5.0 Hz; 4.46 J/cm2 without water and 55% air. Furthermore, the 980-nm diode laser parameters were 2.0 W; 2.0 Hz; 21.41 J/cm2. The samples from each group were subjected to pH cycling. A confocal laser scanning microscope was used to evaluate SR and VL. Difference between the volume of the reference and treated areas + DES/RE was used to determine SR and VL. The mean values of the different groups were subjected to analysis of variance and Tukey's post-hoc test. The VL values were analyzed using the Kruskal-Wallis and Dunn post-hoc test (p < 0.05). The SR of the reference area did not show a statistically significant 1807-3107-bor-38-e025treatment and cariogenic challenge (p > 0.05). Moreover, VL in the FV + Di and FV + Er groups showed a statistically significant difference compared with areas submitted to different types of treatment and cariogenic challenge (p > 0.05). Er,Cr:YSGG and 980-nm diode lasers associated with fluoride varnishes decreased dentin VL in bovine teeth submitted to cariogenic challenge.

Influence of Er:YAG and ND:YAG laser irradiation and fluoride application on surface roughness and dentin surface wear after erosive challenge - An in vitro study.

Background: To evaluate the effectiveness of Er:YAG and Nd:YAG laser on dentin hypersensitivity prevention, associated or not to acidulated phosphate fluoride (APF) after erosive challenge. Material and Methods: 104 specimens were obtained from bovine dentine and divided into groups (n=13): G1: Er:YAG; G2: Er:YAG followed by application of APF; G3: application of APF followed by Er:YAG, simultaneously; G4: Nd:YAG; G5: Nd:YAG followed by application of APF; G6: application of APF followed by Nd:YAG, simultaneously; G7:application of APF; G8: untreated. The parameters for Er:YAG were:10s, distance of 4mm, water cooling flow of 2mL/min, 2Hz, 3.92J/cm2. For the Nd:YAG: 10s, distance of 1mm, without cooling, 10Hz, 70.7J/cm2. The erosive drink was a cola at 4°C, 3×/day for 1 minute, for 5 days. Roughness and wear analysis were done in confocal laser microscope. Data were statistically analyzed (α=0.05). Results: As regards roughness, there was no statistically difference among the groups. The groups irradiated with Er:YAG had a volume loss lower. G6 showed higher values than the groups irradiated with Er:YAG and lower than the other groups. The other groups irradiated with Nd:YAG showed similar wear results to the control. Conclusions: The Er:YAG laser showed the lowest volume loss from wear analysis, suggesting the increased the acid resistance of dentin. Key words:Dentine sensitivity, Lasers, Sodium fluoride.

Influence of preventive remineralizing techniques on surface roughness and volume loss of dentin submitted to erosive and/or abrasive challenges.

Background: The objective this study was to evaluate the influence of preventive remineralizing techniques on surface roughness and volume loss of dentin submitted to erosive and/or abrasive challenges. Material and Methods: One hundred and eighty specimens of bovine root dentin were made; half of each was isolated (without treatment - WT) and half was subjected to the following remineralizing techniques: fluoride varnish (FV); Regenerate Boosting Serum® (RBS); Er,Cr:YSGG laser (L); fluoride varnish+laser (FV+L); Regenerate Boosting Serum®+laser (RBS+L). The specimens were submitted to erosive, abrasive and erosive followed by abrasive challenge. Erosion was carried out for 5 minutes, twice a day for 10 days. Abrasion was performed with an electric toothbrush and slurry solution for 60 seconds. The evaluation was performed by confocal laser scanning microscopy. Analysis of variance and Tukey tests were used for surface roughness; volume loss comparison was performed using the Kruskal-Wallis test and Dunn's post-hoc (p<0.05). Results: There was no statistically significant difference in the surface roughness of the reference area in relation to the areas submitted to different types of treatment and challenges (p>0.05). Regarding volume loss, the untreated group submitted to erosive/abrasive challenges showed greater percentage of volume loss compared to the other groups (p<0.05). Conclusions: It is concluded that preventive remineralizing techniques are effective in maintaining dentin volume after erosive/abrasive challenges. Key words:YSGG lasers, Dentin, Erosion, Tooth Abrasion.

