Tissue Equivalent Curved Organic X-ray Detectors Utilizing High Atomic Number Polythiophene Analogues.

Organic semiconductors are a promising material candidate for X-ray detection. However, the low atomic number (Z) of organic semiconductors leads to poor X-ray absorption thus restricting their performance. Herein, the authors propose a new strategy for achieving high-sensitivity performance for X-ray detectors based on organic semiconductors modified with high -Z heteroatoms. X-ray detectors are fabricated with p-type organic semiconductors containing selenium heteroatoms (poly(3-hexyl)selenophene (P3HSe)) in blends with an n-type fullerene derivative ([6,6]-Phenyl C71 butyric acid methyl ester (PC70 BM). When characterized under 70, 100, 150, and 220 kVp X-ray radiation, these heteroatom-containing detectors displayed a superior performance in terms of sensitivity up to 600 ± 11 nC Gy-1  cm-2 with respect to the bismuth oxide (Bi2 O3 ) nanoparticle (NP) sensitized organic detectors. Despite the lower Z of selenium compared to the NPs typically used, the authors identify a more efficient generation of electron-hole pairs, better charge transfer, and charge transport characteristics in heteroatom-incorporated detectors that result in this breakthrough detector performance. The authors also demonstrate flexible X-ray detectors that can be curved to a radius as low as 2 mm with low deviation in X-ray response under 100 repeated bending cycles while maintaining an industry-standard ultra-low dark current of 0.03 ± 0.01 pA mm-2 .

Photoinduced Current Transient Spectroscopy on Metal Halide Perovskites: Electron Trapping and Ion Drift.

Metal halide perovskites (MHPs) are disruptive materials for a vast class of optoelectronic devices. The presence of electronic trap states has been a tough challenge in terms of characterization and thus mitigation. Many attempts based on electronic spectroscopies have been tested, but due to the mixed electronic-ionic nature of MHP conductivity, many experimental results retain a large ambiguity in resolving electronic and ionic charge contributions. Here we adapt a method, previously used in highly resistive inorganic semiconductors, called photoinduced current transient spectroscopy (PICTS) on lead bromide 2D-like ((PEA)2PbBr4) and standard "3D" (MAPbBr3) MHP single crystals. We present two conceptually different outcomes of the PICTS measurements, distinguishing the different electronic and ionic contributions to the photocurrents based on the different ion drift of the two materials. Our experiments unveil deep level trap states on the 2D, "ion-frozen" (PEA)2PbBr4 and set new boundaries for the applicability of PICTS on 3D MHPs.

Mixed 3D-2D Perovskite Flexible Films for the Direct Detection of 5 MeV Protons.

This study reports on a novel, flexible, proton beam detector based on mixed 3D-2D perovskite films deposited by solution onto thin plastic foils. The 3D-2D mixture allows to obtain micrometer-thick and highly uniform films that constitute the detector's active layer. The devices demonstrate excellent flexibility with stable electric transport properties down to a bending radius of 3.1 mm. The detector is characterized under a 5 MeV proton beam with fluxes in the range [4.5 × 105 - 1.4 × 109 ] H+ cm-2 s-1 , exhibiting a stable response to repetitive irradiation cycles with sensitivity up to (290 ± 40) nC Gy-1 mm-3 and a limit of detection down to (72±2) µGy s-1 . The detector radiation tolerance is also assessed up to a total of 1.7 × 1012 protons impinging on the beam spot area, with a maximum variation of the detector's response of 14%.

Molecular Weight Tuning of Organic Semiconductors for Curved Organic-Inorganic Hybrid X-Ray Detectors.

Curved X-ray detectors have the potential to revolutionize diverse sectors due to benefits such as reduced image distortion and vignetting compared to their planar counterparts. While the use of inorganic semiconductors for curved detectors are restricted by their brittle nature, organic-inorganic hybrid semiconductors which incorporated bismuth oxide nanoparticles in an organic bulk heterojunction consisting of poly(3-hexylthiophene-2,5-diyl) (P3HT) and [6,6]-phenyl C71 butyric acid methyl ester (PC70 BM) are considered to be more promising in this regard. However, the influence of the P3HT molecular weight on the mechanical stability of curved, thick X-ray detectors remains less well understood. Herein, high P3HT molecular weights (>40 kDa) are identified to allow increased intermolecular bonding and chain entanglements, resulting in X-ray detectors that can be curved to a radius as low as 1.3 mm with low deviation in X-ray response under 100 repeated bending cycles while maintaining an industry-standard dark current of <1 pA mm-2 and a sensitivity of ≈ 0.17 µC Gy-1 cm-2 . This study identifies a crucial missing link in the development of curved detectors, namely the importance of the molecular weight of the polymer semiconductors used.

