RESUMO
Background: This retrospective clinical study aimed to assess dental pulp tissue reactions to direct and indirect pulp capping after 10 years of follow-up. Methods: A total of 276 permanent teeth with deep carious lesions were evaluated and divided into five groups: Group (1), direct pulp capping with Mineral Trioxide Aggregate cement; Group (2), direct pulp capping with a resin-based glass ionomer; Group (3), direct pulp capping with TheraCal; Group (4), indirect pulp capping with a three-step total-etch adhesive system; and Group (5), indirect pulp capping with a two-step self-etch adhesive system. Results: A 72.5% success rate was achieved overall. A statistically significant difference was found when comparing direct and indirect pulp capping with a success rate of 23.8% and 93.8%, respectively. For direct pulp-capping procedures, the area of pulp exposure was correlated with pulp necrosis (p = 0.035), while bleeding after exposure appeared independent (p = 0.053). Patient age was significantly related to the maintenance of pulp vitality (p = 0.013). A statistically significant correlation between the pulp-capping material and the occurrence of pulp necrosis was discovered (p = 0.017). For the indirect pulp-capping treatments, a significant correlation between patient age (p = 0.021) and the adhesive system (p = 0.019) with pulp necrosis was described. Conclusions: The pulp-capping material, patient age, and the width of the pulp exposure before the procedure should be carefully considered when performing direct pulp-capping treatments. The performance of the etch-and-rinse adhesive systems was superior to the self-etch system during the indirect pulp-capping procedures.
RESUMO
INTRODUCTION: A growing body of research supports an association between periapical inflammation and an increased risk of developing systemic diseases. There is currently no scientific evidence to support a causal effect of inflammation on the onset of insulin resistance (IR) in patients with apical periodontitis (AP). The aim of this in vitro study was to evaluate any association between AP and levels of serum inflammatory factors potentially associated with the onset of IR, and to investigate the effect of root canal treatment (RCT) on these systemic inflammation markers and on the response in vitro to insulin. METHODS: A total of 27 control subjects and 27 patients with AP were enrolled. Patients with AP underwent RCT and were followed-up 6 and 12 months post-treatment. Enzyme-linked immunosorbent assays were used to evaluate serum levels of proinflammatory cytokines interleukin (IL)-1, IL-6, IL-8, and tumor necrosis factor (TNF)-α. The response in vitro to insulin was assessed by measuring glucose consumption in a human pancreatic epithelioid carcinoma cell line treated with sera from healthy and AP subjects. RESULTS: At baseline AP was associated with significant higher levels of IL-1, IL-6, and IL-8 in the serum of untreated (AP) patients vs controls (P < .001). Glucose consumption decreased in pancreatic cells incubated with baseline serum from patients with AP, in a manner proportional to total cytokines amount. Notably, endodontic treatment was associated with reduced levels of cytokines (P < .001) and improved response to insulin in AP group (P < .001). CONCLUSIONS: Our findings suggest that AP may promote inflammatory-driven IR in an in vitro model, and that RCT may ameliorate inflammatory mediators in vivo and the cellular response to insulin in vitro.
RESUMO
(1) Background: The objective of this in vitro study was to evaluate the impact of different etching times and ethanol pre-treatments on the immediate bond strength of a hydrophilic multi-mode universal adhesive (Clearfil Universal Bond Quick, Kuraray, UBQ) and on the consequent gelatinolytic activity of metalloproteinases (MMPs) on radicular dentin. (2) Methods: Sixty single-root teeth were selected and divided into four groups according to the adhesive protocol applied for fiber post cementation: (G1) 15 s H3PO4 application + UBQ; (G2) 30 s H3PO4 application + UBQ; (G3) 15 s H3PO4 application + ethanol pre-treatment + UBQ; (G4) 30 s H3PO4 + ethanol pre-treatment + UBQ. After adhesive procedures, fiber posts were luted into the post space with a dual-curing cement (DC Core, Kuraray) and light-cured for 40 s. To perform the push-out test and nanoleakage analyses for both coronal end apical areas, 1 mm slices were prepared, following a 24 h storage period in artificial saliva. Additionally, an in situ zymographic assay was conducted to explore endogenous MMP activity within the radicular layer. Results were statistically analyzed with ANOVA and Tukey post hoc tests. Statistical significance was set at p < 0.05. (3) Result: ANOVA revealed a statistically significant difference in push-out bond strength related to the pre-treatment variable but did not highlight any significance of etching time. Specimens pre-treated with ethanol wet bond application showed higher bond strength (p < 0.01). In situ zymography quantification analyses revealed that all tested groups, independently of etching time end ethanol pre-treatment, activated MMP gelatinolytic activity. A significant increase in MMP activity was detected for the 30 s etching time. However, ETOH pre-treatment significantly reduced MMP activity within the adhesive interface (p < 0.01). (4) Conclusions: The tested adhesive showed similar results regardless of the etching time protocol. The gelatinolytic activity of MMPs was observed in all the groups. Further investigations and extended follow-ups are required to validate the results of the present study in vivo.