Er,Cr:YSGG and 980nm diode lasers influence dentin surface volume after cariogenic challenge: in vitro study

Abstract This study aimed to evaluate the influence of the Er,Cr:YSGG irradiation and 980-nm diode lasers on the surface roughness (SR) and volume loss (VL) of dentin subjected to cariogenic challenge. Subsequently, 130 specimens of bovine dentin were divided into the following 13 groups: NT: no treatment; FG: fluoride gel; FV: fluoride varnish; Di: 980-nm diode; Di + FG; Di + FV; FG + D; FV + Di; Er: Er,Cr:YSGG; Er + FG; Er + FV; FG + Er and FV + Er. Er,Cr:YSGG laser parameters were as follows: 0.25 W; 5.0 Hz; 4.46 J/cm2 without water and 55% air. Furthermore, the 980-nm diode laser parameters were 2.0 W; 2.0 Hz; 21.41 J/cm2. The samples from each group were subjected to pH cycling. A confocal laser scanning microscope was used to evaluate SR and VL. Difference between the volume of the reference and treated areas + DES/RE was used to determine SR and VL. The mean values of the different groups were subjected to analysis of variance and Tukey's post-hoc test. The VL values were analyzed using the Kruskal-Wallis and Dunn post-hoc test (p < 0.05). The SR of the reference area did not show a statistically significant 1807-3107-bor-38-e025treatment and cariogenic challenge (p > 0.05). Moreover, VL in the FV + Di and FV + Er groups showed a statistically significant difference compared with areas submitted to different types of treatment and cariogenic challenge (p > 0.05). Er,Cr:YSGG and 980-nm diode lasers associated with fluoride varnishes decreased dentin VL in bovine teeth submitted to cariogenic challenge.

The long-term effect of sub-boiling water on dental unit waterlines and its ability to control cross-contamination in dentistry.

This study investigated the effect of water at high temperature on the physical and mechanical properties of polyurethane and on biofilm removal, aiming for its applicability in dental unit waterlines. The evaluations were carried out after simulating a 1-year period of daily immersion and measured changes in color, microhardness, surface roughness, and tensile strength before and after reproducing a disinfection protocol. For antibiofilm activity measurement, fragments of waterline were contaminated with Pseudomonas aeruginosa and submitted to the disinfection protocols. Relative to effects on the physical and mechanical properties, immersion in water at 60°C did not promote changes in color and tensile strength. However, lower values were observed for microhardness and increased values for surface roughness. Regarding antibiofilm action, water at 60°C significantly reduced the microbial load and promoted substantial changes in cells morphology. In conclusion, disinfection with water at 60°C demonstrated possible application in controlling cross-contamination in dentistry.

Effects of Different Forms of Denture Adhesives on Biofilm Formation, Adhesive Strength and Hygiene of Complete Dentures.

PURPOSE: To evaluate the effect of different forms of denture adhesives on the formation of biofilm and on adhesive strength, as well as the effectiveness of hygiene protocols for their removal. MATERIALS AND METHODS: Samples of the heat-cured polymethyl methacrylate denture base resin were made and divided into four groups: control (no adhesive), ultra Corega cream, Corega strip adhesive, and ultra Corega powder (GlaxoSmithKline). Biofilm formation was evaluated by counting colony-forming units and fluorescence microscopy. To evaluate the effectiveness of the hygiene protocols, the samples were divided into five subgroups: brushing with distilled water; brushing with Protex soap; brushing with Colgate toothpaste; immersion in Corega Tabs; and immersion in Corega Tabs followed by brushing with the solution itself. The remaining adhesive was quantified with ImageJ software. The adhesive strength was tested at different time intervals after application. After verifying the data distribution using Shapiro-Wilk test, parametric or nonparametric analysis was applied (α = .05). RESULTS: Candida albicans formed more biofilm in strip (P = .007) and powder (P = .001), Pseudomonas aeruginosa in cream (P < .001) and powder (P < .001), and Staphylococcus aureus in strip (P < .001). All forms of the adhesives promoted higher biofilm formation when compared to control (P = .003). Brushing with Colgate and Protex was most effective for removing the adhesives (P < .05). Independently, Powder had the highest adhesive strength (P < .05). Only Strip showed a change in adhesive strength, with higher values after 3 hours of application (P = .004). CONCLUSION: Daily treatments with mechanical cleaning of the prosthesis are important for removing the adhesives, since the presence of this material can favor biofilm accumulation. The adhesive strength may vary depending on the commercial type, but all forms can be effective in retaining prostheses for a satisfactory period of time.

Influence of glucose supplementation on biofilm formation of Candida albicans and Candida glabrata isolated from diabetic and non-diabetic individuals.