X-Ray-Induced Modification of the Photophysical Properties of MAPbBr3 Single Crystals.

Methylammonium lead tribromide (MAPbBr3) perovskite single crystals demonstrate to be excellent direct X-ray and gamma-ray detectors with outstanding sensitivity and low limit of detection. Despite this, thorough studies on the photophysical effects of exposure to high doses of ionizing radiation on this material are still lacking. In this work, we present our findings regarding the effects of controlled X-ray irradiation on the optoelectronic properties of MAPbBr3 single crystals. Irradiation is carried out in air with an imaging X-ray tube, simulating real-life application in a medical facility. By means of surface photovoltage spectroscopy, we find that X-ray exposure quenches free excitons in the material and introduces new bound excitonic species. Despite this drastic effect, the crystals recover after 1 week of storage in dark and low humidity conditions. By means of X-ray photoelectron spectroscopy, we find that the origin of the new bound excitonic species is the formation of bromine vacancies, leading to local changes in the dielectric response of the material. The recovery effect is attributed to vacancy filling by atmospheric oxygen and water.

Direct detection of 5-MeV protons by flexible organic thin-film devices.

The direct detection of 5-MeV protons by flexible organic detectors based on thin films is here demonstrated. The organic devices act as a solid-state detector, in which the energy released by the protons within the active layer of the sensor is converted into an electrical current. These sensors can quantitatively and reliably measure the dose of protons impinging on the sensor both in real time and in integration mode. This study shows how to detect and exploit the energy absorbed both by the organic semiconducting layer and by the plastic substrate, allowing to extrapolate information on the present and past irradiation of the detector. The measured sensitivity, S = (5.15 ± 0.13) pC Gy-1, and limit of detection, LOD = (30 ± 6) cGy s-1, of the here proposed detectors assess their efficacy and their potential as proton dosimeters in several fields of application, such as in medical proton therapy.

Designing Ultraflexible Perovskite X-Ray Detectors through Interface Engineering.

X-ray detectors play a pivotal role in development and advancement of humankind, from far-reaching impact in medicine to furthering the ability to observe distant objects in outer space. While other electronics show the ability to adapt to flexible and lightweight formats, state-of-the-art X-ray detectors rely on materials requiring bulky and fragile configurations, severely limiting their applications. Lead halide perovskites is one of the most rapidly advancing novel materials with success in the field of semiconductor devices. Here, an ultraflexible, lightweight, and highly conformable passively operated thin film perovskite X-ray detector with a sensitivity as high as 9.3 ± 0.5 µC Gy-1 cm-2 at 0 V and a remarkably low limit of detection of 0.58 ± 0.05 µGy s-1 is presented. Various electron and hole transporting layers accessing their individual impact on the detector performance are evaluated. Moreover, it is shown that this ultrathin form-factor allows for fabrication of devices detecting X-rays equivalently from front and back side.

Characterization of an organic semiconductor diode for dosimetry in radiotherapy.