RESUMO
PURPOSE: The aim of the present study was to investigate the influence of three post-and-core systems and two crown materials on stresses in restored premolars using Finite Element Analysis (FEA). MATERIALS AND METHODS: A maxillary second premolar 3D model was created in SolidWorks 2014 (Dassault Systémés). Severe loss of tooth structure was simulated with six restorative options: 1) glass-fiber-reinforced composite post and composite core (GFRC)+CAD/CAM leucite-reinforced glass-ceramic crown (LRC); 2) carbon-fiberreinforced composite post and composite core (CFRC)+LRC; 3) metal cast post-and-core (MPC)+LRC 4) GFRC+CAD/CAM composite resin crown (CC); 5) CFRC+CC; 6) MPC+CC. Three-point occlusal loading (150N) was simulated and von Misses and maximum principal stresses calculated. RESULTS: Although maximum von Mises stresses in the crown and dentin were similar across groups (137.9-139.2MPa crown; 17.2-19.6 dentin), there were important differences in stress distribution in dentin. Only in MPC+CC group the maximum stresses were on the bottom of the post preparation cavity. Stress values within the posts were: CFRC(4.8MPa)>GFRC(6.7MPa)>MPC(10.3MPa). CC-restored models presented higher von Mises stresses within the post-and-core compared to the LRC groups. Maximum principal stresses were lower compared to von Mises stresses, following the same trend, and were distributed similarly in all the groups. CONCLUSIONS: Both GFRC and CFRC showed favourable stresses distribution in the dentin and restorative materials, while MPC increased stresses in core, post and post cement. The more rigid crown material seems to transmit less stresses to the underlying core and crown cement compared to CC.
RESUMO
(1) Background: A Dynamic Navigation System (DNS) is an innovative tool that facilitates the management of complex endodontic cases. Despite the number of advantages and limitations of this approach, there is no evidence-based information about its efficiency in comparison with that of the traditional method in endodontics. (2) Objectives: We aimed to explore any beneficial effects of the DNS and compare the outcomes of DNS vs. free-hand (FH) approaches for non-surgical and microsurgical endodontics. (3) Methods: A literature search was conducted in August 2023 to identify randomized, experimental, non-surgical, and microsurgical endodontic studies that compared the DNS with FH approaches. The procedural time (ΔT, s), substance loss (ΔV, mm3), angular deviation (ΔAD, °), coronal/platform linear deviation (ΔLD_C, mm), and apical linear deviation (ΔLD_A, mm) were recorded and analyzed. Quality and risk of bias assessments were conducted according to the Quality Assessment Tool For In Vitro Studies. A meta-analysis was performed using mean difference and standard deviation for each outcome, and heterogeneity (I2) was estimated. p < 0.05 was considered significant. (4) Results: One-hundred and forty-six studies were identified following duplicate removal, and nine were included in the systematic review and meta-analysis. The overall risk of bias was classified as low. The DNS was found to be more accurate and efficient than the FH approach was, resulting in a significantly shorter operation time (p < 0.00001) and less angular (p ≤ 0.0001) and linear deviation (p ≤ 0.01). For substance loss, the advantage of the DNS was significant only for microsurgery (p = 0.65, and p < 0.005, for non-surgical and microsurgical procedures, respectively). A reduced risk of iatrogenic failure using the DNS was observed for both expert and novice operators. (5) Conclusions: The DNS appears beneficial for non-surgical and microsurgical endodontics, regardless of the operator's experience. However, appropriate training and experience are necessary to access the full advantages offered by the DNS.
