Expanding the synthetic toolbox to access pristine and rare-earth-doped BaFBr nanocrystals.

A new synthetic route to access pristine and rare-earth-doped BaFBr nanocrystals is described. Central to this route is an organic-inorganic hybrid precursor of formula Ba5(CF2BrCOO)10(H2O)7 that serves as a dual-halogen source. Thermolysis of this precursor in a mixture of high-boiling point organic solvents yields spherical BaFBr nanocrystals (≈20 nm in diameter). Yb:Er:BaFBr nanocuboids (≈26 nm in length) are obtained following the same route. Rare-earth-doped nanocrystals display NIR-to-visible photon upconversion under 980 nm excitation. The temperature-dependence of the green emission from Er3+ may be exploited for optical temperature sensing between 150 and 450 K, achieving a sensitivity of 1.1 × 10-2 K-1 and a mean calculated temperature of 300.9 ± 1.5 K at 300 K. The synthetic route presented herein not only enables access to unexplored upconverting materials but also, and more importantly, creates the opportunity to develop solution-processable photostimulable phosphors based on BaFBr.

Open-Framework Structures of Anhydrous Sr(CF3COO)2 and Ba(CF3COO)2.

Anhydrous Sr(CF3COO)2 and Ba(CF3COO)2 open-framework structures featuring three-dimensional connectivity of metal-oxygen polyhedra were crystallized from a mixture of water and CF3COOH. Crystallization was induced via evaporation of the solvent mixture under a dry nitrogen flow. This approach differs from that routinely employed for crystallization of metal trifluoroacetates, which achieves solvent evaporation by heating under air and yields hydrated salts. Thermogravimetric and differential thermal analysis as well as single-crystal and synchrotron powder X-ray diffraction were employed to characterize the alkaline-earth trifluoroacetate products. Neither thermal analysis nor single-crystal X-ray diffraction detected the presence of crystallization water molecules, demonstrating these trifluoroacetates can be obtained in anhydrous form. Single-crystal X-ray diffraction studies showed that Sr(CF3COO)2 and Ba(CF3COO)2 are isostructural and crystallize in the rhombohedral R3̅ space group. Both compounds belong to the class of organic-inorganic extended hybrids and exhibit an open-framework structural motif with three-dimensional connectivity of the metal-oxygen polyhedra and one-dimensional channels along the c axis. The channels are decorated with the trifluoromethyl groups of the trifluoroacetate ligands, and their average (minimum) diameters are ∼3.75 (2.60) and 3.45 (2.25) Å for Sr(CF3COO)2 and Ba(CF3COO)2, respectively. This size range is comparable to the kinetic diameter of small molecules such as hydrogen (2.3 Å). Chemical substitution of barium for strontium affects not only the diameter of the channels but also the spatial arrangement of the trifluoromethyl groups within the channels and the coordination environment of the metal atoms. The different coordination requirements of the strontium and barium atoms are accommodated through the displacement of one of the two chemically distinct trifluoroacetate ligands relative to the metal center.