Low Reflection and Low Surface Recombination Rate Nano-Needle Texture Formed by Two-Step Etching for Solar Cells.

In this study, needle-like and pyramidal hybrid black silicon structures were prepared by performing metal-assisted chemical etching (MACE) on alkaline-etched silicon wafers. Effects of the MACE time on properties of the black silicon wafers were investigated. The experimental results showed that a minimal reflectance of 4.6% can be achieved at the MACE time of 9 min. The height of the nanostructures is below 500 nm, unlike the height of micrometers needed to reach the same level of reflectance for the black silicon on planar wafers. A stacked layer of silicon nitride (SiNx) grown by inductively-coupled plasma chemical vapor deposition (ICPCVD) and aluminum oxide (Al2O3) by spatial atomic layer deposition was deposited on the black silicon wafers for passivation and antireflection. The 3 min MACE etched black silicon wafer with a nanostructure height of less than 300 nm passivated by the SiNx/Al2O3 layer showed a low surface recombination rate of 43.6 cm/s. Further optimizing the thickness of ICPCVD-SiNx layer led to a reflectance of 1.4%. The hybrid black silicon with a small nanostructure size, low reflectance, and low surface recombination rate demonstrates great potential for applications in optoelectronic devices.

Enhanced Si Passivation and PERC Solar Cell Efficiency by Atomic Layer Deposited Aluminum Oxide with Two-step Post Annealing.

In this study, aluminum oxide (Al2O3) films were prepared by a spatial atomic layer deposition using deionized water and trimethylaluminum, followed by oxygen (O2), forming gas (FG), or two-step annealing. Minority carrier lifetime of the samples was measured by Sinton WCT-120. Field-effect passivation and chemical passivation were evaluated by fixed oxide charge (Qf) and interface defect density (Dit), respectively, using capacitance-voltage measurement. The results show that O2 annealing gives a high Qf of - 3.9 × 1012 cm-2, whereas FG annealing leads to excellent Si interface hydrogenation with a low Dit of 3.7 × 1011 eV-1 cm-2. Based on the consideration of the best field-effect passivation brought by oxygen annealing and the best chemical passivation brought by forming gas, the two-step annealing process was optimized. It is verified that the Al2O3 film annealed sequentially in oxygen and then in forming gas exhibits a high Qf (2.4 × 1012 cm-2) and a low Dit (3.1 × 1011 eV-1 cm-2), yielding the best minority carrier lifetime of 1097 µs. The SiNx/Al2O3 passivation stack with two-step annealing has a lifetime of 2072 µs, close to the intrinsic lifetime limit. Finally, the passivated emitter and rear cell conversion efficiency was improved from 21.61% by using an industry annealing process to 21.97% by using the two-step annealing process.

Thin-Film Coated Plastic Wrap for Food Packaging.

In this study, the antimicrobial property and food package capability of polymethylpentene (PMP) substrate with silicon oxdie (SiOx) and organic silicon (SiCxHy) stacked layers deposited by an inductively coupled plasma chemical vapor deposition system were investigated. The experimental results show that the stacked pair number of SiOx/SiCxHy on PMP is limited to three pairs, beyond which the films will crack and cause package failure. The three-pair SiOx/SiCxHy on PMP shows a low water vapor transmission rate of 0.57 g/m²/day and a high water contact angle of 102°. Three-pair thin-film coated PMP demonstrates no microbe adhesion and exhibits antibacterial properties within 24 h. Food shelf life testing performed at 28 °C and 80% humidity reports that the three-pair thin-film coated PMP can enhance the food shelf-life to 120 h. The results indicate that the silicon-based thin film may be a promising material for antibacterial food packaging applications to extend the shelf-life of food products.