RESUMO
INTRODUCTION: Computer simulations are stimulating increased attention in dentistry. Augmented reality superimposes a virtual scenario over an existing reality and allows interaction with it. Virtual reality (VR) simulates a fully immersive situation permitting the user to experience the full environment in real time. Haptic technology provides tactile and realistic force feedback for the user to experience the immersive situation as if they were really there. Preclinical training is important to gain familiarity with difficult surgical techniques and to implement interpersonal skills. Developing a valid assessment of surgical simulation is challenging. This paper wants to present a newly realized VR simulation in endodontic microsurgery through the developmental digital workflow, the demonstration of a haptic VR scenario and student self-assessment and self-reflection feedback. METHODS: The volumes were exported in a stereolithography format to prepare and optimize in terms of shape and shade for the VR simulation. The graphics and touchable haptic solid were created using Virteasy Editor, which allows the transformation of 3D surfaces into graphical and volumetric haptic solids depending on their material (enamel, dentine, pulp and bone). Users were asked to execute the osteotomy and root-resection preparation. The assessment criteria were determined, and the feedback statements were created by a questionnaire with fixed answers. Objective and qualitative criteria for assessing the preparation were obtained from the literature. RESULTS: This study provides proof that it is possible to provide reliable and clinically relevant qualitative feedback with a VR simulator. CONCLUSION: VR simulation offers an innovative approach with all the benefits of clinical experience. It permits you to save your own progress and review the assessment at any time.
RESUMO
BACKGROUND: To investigate the effect of 0.3 M 1-ethyl-3(3-dimethylaminopropyl) carbodiimide (EDC) aqueous solution pretreatment on push-out bond strength (PBS) and matrix-metalloproteinases (MMPs) activity within radicular dentin when different post cementation strategies were employed. METHODS: One hundred and twenty monoradicular human teeth were endodontically treated and randomly divided into six groups, depending on the cementation strategy and root dentin pretreatment (n = 20): EAR: cementation with an etch-and-rinse adhesive (LuxaBond Total Etch, DMG) and resin cement (LuxaCore Z Dual, DMG); EAR/EDC: 1 min EDC pretreatment after etching + EAR; SE: cementation with a self-etch primer (Multilink Primer, Ivoclar Vivadent) and corresponding cement (Multilink Automix, Ivoclar Vivadent); SE/EDC: self-etch primer + EDC pretreatment + SE; SA: cementation with a universal self-adhesive cement (RelyX Universal, 3 M); SA/EDC: EDC pretreatment + SA. Slices were submitted to PBS test and interfacial nanoleakage evaluation 24 h after cementation or after thermocycling (40.000 cycles, 5-55 °C). To investigate the effect of EDC on MMPs activity, 4 additional first maxillary premolars per group were processed for in situ zymography analysis. Multivariate ANOVA and post hoc Tukey tests were used to analyze PBS values. The data from in situ zymography were analyzed with Kruskal-Wallis test and Dunn's pairwise multiple comparison procedures (α = 0.05). RESULTS: The variables "EDC pretreatment", "root region" and "thermocycling" significantly influenced PBS (p < 0.05), while the variable "cementation strategy" had no influence (p > 0.05). Thermocycling significantly reduced PBS in SE and SA groups (p < 0.05). EDC was effective in preserving PBS after artificial aging. EDC pretreatment significantly reduced enzymatic activity at baseline in EAR and SE groups, and in SA group after thermocycling (p < 0.05). CONCLUSIONS: The use of EDC prevents the reduction of bond-strength values after artificial aging and silences endogenous enzymatic activity within radicular dentin when different cementation strategies were employed.
Assuntos
Colagem Dentária , Humanos , Carbodi-Imidas/química , Dentina , Cimentos de Resina/uso terapêutico , Cimentos de Resina/química , Metaloproteinases da Matriz , Teste de MateriaisRESUMO
PURPOSE: To retrospectively evaluate the clinical behavior of direct anterior composite restorations performed with a universal adhesive or with a three-step etch-and-rinse (E&R) adhesive. MATERIAL AND METHODS: Patients were randomly treated with a three-step E&R adhesive (Optibond FL, Kerr) or a universal adhesive (Clearfil Universal Bond Quick, Kuraray Noritake) applied in E&R mode. All restorations were performed with a nanohybrid composite (ClearFil Majesty ES-2, Kuraray Noritake) by the same experienced operator. Two calibrated examiners evaluated the restorations using a dental mirror and explorer, in accordance with modified United States Public Health Service (USPHS) procedures. Clinical events were registered and classified as either failure (F), survival (SR), or success (S). RESULTS: 168 restorations were evaluated in 90 patients with an average follow-up period of 37.9 (± 22.9) months. A total of 132 restorations were performed on vital teeth, and 36 were performed on endodontically treated teeth (ETT). A total of 128 Class-IV and 40 Class-III restorations were performed. In 89 restorations, a three-step E&R adhesive was applied (14 Class-III and 75 Class-IV), while in 79, a universal adhesive was used (26 Class-III and 53 Class-IV, p = 0.0091). A Cox regression analysis was performed (p < 0.05) to analyze which factors were involved in the failure of the restorations, considering failure (F) as restorations that needed re-intervention at the follow-up period of 37.9 (± 22.9) months. No statistically significant differences were observed when considering parameters directly involved with the adhesives tested. Endodontically treated teeth were more prone to fractures (p = 0.0006) compared to vital teeth. Restorations made with universal adhesives failed by fracturing significantly more frequently (p = 0.0234), while restorations made on endodontically treated teeth had a significantly worse outcome (p = 0.0001). Restorations made on canines also failed significantly more frequently (HR = 3.8, 95% CI = 1.4-10.1, p = 0.0062). CONCLUSIONS: Based on the obtained results, both the universal adhesive and the three-step E&R adhesive proved to be good treatment choices for direct anterior restorations after 37.9 (± 22.9) months of follow-up. Tooth vitality seems fundamental for the prognosis of a direct anterior composite restoration over time.