OBJECTIVE: This study evaluated the effect of different glucose concentration on biofilm formation of Candida albicans and Candida glabrata strains isolated from diabetic and non-diabetic individuals. METHODS: The study was divided into two stages: (I) selection and identification of 48 C. albicans and C. glabrata strains by polymerase chain reaction followed by restriction fragment length polymorphism analysis (PCR/RFLP); (II) evaluation of biofilm formation by means of viability rates (colony-forming units), biofilm dry matter (mg) and biofilm-covered areas (µm2). Statistical comparisons were performed through nonparametric analysis of longitudinal data in factorial experiments with pairwise comparisons using Friedman Conover's test (α = 0.05). RESULTS: All the Candida spp. had their identifications confirmed by PCR/RFLP. C. albicans biofilm of strains from diabetic individuals cultivated in different glucose concentration showed higher viability rates than strains from non-diabetic individuals. No difference was observed on viability of C. glabrata biofilm. Regarding biofilm dry matter, C. albicans biofilm of strains from diabetic individuals cultivated in different glucose concentration showed lower amount in weight than strains from non-diabetic individuals. In C. glabrata strains, this result was only observed in biofilms cultivated with no glucose supplementation. With regard to biofilm-covered areas, only glucose supplementation and non-diabetic condition showed a positive effect on C. albicans biofilm development, and no condition affected C. glabrata biofilm formation. CONCLUSION: The strain type (C. albicans and C. glabrata) isolated from diabetic and non-diabetic individuals influenced on biofilm formation, but glucose supplementation did not.

Cytotoxicity and Elemental Release of Dental Acrylic Resin Modified with Silver and Vanadium Based Antimicrobial Nanomaterial / Citotoxicidade e Liberação Elementar de Resina Acrílica Odontológica Modificada com Nanomaterial Antimicrobiano a Base de Prata e Vanádio

The acrylic resin used for the prosthesis base accumulates biofilm, causing diseases such as stomatitis. The addition of some nanoparticles promotes antimicrobial action. This study incorporated the nanostructured silver vanadate decorated with silver nanoparticles (AgVO3) to the acrylic resin by two methods and evaluated the cytotoxicity for human gingival fibroblasts (HGF) and the released silver and vanadium ions. The concentrations of 0.5, 1, 2.5, and 5% of AgVO3 was incorporated by vacuum spatulation and polymeric film. The vacuum spatulation was performed for 60 s using the Turbomix equipment, and the polymeric film was obtained from the polymer solubilization in chloroform, the film was subjected to a cryogenic grinding, and the powder obtained was manually mixed at the monomer. HGF cell viability was assessed after 24 hours, 7 and 14 days by the MTT assay. The release of silver (Ag) and vanadium (V) ions were quantified by inductively coupled plasma mass spectrometry after 30 days. Kruskal-Wallis and Dunn's test were applied (α = 0.05). The HGF viability was inversely proportional to the incubation time. Both incorporation techniques and the negative and positive control groups presented significant statistical differences (p<0.05). The experimental groups presented no statistical difference compared to the negative control (p>0.05), except the vacuum spatulation group with 5% of AgVO3 that showed greater viability than the negative control (p=0.013) in 24 hours. The release of Ag and V ions was proportional to the concentration of AgVO3 The 5% group presented a significant difference compared to the other groups (p<0.05). In conclusion, the acrylic resin with and without the AgVO3 incorporation had a small cytotoxic potential for HGF in 24 hours, with a lower viability in longer contact times; the release of Ag and V ions was proportional to the concentration of AgVO3, not influencing cell viability. (AU)