PURPOSE: The development of novel detectors for dosimetry in advanced radiotherapy modalities requires materials that have a water equivalent response to ionizing radiation such that characterization of radiation beams can be performed without the need for complex calibration procedures and correction factors. Organic semiconductors are potentially an ideal technology in fabricating devices for dosimetry due to tissue equivalence, mechanical flexibility, and relatively cheap manufacturing cost. The response of a commercial organic photodetector (OPD), coupled to a plastic scintillator, to ionizing radiation from a linear accelerator and orthovoltage x-ray tube has been characterized to assess its potential as a dosimeter for radiotherapy. The radiation hardness of the OPD has also been investigated to demonstrate its longevity for such applications. METHODS: Radiation hardness measurements were achieved by observing the response of the OPD to the visible spectrum and 70 keV x rays after pre-exposure to 40 kGy of ionizing radiation. The response of a preirradiated OPD to 6-MV photons from a linear accelerator in reference conditions was compared to a nonirradiated OPD with respect to direct and indirect (RP400 plastic scintillator) detection mechanisms. Dose rate dependence of the OPD was measured by varying the surface-to-source distance between 90 and 300 cm. Energy dependence was characterized from 29.5 to 129 keV with an x-ray tube. The percentage depth dose (PDD) curves were measured from 0.5 to 20 cm and compared to an ionization chamber. RESULTS: The OPD sensitivity to visible light showed substantial degradation of the broad 450 to 600 nm peak from the donor after irradiation to 40 kGy. After irradiation, the spectral shape has a dominant absorbance peak at 370 nm, as the acceptor better withstood radiation damage. Its response to x rays stabilized to 30% after 35 kGy, with a 0.5% difference between 770 Gy increments. The OPD exhibited reproducible detection of ionizing radiation when coupled with a scintillator. Indirect detection showed a linear response from 25 to 500 cGy and constant response to dose rates from 0.31 Gy/pulse to 3.4 × 10-4  Gy/pulse. However, without the scintillator, response increased by 100% at low dose rates. Energy independence between 100 keV and 1.2 MeV advocates their use as a dosimeter without beam correction factors. A dependence on the scintillator thickness used during a comparison of the PDD to the ionizing chamber was identified. A 1-mm-thick scintillator coupled with the OPD demonstrated the best agreement of ± 3%. CONCLUSIONS: The response of OPDs to ionizing radiation has been characterized, showing promising use as a dosimeter when coupled with a plastic scintillator. The mechanisms of charge transport and trapping within organic materials varies for visible and ionizing radiation, due to differing properties for direct and indirect detection mechanisms and observing a substantial decrease in sensitivity to the visible spectrum after 40 kGy. This study proved that OPDs produce a stable response to 6-MV photons, and with a deeper understanding of the charge transport mechanisms due to exposure to ionizing radiation, they are promising candidates as the first flexible, water equivalent, real-time dosimeter.

Morphology and mobility as tools to control and unprecedentedly enhance X-ray sensitivity in organic thin-films.

Organic semiconductor materials exhibit a great potential for the realization of large-area solution-processed devices able to directly detect high-energy radiation. However, only few works investigated on the mechanism of ionizing radiation detection in this class of materials, so far. In this work we investigate the physical processes behind X-ray photoconversion employing bis-(triisopropylsilylethynyl)-pentacene thin-films deposited by bar-assisted meniscus shearing. The thin film coating speed and the use of bis-(triisopropylsilylethynyl)-pentacene:polystyrene blends are explored as tools to control and enhance the detection capability of the devices, by tuning the thin-film morphology and the carrier mobility. The so-obtained detectors reach a record sensitivity of 1.3 · 104 µC/Gy·cm2, the highest value reported for organic-based direct X-ray detectors and a very low minimum detectable dose rate of 35 µGy/s. Thus, the employment of organic large-area direct detectors for X-ray radiation in real-life applications can be foreseen.

Highly efficient surface-emitting semiconductor lasers exploiting quasi-crystalline distributed feedback photonic patterns.

Quasi-crystal distributed feedback lasers do not require any form of mirror cavity to amplify and extract radiation. Once implemented on the top surface of a semiconductor laser, a quasi-crystal pattern can be used to tune both the radiation feedback and the extraction of highly radiative and high-quality-factor optical modes that do not have a defined symmetric or anti-symmetric nature. Therefore, this methodology offers the possibility to achieve efficient emission, combined with tailored spectra and controlled beam divergence. Here, we apply this concept to a one-dimensional quantum cascade wire laser. By lithographically patterning a series of air slits with different widths, following the Octonacci sequence, on the top metal layer of a double-metal quantum cascade laser operating at THz frequencies, we can vary the emission from single-frequency-mode to multimode over a 530-GHz bandwidth, achieving a maximum peak optical power of 240 mW (190 mW) in multimode (single-frequency-mode) lasers, with record slope efficiencies for multimode surface-emitting disordered THz lasers up to ≈570 mW/A at 78 K and ≈720 mW/A at 20 K and wall-plug efficiencies of η ≈ 1%.