Assuntos
Colagem Dentária , Dente não Vital , Humanos , Resinas Compostas/química , Colagem Dentária/métodos , Cimentos Dentários/química , Restauração Dentária Permanente/métodos , Adesivos Dentinários/química , Cimentos de Resina/química , Estudos RetrospectivosRESUMO
STATEMENT OF PROBLEM: Intraoral scanners (IOSs) are widely used for partial-coverage adhesive restorations, but data on their performance in such preparations with complex geometries are sparse. PURPOSE: The purpose of this in vitro study was to investigate whether the partial-coverage adhesive preparation design and finish line depth affect the trueness and precision of different IOSs. MATERIAL AND METHODS: Seven partial-coverage adhesive preparation designs (4 different onlays, 2 endocrowns, and 1 occlusal veneer) were tested on copies of the same tooth placed in a typodont mounted on a mannequin. Each preparation was scanned 10 times with 6 different IOSs (total 420 scans) under the same light conditions. Trueness and precision, defined according to the International Organization for Standardization (ISO) 5725-1 standard, were analyzed with a best-fit algorithm by superimposition. The obtained data were analyzed by a 2-way analysis of variance to examine the effects of partial-coverage adhesive preparation design, IOS, and their interactions (α=.05). RESULTS: Significant differences were found among different preparation designs and IOSs (P<.05) in terms of both trueness and precision. Significant differences were also found among mean positive and negative values (P<.05). Moreover, crosslinks observed between the preparation area and the adjacent teeth correlated with the finish line depth. CONCLUSIONS: Complex partial adhesive preparation designs affect the trueness and precision of IOSs, resulting in significant differences among them. Interproximal preparations should take into account the IOS's resolution and placing the finish line close to adjacent structures should be avoided.
Assuntos
Desenho Assistido por Computador , Imageamento Tridimensional , Técnica de Moldagem Odontológica , Modelos Dentários , Arco DentalRESUMO
PURPOSE: To evaluate the fracture strength of endodontically treated molars filled with different composite resins with vs without fiber reinforcement. MATERIALS AND METHODS: A total of 60 intact mandibular molars were selected and endodontically treated. A standardized mesio-occlusal-distal cavity was prepared with cervical margins 1 mm above the cementoenamel junction and oral and buccal walls with 1.5-mm thickness. Universal adhesive was used in all specimens in etch-and-rinse mode. Specimens were divided into four groups (n = 15 each) according to restoration technique: group CSM = adhesive overlay with hybrid ceramic; group EXP = direct restoration with short fiber-reinforced composite; group ESU = direct restoration with nanohybrid composite; and group EST = direct restoration with nanohybrid composite reinforced with horizontal bidirectional glass fibers placed over the pulpal chamber floor. After 7 days of storage in water, samples were loaded until fracture using a universal testing machine. The maximum breaking loads were recorded in Newtons, and statistical analysis was then conducted with two-way ANOVA and post hoc Tukey test. Fragments were analyzed using scanning electron microscopy. RESULTS: Mean fracture resistance values were: CSM = 1,428.91 ± 316.90 N; EXP = 1,874.57 ± 299.47 N; ESU = 1,557.44 ± 355.65 N; and EST = 1,870.27 ± 145.11 N. The CSM and EXP groups showed the highest strength values when compared to the other groups. The variable fiber insertion did not significantly alter the fracture resistance. The origin of the fracture was always located on the occlusal surface, mainly in the major contact loading area. CONCLUSION: The use of fiber-reinforced composite showed great improvement in fracture resistance, similar to a cuspal coverage restoration. However, only short fiber-reinforced composites showed a favorable fracture pattern. Int J Prosthodont 2023;36:603-611.