A resina acrílica utilizada para a base da prótese acumula biofilme, causando doenças como a estomatite. A adição de algumas nanopartículas promove ação antimicrobiana. Este estudo incorporou o vanadato de prata nanoestruturado decorado com nanopartículas de prata (AgVO3) à resina acrílica por dois métodos e avaliou a citotoxicidade para fibroblastos gengivais humanos (HGF) e os íons prata e vanádio liberados. As concentrações de 0,5%, 1%, 2,5% e 5% de AgVO3 foram incorporadas por espatulação a vácuo e filme polimérico. A espatulação a vácuo foi realizada por 60 s no equipamento Turbomix, e o filme polimérico foi obtido a partir da solubilização do polímero em clorofórmio, o filme foi submetido a uma moagem criogênica e o pó obtido foi misturado manualmente ao monômero. A viabilidade celular de HGF foi avaliada após 24 horas, 7 e 14 dias pelo ensaio de MTT. A liberação de íons prata (Ag) e vanádio (V) foi quantificada por espectrometria de massa com plasma indutivamente acoplado após 30 dias. Os testes de Kruskal-Wallis e Dunn foram aplicados (α=0,05). A viabilidade de HGF foi inversamente proporcional ao tempo de incubação. As técnicas de incorporação e os grupos controle negativo e positivo apresentaram diferença estatisticamente significante (p<0,05). Os grupos experimentais não apresentaram diferença estatística em relação ao controle negativo (p>0,05), exceto o grupo de espatulação a vácuo com 5% de AgVO3 que apresentou maior viabilidade que o controle negativo (p = 0,013) em 24 horas. A liberação de íons Ag e V foi proporcional à concentração de AgVO3. O grupo 5% apresentou diferença significativa em relação aos demais grupos (p <0,05). Em conclusão, a resina acrílica com e sem a incorporação de AgVO3 apresentou um pequeno potencial citotóxico para o HGF em 24 horas, com menor viabilidade nos tempos de maior contato, e a liberação de íons Ag e V foi proporcional à concentração de AgVO3, não influenciando na viabilidade celular. (AU)

Influence of Er,Cr:YSGG laser on root dentin submitted to erosive and/or abrasive challenges.

This study evaluated how Er,Cr:YSGG laser, associated or not with 5% fluoride varnish, influences the surface roughness and volume loss of bovine root dentin submitted to erosive and/or abrasive wear. One hundred and twenty dentin specimens were divided into the groups: without preventive treatment (WPT), 5% fluoride varnish (FV); Er,Cr:YSGG laser irradiation (L), and varnish combined with laser (FV + L). The specimens (n = 10) were subdivided into: 1 = erosion (E); 2 = abrasion (A); and 3 = erosion followed by abrasion (E + A). The erosive solution used was a soft-drink (pH = 2.42 at 4ºC) applied in 5-min cycles twice a day for 10d. Abrasive wear involved brushing for 60s with an electric brush (1,600-oscillations/s) at a load of 2.0N. Surface roughness and volume loss were evaluated using a laser scanning confocal microscope. Roughness data were submitted to one-way ANOVA and Tukey post-hoc test. For volume loss, the Kruskal-Wallis and Dunn's post-hoc tests were used (α = 5%). The lowest values of roughness were found in the control areas of all subgroups (p > 0.05). In the experimental area, the [(WPT) + (E+A)] subgroup had a significantly higher roughness (5.712 ± 0.163 µm 2 ) than the other subgroups (p < 0.05). The L and (FV + L) groups had statistically similar roughness, regardless of the type of wear. The (FV + L) group had the lowest volume loss, regardless of the type of wear performed: [(FV + L) + (E)] = 7.5%, [(FV + L) + (A) = 7.3%, and [(FV + L) + (E + A)] = 8.1%. The subgroup [(WPT) + (E + A)] had the highest volume loss (52.3%). The proposed treatments were effective in controlling dentin roughness. Laser irradiation can be an effective method to increase root dentin resistance after challenges and limit problems related to non-carious lesions.

Comparison of oral microbiome profile of polymers modified with silver and vanadium base nanomaterial by next-generation sequencing.

This study aimed to evaluate two methods of the incorporation of nanostructured silver vanadate decorated with silver nanoparticles (AgVO3) into acrylic resin and characterize the profile of early and late microbial communities in class and family taxonomic level by pyrosequencing. The specimens were made by adding different concentrations of AgVO3 (1, 2.5, and 5%) to the heat-activated acrylic resin by two methods: vacuum spatulation (VS) and polymeric film (PF). A control group (0%) without AgVO3 was also obtained for both methods. After 24 h and 7 days of incubation in human saliva, biofilm samples were collected, DNA was extracted, and 16S rRNA genes were sequenced by the 454-Roche sequencing platform. Seventeen classes and 51 families of bacteria were identified. The abundance of Bacteroidia, Bacilli, Negativicutes, Fusobacteria and Betaproteobacteria classes decreased after 7 days of incubation, and Clostridia, Gammaproteobacteria, and unclassified bacteria increased. The Negativicutes and Betaproteobacteria classes were more abundant when the PF method was used, and Gammaproteobacteria was more abundant when VS was used. The incorporation of 5% AgVO3 promoted a reduction in the prevalence of Bacilli, Clostridia, Negativicutes, Betaproteobacteria, and unclassified bacteria, and increased Gammaproteobacteria. The addition of AgVO3 to acrylic resin altered the early and mature microbiome formed on the specimen surface, and the PF method presented a more favorable microbial profile than the VS method.

