Multifunctional Chiral d10 -Metal Coordination Polymers: Tunable Photoluminescence and Efficient Second-Harmonic Generation with Circular Dichroic Response.

A series of homochiral coordination polymers (HCPs), [M2 (SIAP)2 (bpy)2 ] [M(S)] and [M2 (RIAP)2 (bpy)2 ] [M(R)] (M = Zn or Cd, SIAP or RIAP = (S,S)- or (R,R)- 2,2'-(isophthaloylbis(azanediyl))di-propionic acid, bpy = 4,4'-bipyridine), is successfully synthesized through solvothermal reactions, self-assembling d10 metal cations, chiral dicarboxylic ligands, and π-conjugated bipyridyl ligands. The HCPs crystallize in the extremely rare triclinic chiral space group, P1, and present 3D framework structures attributed to the strong intermolecular interactions, such as hydrogen bonds and π-π stacking. Due to the unique crystal structures, the title compounds reveal efficient photoluminescence emission across a broad visible range, with significant brightness and color tuning by varying the excitation wavelength. Moreover, they exhibit efficient phase-matched second-harmonic generation (SHG) with very high laser-induced damage thresholds, essential for high-power nonlinear optical (NLO) applications. Intriguingly, the title compounds exhibit a measurable contrast in the SHG response under right- and left-handed circularly polarized excitation, thereby providing a unique case of SHG circular dichroism from the chiral centers of SIAP2- or RIAP2- ligand packed in the noncentrosymmetric environment. These exceptional attributes position these HCPs as promising candidates for multifunctional materials, with potential applications ranging from NLO devices to tailored luminescent systems with polarization control.

Crystal structure, electronic structure, and optical properties of the novel Li4CdGe2S7, a wide-bandgap quaternary sulfide with a polar structure derived from lonsdaleite.

The novel quaternary thiogermanate Li4CdGe2S7 (tetralithium cadmium digermanium heptasulfide) was discovered from a solid-state reaction at 750 °C. Single-crystal X-ray diffraction data were collected and used to solve and refine the structure. Li4CdGe2S7 is a member of the small, but growing, class of I4-II-IV2-VI7 diamond-like materials. The compound adopts the Cu5Si2S7 structure type, which is a derivative of lonsdaleite. Crystallizing in the polar space group Cc, Li4CdGe2S7 contains 14 crystallographically unique ions, all residing on general positions. Like all diamond-like structures, the compound is built of corner-sharing tetrahedral units that create a relatively dense three-dimensional assembly. The title compound is the major phase of the reaction product, as evidenced by powder X-ray diffraction and optical diffuse reflectance spectroscopy. While the compound exhibits a second-harmonic generation (SHG) response comparable to that of the AgGaS2 (AGS) reference material in the IR region, its laser-induced damage threshold (LIDT) is over an order of magnitude greater than AGS for λ = 1.064 µm and τ = 30 ps. Bond valence sums, global instability index, minimum bounding ellipsoid (MBE) analysis, and electronic structure calculations using density functional theory (DFT) were used to further evaluate the crystal structure and electronic structure of the compound and provide a comparison with the analogous I2-II-IV-VI4 diamond-like compound Li2CdGeS4. Li4CdGe2S7 appears to be a better IR nonlinear optical (NLO) candidate than Li2CdGeS4 and one of the most promising contenders to date. The exceptional LIDT is likely due, at least in part, to the wider optical bandgap of ∼3.6 eV.

Heteroanionic Control of Exemplary Second-Harmonic Generation and Phase Matchability in 1D LiAsS2-xSex.

The isostructural heteroanionic compounds ß-LiAsS2-xSex (x = 0, 0.25, 1, 1.75, 2) show a positive correlation between selenium content and second-harmonic response and greatly outperform the industry standard AgGaSe2. These materials crystallize in the noncentrosymmetric space group Cc as one-dimensional 1/∞ [AsQ2]- (Q = S, Se, S/Se) chains consisting of corner-sharing AsQ3 trigonal pyramids with charge-balancing Li+ atoms interspersed between the chains. LiAsS2-xSex melts congruently for 0 ≤ x ≤ 1.75, but when the Se content exceeds x = 1.75, crystallization is complicated by a phase transition. This behavior is attributed to the ß- to α-phase transition present in LiAsSe2, which is observed in the Se-rich compositions. The band gap decreases with increasing Se content, starting at 1.63 eV (LiAsS2) and reaching 1.06 eV (ß-LiAsSe2). Second-harmonic generation measurements as a function of wavelength on powder samples of ß-LiAsS2-xSex show that these materials exhibit significantly higher nonlinearity than AgGaSe2 (d36 = 33 pm/V), reaching a maximum of 61.2 pm/V for LiAsS2. In comparison, single-crystal measurements for LiAsSSe yielded a deff = 410 pm/V. LiAsSSe, LiAsS0.25Se1.75, and ß-LiAsSe2 show phase-matching behavior for incident wavelengths exceeding 3 µm. The laser-induced damage thresholds from two-photon absorption processes are on the same order of magnitude as AgGaSe2, with S-rich materials slightly outperforming AgGaSe2 and Se-rich materials slightly underperforming AgGaSe2.

