Luminescent materials with dual-mode excitation and tunable emission color for anti-counterfeiting applications.

GdVO4-based dual-mode phosphors were successfully synthesized via a hydrothermal approach. The X-ray diffraction analysis determined the tetragonal structure as well as I41/amd space group of products by comparing with a reference pattern no. ICDD #01-072-0277. The morphology of yielded phosphors was confirmed by transmission electron microscopy and scanning electron microscopy. Detailed spectroscopy analysis revealed tunable luminescence properties with an increasing Yb3+ content in series of GdVO4: x% Yb3+, y% Tm3+, 5% Eu3+ (x = 5, 10, 15, 20; y = 0.1, 0.5, 1) phosphors. For Yb3+, Tm3+, and Eu3+- codoped phosphors we observed bands related to the 1G4 → 3H6 and 1G4 → 3F4 transitions of Tm3+ ions, occurred through the cooperative up-conversion mechanism, where two nearby Yb3+ ions were involved in near-infrared absorption. Moreover, the GdVO4: 20% Yb3+, 0.5% Tm3+, 5% Eu3+ showed the most outstanding color tunability from red color (x = 0.6338, y = 0.3172) under UV to blue color (x = 0.2640, y = 0.1988) under NIR excitation, which can be applied in anti-counterfeiting activity.

New Multicolor Tungstate-Molybdate Microphosphors as an Alternative to LED Components.

Due to the ongoing need to create phosphors with the appropriate emission color for the production of light emitting diodes, we decided to synthesize a series of multicolour microphosphors with tunable visible emissions, depending on the composition of dopant ions. In this work, we investigated the structure, morphology, and luminescent properties of new molybdate-tungstate phosphors co-doped with Tb3+ and Eu3+ ions. The conventional high temperature solid state method was used to prepare a series of CaMoyW1-yO4:Eu3+x/Tb3+1-x materials. In order to obtain phosphors with the most promising luminescent properties, the experiment was planned by taking into account the different composition of the matrix and the concentration of the particular dopant ions (Eu3+x/Tb3+1-x, x = 0.001, 0.003, 0.005, 0.007, 0.009). As a result, luminescent materials were obtained with a pure tetragonal crystal structure, the space group of I41/a, confirmed by X-ray diffraction (XRD). The size and shape of the particles obtained from the materials were analyzed based on scanning electron microscopy images. Luminescence spectroscopy (excitation and emission spectra, decay lifetimes) was utilized to characterize the luminescence properties of the as-prepared phosphors. The color change of the emission from green-yellow to orange-red was confirmed using the 1931 Comission Internationale de l'Eclairage (CIE) chromaticity coordinates and color correlated temperature (CCT).