Influence of Er, Cr: YSGG laser on root dentin submitted to erosive and/or abrasive challenges

Abstract This study evaluated how Er,Cr:YSGG laser, associated or not with 5% fluoride varnish, influences the surface roughness and volume loss of bovine root dentin submitted to erosive and/or abrasive wear. One hundred and twenty dentin specimens were divided into the groups: without preventive treatment (WPT), 5% fluoride varnish (FV); Er,Cr:YSGG laser irradiation (L), and varnish combined with laser (FV + L). The specimens (n = 10) were subdivided into: 1 = erosion (E); 2 = abrasion (A); and 3 = erosion followed by abrasion (E + A). The erosive solution used was a soft-drink (pH = 2.42 at 4ºC) applied in 5-min cycles twice a day for 10d. Abrasive wear involved brushing for 60s with an electric brush (1,600-oscillations/s) at a load of 2.0N. Surface roughness and volume loss were evaluated using a laser scanning confocal microscope. Roughness data were submitted to one-way ANOVA and Tukey post-hoc test. For volume loss, the Kruskal-Wallis and Dunn's post-hoc tests were used (α = 5%). The lowest values of roughness were found in the control areas of all subgroups (p > 0.05). In the experimental area, the [(WPT) + (E+A)] subgroup had a significantly higher roughness (5.712 ± 0.163 μm 2 ) than the other subgroups (p < 0.05). The L and (FV + L) groups had statistically similar roughness, regardless of the type of wear. The (FV + L) group had the lowest volume loss, regardless of the type of wear performed: [(FV + L) + (E)] = 7.5%, [(FV + L) + (A) = 7.3%, and [(FV + L) + (E + A)] = 8.1%. The subgroup [(WPT) + (E + A)] had the highest volume loss (52.3%). The proposed treatments were effective in controlling dentin roughness. Laser irradiation can be an effective method to increase root dentin resistance after challenges and limit problems related to non-carious lesions.

Cytotoxicity and release ions of endodontic sealers incorporated with a silver and vanadium base nanomaterial.

The modification of endodontic sealers with nanoparticles to confer antimicrobial activity allow greater effect, with interaction at a molecular level. The nanostructured silver vanadate decorated with silver nanoparticles (AgVO3) is a nanomaterial unprecedented in dentistry for this application. This study incorporated the AgVO3 into three endodontic sealers of different compositions and evaluate the cytotoxicity and release of compounds. The groups of commercially available AH Plus, Sealer 26, and Endomethasone N and groups of the same sealers with incorporated AgVO3 (at concentrations 2.5, 5, 10%) were prepared, and extracts of the specimens were obtained for 24 h. The cell viability (cytotoxicity) of human gingival fibroblasts (HGF) was assessed after 24 h, 7 and 14 days. Silver (Ag+) and vanadium (V4+/V5+) ion release was quantified after 24 h by ICP-MS. Data were analyzed by Kruskal-Wallis and Dunn's post-hoc (α = 0.05). The cell viability was inversely proportional to treatment time. The Sealer 26 and Endomethasone N groups were cytotoxic for HGF cells, regardless of the incorporation of the AgVO3 (p > 0.05), and the incorporation reduced cell viability of AH Plus (p < 0.05). The release of ions was proportional to the concentration of AgVO3. AH Plus released more Ag+ ions, and Sealer 26 and Endomethasone N releases more V4+/V5+ ions. In conclusion, it was not possible to confirm the influence of AgVO3 on HGF cell viability to Sealer 26 and Endomethasone N, however, nanomaterial influenced cell-viability to AH Plus, so the commercial sealers can be cytotoxic in synergy with the nanomaterial. The release of Ag+ and V4+/V5+ was proportional to the AgVO3 incorporated.

Effects of Denture Cleansing Solutions on Different Materials Used for Fabrication of Polymer Attachment Components.