Cu4MnGe2S7 and Cu2MnGeS4: two polar thiogermanates exhibiting second harmonic generation in the infrared and structures derived from hexagonal diamond.

The new, quaternary diamond-like semiconductor (DLS) Cu4MnGe2S7 was prepared at high-temperature from a stoichiometric reaction of the elements under vacuum. Single crystal X-ray diffraction data were used to solve and refine the structure in the polar space group Cc. Cu4MnGe2S7 features [Ge2S7]6- units and adopts the Cu5Si2S7 structure type that can be considered a derivative of the hexagonal diamond structure. The DLS Cu2MnGeS4 with the wurtz-stannite structure was similarly prepared at a lower temperature. The achievement of relatively phase-pure samples, confirmed by X-ray powder diffraction data, was nontrival as differential thermal analysis shows an incongruent melting behaviour for both compounds at relatively high temperature. The dark red Cu2MnGeS4 and Cu4MnGe2S7 compounds exhibit direct optical bandgaps of 2.21 and 1.98 eV, respectively. The infrared (IR) spectra indicate potentially wide windows of optical transparency up to 25 µm for both materials. Using the Kurtz-Perry powder method, the second-order nonlinear optical susceptibility, χ(2), values for Cu2MnGeS4 and Cu4MnGe2S7 were estimated to be 16.9 ± 2.0 pm V-1 and 2.33 ± 0.86 pm V-1, respectively, by comparing with an optical-quality standard reference material, AgGaSe2 (AGSe). Cu2MnGeS4 was found to be phase matchable at λ = 3100 nm, whereas Cu4MnGe2S7 was determined to be non-phase matchable at λ = 1600 nm. The weak SHG response of Cu4MnGe2S7 precluded phase-matching studies at longer wavelengths. The laser-induced damage threshold (LIDT) for Cu2MnGeS4 was estimated to be ∼0.1 GW cm-2 at λ = 1064 nm (pulse width: τ = 30 ps), while the LIDT for Cu4MnGe2S7 could not be ascertained due to its weak response. The significant variance in NLO properties can be reasoned using the results from electronic structure calculations.

Structure Tuning, Strong Second Harmonic Generation Response, and High Optical Stability of the Polar Semiconductors Na1-xKxAsQ2.

The mixed cation compounds Na1-xKxAsSe2 (x = 0.8, 0.65, 0.5) and Na0.1K0.9AsS2 crystallize in the polar noncentrosymmetric space group Cc. The AAsQ2 (A = alkali metals, Q = S, Se) family features one-dimensional (1D) 1/∞[AQ2-] chains comprising corner-sharing pyramidal AQ3 units in which the packing of these chains is dependent on the alkali metals. The parallel 1/∞[AQ2-] chains interact via short As···Se contacts, which increase in length when the fraction of K atoms is increased. The increase in the As···Se interchain distance increases the band gap from 1.75 eV in γ-NaAsSe2 to 2.01 eV in Na0.35K0.65AsSe2, 2.07 eV in Na0.2K0.8AsSe2, and 2.18 eV in Na0.1K0.9AsS2. The Na1-xKxAsSe2 (x = 0.8, 0.65) compounds melt congruently at approximately 316 °C. Wavelength-dependent second harmonic generation (SHG) measurements on powder samples of Na1-xKxAsSe2 (x = 0.8, 0.65, 0.5) and Na0.1K0.9AsS2 suggest that Na0.2K0.8AsSe2 and Na0.1K0.9AsS2 have the highest SHG response and exhibit significantly higher laser-induced damage thresholds (LIDTs). Theoretical SHG calculations on Na0.5K0.5AsSe2 confirm its SHG response with the highest value of d33 = 22.5 pm/V (χ333(2) = 45.0 pm/V). The effective nonlinearity for a randomly oriented powder is calculated to be deff = 18.9 pm/V (χeff(2) = 37.8 pm/V), which is consistent with the experimentally obtained value of deff = 16.5 pm/V (χeff(2) = 33.0 pm/V). Three-photon absorption is the dominant mechanism for the optical breakdown of the compounds under intense excitation at 1580 nm, with Na0.2K0.8AsSe2 exhibiting the highest stability.