Assuntos
Fraturas dos Dentes , Dente não Vital , Humanos , Resistência à Flexão , Fraturas dos Dentes/prevenção & controle , Dente não Vital/terapia , Cimentos Dentários , Resinas Compostas , Dente Molar , Análise do Estresse Dentário , Teste de Materiais , Restauração Dentária PermanenteRESUMO
PURPOSE: To evaluate the effect of three different curing protocols based on different ratios of self-curing and light-curing periods on the bond strength and nanoleakage of fiber posts luted with dual-curing self-adhesive cements. MATERIALS AND METHODS: A total of 48 single-root teeth were endodontically treated and obturated, and an 8-mm post space was prepared with dedicated drills. Specimens were randomly divided into two groups according to the self-adhesive cement employed: group 1 (G1) = PANAVIA SA Plus (Kuraray Noritake), and group 2 (G2) = Bifix SE (VOCO). The specimens were further divided into three subgroups (n = 8 each) according to the light-curing protocol applied: no light-curing (SG1), 20 seconds of light-curing 20 seconds after cement injection (SG2), and 20 seconds of light-curing 120 seconds after cement injection (SG3). Slices of 1-mm thickness were prepared for the pushout test and nanoleakage analyses of the coronal and apical regions after 24 hours of storage in artificial saliva. Results were statistically analyzed with three-way ANOVA and Tukey post hoc tests. Statistical significance was set for P < .05. RESULTS: Three-way ANOVA analysis showed that the factors of cement (P = .02) and curing protocol (P < .001) had a significant influence on bond strength. Tukey post hoc test reported that light-curing 120 seconds after injection showed higher bond strength compared to both no light-curing and photoactivation after 20 seconds. CONCLUSION: To achieve the highest bond strength with self-adhesive cements, photoactivation with a 120-second delay after mixing is required. There is no difference between light-curing immediately and light-curing 20 seconds after mixing.
Assuntos
Colagem Dentária , Técnica para Retentor Intrarradicular , Cimentos de Resina/química , Colagem Dentária/métodos , Análise do Estresse Dentário , Teste de Materiais , DentinaRESUMO
The aim of the present study was to evaluate the fatigue to cyclic and static resistance of indirect restorations with different preparation designs made either of lithium disilicate (LS) or polymer-infiltrated ceramic network (PICN). Eighty-four (n = 84) molars were chosen, endodontically treated, and prepared with standardized MOD cavities. The molars were randomly divided into 6 study groups (n = 14) taking into account the "preparation design'' (occlusal veneer with 1.2 mm occlusal thickness; overlay with 1.6 mm occlusal thickness; adhesive crown with 2 mm occlusal thickness) and the "CAD/CAM material'' (E-max CAD, Ivoclar vivadent; Vita Enamic, Vita). A fatigue test was conducted with a chewing simulator set at 50 N for 1,500,000 cycles. Fracture resistance was assessed using a universal testing machine with a 6 mm diameter steel sphere applied to the specimens at a constant speed of 1 mm/min. A SEM analysis before the fracture test was performed to visually analyze the tooth-restoration margins. A statistical analysis was performed with a two-way ANOVA and a post-hoc pairwise comparison was performed using the Tukey test. The two-way ANOVA test showed that both the preparation design factor (p = 0.0429) and the CAD/CAM material factor (p = 0.0002) had a significant influence on the fracture resistance of the adhesive indirect restorations. The interaction between the two variables did not show any significance (p = 0.8218). The occlusal veneer had a lower fracture resistance than the adhesive crown (p = 0.042) but not lower than the overlay preparation (p = 0.095). LS was more resistant than PICN (p = 0.002). In conclusion, in the case of endodontically treated teeth, overlay preparation seems to be a valid alternative to the traditional full crown preparation, while occlusal veneers should be avoided in restoring non-vital molars with a high loss of residual tooth structure. LS material is more resistant compared to PICN.