AIMS: To evaluate the effects of different cleansing solutions on the physical-mechanical properties (roughness, surface hardness, and fatigue resistance) of three polymeric materials used to manufacture retentive attachments for overdentures. MATERIALS AND METHODS: The roughness and surface hardness analyses each employed 150 specimens measuring . 9 mm × 2 mm in thickness (polyacetal, polytetrafluoroethylene [PTFE], and polyethylene terephthalate [PET]; n = 50 each). For fatigue resistance analysis, 180 retentive attachments measuring 4 mm × 3 mm in height (n = 60 each) were used. The properties were evaluated before and after immersion in different cleansing solutions: distilled water, alkaline peroxide, 0.5% sodium hypochlorite (NaOCl), and Listerine. After the data distribution was verified using Shapiro-Wilk test, parametric or nonparametric analysis was applied (α = .05). RESULTS: The use of NaOCl caused a significant alteration in the roughness of the materials (P = .011), with a reduction in roughness in polyacetal and an increase in PTFE. The type of solution also influenced the surface hardness (P = .036); with the exception of distilled water, the other solutions promoted increased hardness. During the 24-month period, immersion in water, peroxide, and NaOCl (0.5%) caused increased fatigue resistance (P < .05) of the PET attachments. The immersion protocol resulted in greater fatigue resistance (P < .05) in polyacetal, while PTFE was not affected (P > .05). CONCLUSION: Regarding the physical-mechanical properties evaluated, the polymers PET, polyacetal, and PTFE were susceptible to cleansing solutions.

Effect of Thermomechanical Fatigue on Shear Strength between a Conventional and an Experimental Polymer for Prosthetic Application / Efeito da Fadiga Termomecânica na Resistência ao Cisalhamento Entre um Polímero Convencional e um Polímero Experimental para Aplicação Protética

The incorporation of antimicrobial agents may influence the mechanical properties of acrylic resins. Thus, the use of these agents only in regions of dental prostheses subject to greater contamination may be an alternative. This study evaluates the effect of thermomechanical fatigue on the bond strength between a conventional and an experimental acrylic resin incorporated with nanostructured silver vanadate decorated with silver nanoparticles (AgVO3). 60 specimens (Ø13mm x 23mm height) in self-curing resin were obtained and divided into groups according to the experimental resin incorporated with AgVO3 (Ø4mm x 6mm height): G1­Conventional x Conventional, G2­Conventional x 2.5% of AgVO3, G3­Conventional x 5% of AgVO3. Ten samples of each group were subjected to bond strength analysis after manufacture, and 10 were previously submitted to 1.200.000 cycles with 98N load and 2Hz/second frequency and alternating baths of 5 ºC, 37ºC and 55 ºC. The fracture area was analyzed. The data were submitted to analysis of variance of two-factors with Bonferroni adjustment for post hoc comparisons (α=0.05) was used. The fatigue did not affect the bond strength (p=0.416), however, there was influence of the AgVO3 concentration on the bond strength between the resins (p=0.013). Mixed failures with adhesive predominance were observed in samples without AgVO3 and cohesive failures in samples with the nanomaterial. The use of AgVO3 can improve or maintain the bond strength between resins with no thermomechanical fatigue influence. (AU).

A incorporação de agentes antimicrobianos pode influenciar nas propriedades mecânicas de resinas acrílicas. Desta forma, o uso destes agentes apenas em regiões das próteses dentárias sujeitas a maior contaminação pode ser uma alternativa. Este estudo avalia o efeito da fadiga termomecânica na resistência de união entre uma resina acrílica convencional e uma experimental incorporada com vanadato de prata nanoestruturado decorado com nanopartículas de prata (AgVO3). Foram obtidos 60 espécimes (Ø13mm x 23mm de altura) em resina autopolimerizável, divididos em grupos de acordo com a resina experimental incorporada com AgVO3 (Ø4mm x 6mm de altura): G1-Convencional x Convencional, G2-Convencional x 2,5% de AgVO3, G3 -Convencional x 5% de AgVO3. Dez amostras de cada grupo foram submetidas à análise de resistência à união após a confecção e 10 foram submetidas previamente a 1.200.000 ciclos com carga de 98 N e frequência de 2Hz/segundo e banhos alternados de 5 ºC, 37 ºC e 55 ºC. A área de fratura foi analisada. Os dados foram submetidos à análise de variância de dois fatores com ajuste de Bonferroni para comparações pos hoc (α = 0,05). A fadiga não afetou a força de união (p=0,416), no entanto, houve influência da concentração de AgVO3 na resistência de união entre as resinas (p=0,013). Falhas mistas com predominância adesiva foram observadas nas amostras sem AgVO3 e falhas coesivas nas amostras contendo o nanomaterial. O uso de AgVO3 pode melhorar ou manter a resistência da união entre as resinas sem influência da fadiga termomecânica.

Influence of an Alternative Implant Design and Surgical Protocol on Primary Stability.