Space Environment Effects on Flexible, Low-Voltage Organic Thin-Film Transistors.

Organic electronic devices fabricated on flexible substrates are promising candidates for applications in environments where flexible, lightweight, and radiation hard materials are required. In this work, device parameters such as threshold voltage, charge mobility, and trap density of 13-bis(triisopropylsilylethynyl)pentacene (TIPS-pentacene)-based organic thin-film transistors (OTFTs) have been monitored for performing electrical measurements before and after irradiation by high-energy protons. The observed reduction of charge carrier mobility following irradiation can be only partially ascribed to the increased trap density. Indeed, we used other techniques to identify additional effects induced by proton irradiation in such devices. Atomic force microscopy reveals morphological defects occurring in the organic dielectric layer induced by the impinging protons, which, in turn, induce a strain on the TIPS-pentacene crystallites lying above. The effects of this strain are investigated by density functional theory simulations of two model structures, which describe the TIPS-pentacene crystalline films at equilibrium and under strain. The two different density of states distributions in the valence band have been correlated with the photocurrent spectra acquired before and after proton irradiation. We conclude that the degradation of the dielectric layer and the organic semiconductor sensitivity to strain are the two main phenomena responsible for the reduction of OTFT mobility after proton irradiation.

Direct X-ray photoconversion in flexible organic thin film devices operated below 1 V.

The application of organic electronic materials for the detection of ionizing radiations is very appealing thanks to their mechanical flexibility, low-cost and simple processing in comparison to their inorganic counterpart. In this work we investigate the direct X-ray photoconversion process in organic thin film photoconductors. The devices are realized by drop casting solution-processed bis-(triisopropylsilylethynyl)pentacene (TIPS-pentacene) onto flexible plastic substrates patterned with metal electrodes; they exhibit a strong sensitivity to X-rays despite the low X-ray photon absorption typical of low-Z organic materials. We propose a model, based on the accumulation of photogenerated charges and photoconductive gain, able to describe the magnitude as well as the dynamics of the X-ray-induced photocurrent. This finding allows us to fabricate and test a flexible 2 × 2 pixelated X-ray detector operating at 0.2 V, with gain and sensitivity up to 4.7 × 104 and 77,000 nC mGy-1 cm-3, respectively.

Toward Low-Voltage and Bendable X-Ray Direct Detectors Based on Organic Semiconducting Single Crystals.

Organic materials have been mainly proposed as ionizing radiation detectors in the indirect conversion approach. The first thin and bendable X-ray direct detectors are realized (directly converting X-photons into an electric signal) based on organic semiconducting single crystals that possess enhanced sensitivity, low operating voltage (≈5 V), and a minimum detectable dose rate of 50 µGy s(-1) .

Organic semiconducting single crystals as solid-state sensors for ionizing radiation.

So far, organic semiconductors have been mainly proposed as detectors for ionizing radiation in the indirect conversion approach, i.e. as scintillators, which convert ionizing radiation into visible photons, or as photodiodes, which detect visible photons coming from a scintillator and convert them into an electrical signal. The direct conversion of ionizing radiation into an electrical signal within the same device is a more effective process than indirect conversion, since it improves the signal-to-noise ratio and it reduces the device response time. We report here the use of Organic Semiconducting Single Crystals (OSSCs) as intrinsic direct ionizing radiation detectors, thanks to their stability, good transport properties and large interaction volume. Ionizing radiation X-ray detectors, based on low-cost solution-grown OSSCs, are here shown to operate at room temperature, providing a stable linear response with increasing dose rate in the ambient atmosphere and in high radiation environments.

Organic semiconducting single crystals as next generation of low-cost, room-temperature electrical X-ray detectors.

Direct, solid-state X-ray detectors based on organic single crystals are shown to operate at room temperature, in air, and at voltages as low as a few volts, delivering a stable and reproducible linear response to increasing X-ray dose rates, with notable radiation hardness and resistance to aging. All-organic and optically transparent devices are reported.