RESUMO
PURPOSE: To evaluate the effect of different pretreatment protocols and adhesives on the shear bond strength and surface morphology of aprismatic enamel. MATERIALS AND METHODS: Human maxillary incisors (N = 120) were assigned to five different groups according to pretreatment: 1) no treatment; 2) glycine; 3) sodium bicarbonate; 4) Al2O3 and 5) extra-fine bur. Then the teeth were divided into three subgroups, according to the adhesive applied: 3-step etch-and-rinse (ER), universal adhesive in ER mode, and universal adhesive in self-etch (SE) mode. Shear bond strength (SBS) testing was performed with a universal testing machine. For SEM observation, fifteen human molars were collected and analyzed after pretreatment with/without etching with 37% H3PO4 for 30s. RESULTS: Al2O3 showed higher SBS than all other groups considered. Comparable SBS values were obtained for other pretreatments. Universal adhesive in E&R mode performed better than did 3-step E&R and universal adhesive in SE mode. SEM images showed visible differences in enamel surface roughness. CONCLUSIONS: Airborne-particle abrasion with Al2O3 followed by etching with H3PO4 increased SBS on aprismatic enamel. The combination of airborne-particle abrasion with alumina powder followed by 15 s of H3PO4 etching and application of a universal adhesive in E&R mode proved to be the most effective adhesive protocol.
Assuntos
Condicionamento Ácido do Dente , Colagem Dentária , Humanos , Condicionamento Ácido do Dente/métodos , Colagem Dentária/métodos , Cimentos Dentários/química , Bicarbonato de Sódio , Pós , Teste de Materiais , Esmalte Dentário , Resistência ao Cisalhamento , Óxido de Alumínio , Glicina , Cimentos de Resina/química , Adesivos DentináriosRESUMO
OBJECTIVES: This in vitro research aimed to quantitatively evaluate the enamel and dentin tissue removal and the residual adhesion surface area (RAS) after different margin designs and locations for indirect partial restorations (IPR). METHODS: A human molar was scanned using a Micro-CT and the STL file obtained was used to 3D-print 50 resin-tooth replicas. IPR standardized preparations were performed. The specimens were randomly assigned to 5 groups (n = 10), according to preparation and margin location to the dental equator (DE): 1) Rounded shoulder above the DE (SA); 2) Hollow chamfer above the DE (CA); 3) Butt joint above the DE (BJ); 4) Rounded shoulder below the DE (SB); 5) Chamfer below the DE (CB). Then, the tooth replicas were scanned and each STL file was aligned and superimposed to the original STL model file. Data of enamel and dentin volume removal and RAS were assessed and statistically analyzed (one-way ANOVA and Kruskal-Wallis tests for the two dental substrates respectively). Significance was set at p<0.05. RESULTS: Differences in dental tissue reductions were related to the margin location. Above the equator, SA, CA, and BJ performed comparably (p>0.05). Below the equator, CB was significantly more conservative in enamel reduction than SB (p<0.05) and showed the highest enamel adhesive surface exposure among the tested preparations (p<0.05). CONCLUSIONS: When the preparation margin is placed above DE, BJ determines a greater exposure of dentin, reducing the adhesive surface in enamel. Below DE, SB seems to be more aggressive in terms of tissue removal compared to CB. CLINICAL SIGNIFICANCE: The results of this in vitro study suggest that in teeth requiring partial restoration with the margin below the dental equator, a chamfer preparation would be more conservative than a shoulder preparation. When above the equator, preparations with flat designs would expose more dentine providing a worse substrate for adhesion.
Assuntos
Condicionamento Ácido do Dente , Preparo da Cavidade Dentária , Humanos , Condicionamento Ácido do Dente/métodos , Resinas Compostas , Esmalte Dentário/diagnóstico por imagem , Restauração Dentária Permanente/métodos , Dentina/diagnóstico por imagem , Cimentos de Resina , Microtomografia por Raio-XRESUMO
The present study aimed to evaluate the wear rate of polymer-infiltrated network composites and ceramics against enamel in a bruxism-simulated scenario. Ninety-six (n = 96) molars were divided into six groups (n = 16) according to their occlusal material: group 1-a polymer-infiltrated network ceramic (PINC); group 2-a second polymer-infiltrated network ceramic (PINC2); group 3-nanohybrid resin-based composite (CO); group 4-cubic zirconia (ZR); group 5-lithium disilicate (LS); and group 6-sound enamel (EN). A laser scanner was used to digitalize all of the occlusal surfaces before and after a fatigue test, which was conducted with a chewing simulator set at 80 N and semicircular movement in order to simulate bruxist movement and loads. Statistical analysis of volume loss was performed with a one-way ANOVA and post hoc Bonferroni test. ZR had significantly inferior wear to PINC (p ≤ 0.01) and CO (p = 0.04). LS wore the antagonist enamel significantly more than PINC, CO, PINC2 and EN (p ≤ 0.01). On the other hand, ZR wore the antagonist enamel significantly more than CO (p ≤ 0.01) and PINC2 (p = 0.05). In conclusion, PINCs better preserved antagonist enamel at the expense of a higher wear of their own. LS causes significantly higher enamel wear compared with PINCs. ZR caused significantly higher enamel wear compared with CO and PINC2, but it was wear-resistant.