The purpose of thisin vitrostudy was to evaluate the influence of a new proposal of implant design and surgical protocol on primary stability in different bone densities. Four groups were tested (n=9): G1 - tapered, cone morse, Ø 4.3 mm x 10 mm in length (Alvim CM); G2 - experimental tapered; G3 - cylindrical, cone morse, Ø 4.0 mm x 11 mm in length (Titamax CM) and G4 - experimental cylindrical. The experimental implants were obtained from a design change in the respective commercial models. The insertion was performed in polyurethane (PU) blocks 0.24 g/cm3(20 pcf) and 0.64 g/cm3(40 pcf), according to different surgical protocols. The primary stability was measured by means of insertion torque (IT) and pullout test. Data were analyzed by ANOVA, Tukey's test (α=0.05) and Pearson's correlation. For IT and pullout, conventional and experimental implants showed no difference between them when inserted in the 20 pcf PU (p>0.05). In the 40 pcf PU, the modified implants exhibited greater IT (p<0.05) and lower pullout (p<0.05) compared to the respective conventional models. The implant design tested associated with the surgical protocol, positively influenced primary stability in higher density bones.

Influence of an alternative implant design and surgical protocol on primary stability

Abstract The purpose of thisin vitrostudy was to evaluate the influence of a new proposal of implant design and surgical protocol on primary stability in different bone densities. Four groups were tested (n=9): G1 - tapered, cone morse, Ø 4.3 mm x 10 mm in length (Alvim CM); G2 - experimental tapered; G3 - cylindrical, cone morse, Ø 4.0 mm x 11 mm in length (Titamax CM) and G4 - experimental cylindrical. The experimental implants were obtained from a design change in the respective commercial models. The insertion was performed in polyurethane (PU) blocks 0.24 g/cm3(20 pcf) and 0.64 g/cm3(40 pcf), according to different surgical protocols. The primary stability was measured by means of insertion torque (IT) and pullout test. Data were analyzed by ANOVA, Tukey's test (α=0.05) and Pearson's correlation. For IT and pullout, conventional and experimental implants showed no difference between them when inserted in the 20 pcf PU (p>0.05). In the 40 pcf PU, the modified implants exhibited greater IT (p<0.05) and lower pullout (p<0.05) compared to the respective conventional models. The implant design tested associated with the surgical protocol, positively influenced primary stability in higher density bones.

Resumo O objetivo deste estudo in vitro foi avaliar a influência de uma nova proposta de design de implante e protocolo cirúrgico na estabilidade primária em diferentes densidades ósseas. Foram testados quatro grupos (n=9): G1 - cônico, cone morse, Ø 4,3 mm x 10 mm de comprimento (Alvim CM); G2 - experimental cônico; G3 - cilíndrico, cone morse, Ø 4,0 mm x 11 mm de comprimento (Titamax CM) e G4 - experimental cilíndrico. Os implantes experimentais foram obtidos a partir de uma mudança no design dos respectivos modelos comerciais. A inserção foi realizada em blocos de poliuretano (PU) 0,24 g/cm3 (20 pcf) e 0,64 g/cm3 (40 pcf), de acordo com diferentes protocolos cirúrgicos. A estabilidade primária foi aferida por meio do torque de inserção (TI) e ensaio de arrancamento. Os dados foram analisados por ANOVA, teste de Tukey (α=0,05) e correlação de Pearson. Para TI e arrancamento, os implantes convencionais e experimentais não mostraram diferença entre si quando inseridos na PU de 20 pcf (p>0,05). Na PU de 40 pcf, os implantes modificados exibiram maior TI (p <0,05) e menor arrancamento (p <0,05) em relação aos respectivos modelos convencionais. O design do implante testado associado ao protocolo cirúrgico, influenciou positivamente a estabilidade primária em ossos de maior densidade.

Influence of Er,Cr:YSGG laser, associated or not to desensitizing agents, in the prevention of acid erosion in bovine root dentin.