RESUMO
Objectives of the study were to investigate biomechanical properties of severely compromised premolars restored with composite restorations using finite element analysis (FEA), and in vitro fracture resistance test. A 3-D model of an endodontically treated premolar was created in Solidworks. Different composite restorations were modelled (direct restoration-DR; endo-crown-EC; post, core, and crown-C) with two different supporting tissues: periodontal ligament/alveolar bone (B), and polymethyl methacrylate (PMMA). Models were two-point axially loaded occlusally (850 N). Von Mises stresses and strains were calculated. The same groups were further tested for static fracture resistance in vitro (n = 5, 6.0 mm-diameter ball indenter, vertical load). Fracture resistance data were statistically analyzed (p < 0.050). The highest stresses and strains in all FEA models were observed on occlusal and vestibular cervical surfaces, corresponding to fracture propagation demonstrated in vitro. C showed the lowest stress in dentin, while EC showed lower stresses and strains in crown cement. B models demonstrated larger high stress areas in the root than PMMA models. No significant differences in fracture resistance (N) were observed between groups (DR: 747.7 ± 164.0, EC: 867.3 ± 108.1, C: 866.9 ± 126.3; p = 0.307). More conservative restorations seem a feasible alternative for endodontically treated premolars to conventional post-core-crown.
Assuntos
Fraturas dos Dentes , Dente não Vital , Dente Pré-Molar , Resinas Compostas , Coroas , Análise de Elementos Finitos , Humanos , Polimetil Metacrilato , Fraturas dos Dentes/prevenção & controle , Dente não Vital/terapiaRESUMO
The aim of this in vitro study was to evaluate the effects of substrate and cement shades on the translucency and color of lithium-disilicate and zirconia CAD/CAM materials. Two light-cured resin cements (RelyX Veneer Cement; 3M; Choice 2 Veneer Cement; Bisco Dental) with a standardized thickness (0.1 mm) were tested in combination with two different monolithic CAD/CAM materials (E-Max CAD (LI2SI2O5); Ivoclar Vivadent; Katana (ZrO2); Kuraray-Noritake Dental) on two different colored composite substrates used as a dentin (Filtek Supreme XTE; 3M); for a total of 12 combinations (n = 10). The specimens' color was measured with a spectrophotometer (Spectroshade; MHT). Measurements were taken using the CIELAB color coordinate system (L*a*b*) against black and white backgrounds. L*a*b* values were statistically analyzed for the variables Substrate, Ceramic, and Cement by applying a Three-Way ANOVA followed by the Tukey Test for post-hoc comparison (p < 0.05). Translucency Parameter (TP) and Constant Ratio (CR) were assessed to evaluate translucency; acceptability and perceptibility thresholds (ΔE00 1.8 and 0.8) were used. Statistically significant influence was found for factors ceramic material, cement shade, and substrate color (p < 0.05). Unacceptable color differences were reported for Li2Si2O5. Opacity was significantly higher when white opaque cement shade was employed. Ceramic type and cement shade significantly influenced L*a*b* color coordinates. The final translucency and color of ceramic restorations can, therefore, be influenced by ceramic material, cement shade, and substrate color.