This in vitro study evaluated the influence of the Er,Cr:YSGG laser, associated or not to desensitizing agents, in the prevention of acid erosion in bovine root dentin. Eighty dentin specimens were selected and divided into eight groups (n = 10): G1: negative control; G2: positive control (5% fluoride varnish-FV); G3: Er,Cr:YSGG laser; G4: FV + laser; G5: 3% potassium oxalate; G6: 3% potassium oxalate + laser; G7: biphasic calcium silicate/phosphate gel (gel); G8: gel + laser. Laser parameters: 0.5 W, 6.25 J/cm2 at 1-mm distance. The erosive drink used was a cola soft-drink (pH = 2.42 at 4 °C), lasting 5 min, twice a day, with 6-h intervals between the challenges, during 14 days. Kolmogorov-Smirnov and Levene's tests were satisfied. The surface roughness data were submitted to ANOVA and Tukey post hoc tests. For the wear profile, Kruskal-Wallis and Dunn post hoc tests were used. Afterwards, the Spearman correlation test was performed. All statistical tests assumed a significance level of 5% (α = 0.05). G1 presented the highest surface roughness value after the erosive challenge (3.586 µm2 ± 0.205 µm2) and the G7 presented the lowest surface roughness value after the erosive challenge (1.071 µm2 ± 0.180 µm2). For the lost volume, G4 presented the lowest percentage (9.7% ± 0.9%), while G1 had the highest percentage (41.8% ± 2.5%), both with p < 0.05. There was a weak correlation between the response variables (ρ = 0.33). All groups presented lower values of surface roughness and loss of volume when compared to the negative control group. For the surface roughness, the biphasic calcium silicate/phosphate gel presented the best result. For volume loss, the 5% fluoride varnish + Er,Cr:YSGG laser showed the best results compared to the other groups.

Alternative fixation system for implant-retained overdenture: case report / Sistema alternativo de fixação para overdenture implanto-retida: relato de caso

ABSTRACT The aim of this case report was to describe a prosthetic rehabilitation associated with an alternative model of polymer capsule for fixation system of implant-retained overdentures. Patient sought treatment at the clinic of School of Dentistry of Ribeirão Preto, due to lack of retention of their conventional total superior prostheses and inferior overdenture. The initial complaint was clinicallyconfirmed by altered intermaxillary relationships and severe reabsorption of the maxillary crest. In order to restore the function and improve its quality of life, it was proposed a prosthetic solution including implant fixed prosthesis to maxilla and a mandibular overdenture, with ball-type attachments associated with an alternative model of polymer capsule. This treatment was proposed inorder to reestablish the intermaxillary relationships and adequate occlusion, maintain retention and stability of the prosthesis. At the end of treatment and during a one-year follow-up of the case, the patient reported satisfaction and significant improvement in quality of life.

RESUMO O objetivo deste relato de caso foi descrever uma reabilitação protética associada a um modelo alternativo de cápsula polimérica para sistema de fixação de overdentures implantado-retidas. Paciente procurou tratamento na clínica da Faculdade de Odontologia de Ribeirão Preto, devido falta de retenção de suas próteses totais superiores convencionais e overdenture inferior. A queixa inicialfoi clinicamente confirmada por relações intermaxilares alteradas e reabsorção severa da crista maxilar. Para restaurar a função e melhorar sua qualidade de vida, propôs-se como solução protética, a confecção de prótese fixa sobre implantes para a maxila e overdenture mandibular, com acessórios tipo bola associados a um modelo alternativo de cápsula polimérica. Esse tratamento foiproposto a fim de restabelecer as relações intermaxilares e a oclusão adequada, manter a retenção e a estabilidade da prótese. Ao final do tratamento e durante o acompanhamento de um ano do caso, o paciente relatou satisfação e melhora significativa na qualidade de vida.

Analysis of the oral microbiome on the surface of modified dental polymers.

OBJECTIVES: This study characterized the microbial diversity of formed biofilm on the surface of acrylic resins modified with nanostructured silver vanadate decorated with silver nanoparticles (AgVO3) after incubation in human saliva. DESIGN: Resin specimens prepared with AgVO3 at concentrations 0%, 1%, 2.5%, and 5% by either vacuum mixing or polymer solubilization were characterized by scanning electron microscopy (SEM) and X-ray diffraction (XRD). After 24 h and 7 days of saliva incubation, biofilm samples were collected from the surface of the specimens. The 16S rDNA genes were amplified, sequenced with the 454-Roche next-generation sequencing platform and analyzed to identify the Operational Taxonomic Units at the genus or higher level. RESULTS: Significant differences in the dispersion pattern of the nanoparticles were observed among the two different methods of AgVO3 incorporation. In the microbiological analysis, a total of 103 genera and 7 more inclusive taxa, representing the phyla Bacteroidetes, Firmicutes and Proteobacteria were identified colonizing resin surfaces. The incorporation method of the AgVO3 had little to no significant effect on the microbiota of samples. Significant time and concentration-dependent responses to AgVO3 caused changes in the taxonomic profile at the phylum and genus level. CONCLUSIONS: The results show differences in relation to the microbial diversity of modified resins during the initial phase of biofilm maturation. The incorporation of AgVO3 seems to significantly affect the colonizing microbiota.