RESUMO
The aim was to evaluate the antibacterial efficacy and penetration depth into dentinal tubules of a solution of chitosan nanodroplets (NDs) loaded with Benzalkonium Chloride (BAK). Seventy-two human single-root teeth with fully formed apex were used. Cylindrical root dentin blocks were longitudinally sectioned and enlarged to a size of a Gates Glidden drill #4. After sterilization, root canals were infected with Enterococcus faecalis ATCC 29212 and further incubated for three weeks. Specimens were assigned to three experimental groups (n = 20), plus positive (n = 6) and negative (n = 6) controls. In the first group, irrigation was achieved with 2 mL of NDs solution loaded with BAK (NDs-BAK), in the second with 2 mL of 5% sodium hypochlorite (NaOCl) and in the last with 2 mL of 2% chlorhexidine (CHX). Specimens were rinsed and vertically fractured. Confocal laser scanning microscopy (CLSM) and viability staining were used to analyze the proportions of dead and live bacteria quantitatively. The volume ratio of red fluorescence (dead) was calculated in 3D reconstructions. Data were analyzed by one-way ANOVA and post hoc Bonferroni tests (p < 0.05). The ratio of red fluorescence over the whole green/red fluorescence resulted in a significant comparison of NDs-BAK with NaOCl (p < 0.01) and NaOCl with CHX (p < 0.01). No differences were found between NDs-BAK and CHX (p > 0.05). The mean depth of efficacy was, respectively: NDs-BAK 325.25 µm, NaOCl 273.36 µm and CHX 246.78 µm with no statistical differences between groups. The NaOCl solution showed the highest antimicrobial efficacy, but nanodroplets with BAK seemed to have the same effect as CHX with a high depth of efficacy.
RESUMO
PURPOSE: To evaluate push-out bond strength (PBS) and interfacial nanoleakage (NL) of adhesively luted fiber posts using different composite cements and polymerization protocols. MATERIAL AND METHODS: 100 premolars were endodontically treated and assigned to the following groups (n=10): RelyX Universal light-cure (3M Oral Care); RelyX Universal self-cure (3M Oral Care); Maxcem Elite Chroma light-cure (Kerr); Maxcem Elite Chroma self-cure (Kerr); Calibra Universal light-cure (Dentsply Sirona); Calibra Universal self-cure (Dentsply Sirona); Multilink Automix light cure (Ivoclar Vivadent); Multilink Automix self-cure (Ivoclar Vivadent); Luxacore Z Dual light-cure (DMG); Luxacore Z Dual self-cure (DMG). Half of the teeth from each group were subjected to the PBS test after 24 h (T0), while the other half was tested after 12 months (T12) of artificial saliva aging. An additional 4 teeth per group were prepared for NL expression. PBS values were analyzed using multivariate ANOVA and Tukey's post-hoc test. NL scores were analyzed using chi-squared tests (α = 0.05). RESULTS: Statistical analysis revealed that the variables "cement" and "aging" significantly influenced PBS (p < 0.05), but not "polymerization" and "root region" (p > 0.05). Significantly lower PBS values (p < 0.05) were detected for the Calibra Universal groups compared to other cements, while the RelyX Universal groups performed equally well (p > 0.05) or better than other cements (p < 0.05). At T12, PBS values increased in the majority of groups, irrespective of root region (p < 0.05). Differences in NL expression were present at T0, and in general, the aging process increased marginal infiltration. CONCLUSION: Aging and choice of composite cement influenced PBS, while root region and polymerization protocol seemed to have no influence on posts' resistance to dislodgment.
Assuntos
Cimentos Dentários , Cimentos de Ionômeros de Vidro , Materiais Dentários , Dentina , PolimerizaçãoRESUMO
This study aimed to investigate matrix metalloproteinase (MMP) activity in human dentin using in-situ and gelatin zymography, after at-home and in-office bleaching, related to their clinical exposure times. Dentin specimens (n = 5) were treated with 35% hydrogen peroxide (50 min per session/4 sessions), 10% carbamide peroxide (180 min/21 sessions), or no treatment. All were subjected to in-situ zymography. Dentin slices were, subsequently, obtained, covered with fluorescein-conjugated gelatin, and examined with confocal laser-scanning microscopy. The fluorescence intensity was quantified and statistically analyzed using one-way ANOVA and Bonferroni tests (α = 0.05). Furthermore, gelatin zymography was performed on protein extracts obtained from dentin powder (N = 8 teeth), treated with hydrogen peroxide or carbamide peroxide, with different exposure times (10/50 min for hydrogen peroxide; 252/1260 min for carbamide peroxide). The results of the in-situ zymography showed no statistical differences between the bleached specimens and the control group, with a medium level of gelatinolytic activity expressed in the dentin tubules. The results of gelatin zymography showed an increased expression of pro-MMP-9 in carbamide peroxide groups. The expression of pro-MMP-2 decreased in all the experimental groups. The bleaching treatments performed on the enamel of sound teeth do not influence dentinal enzymatic activity. However, when unprotected dentin tissue is bleached, matrix metalloproteinases are more expressed, particularly when carbamide peroxide is used, proportional to the exposure time.