Optimization of Sibipiruna activated carbon preparation by simplex-centroid mixture design for simultaneous adsorption of rhodamine B and metformin.

The present paper reports the application of augmented simplex-centroid mixture design to obtain a high BET surface area activated carbon using as reactants KOH, K2CO3 and K2C2O4. The optimum mixture composition was 2.51 g of KOH, 0.49 g of K2CO3 and absence of K2C2O4, generating an optimized AC (ACop) with SBET value equals to 1984 m2 g-1. The results herein obtained show that low amounts of K2CO3 can catalyze the pore development in the presence of KOH, increasing the surface area. Furthermore, the fractal dimensions of ACop are greater than 2.72, indicating the material has a complex pore structure with irregularities self-similar upon variations of resolution, as seen by SEM images. The TPD curves showed that the ACop has different oxygenated molecular fragments, which agrees with the pHPZC value (5.05). The ACop was applied in the adsorption of rhodamine B (RhB) and metformin (Met) in both binary and monocomponent systems. The simultaneous adsorption at 30 °C reveals that the adsorption capacity of RhB is 630.94 mg g-1, while for Met the value is 103.83 mg g-1.

KOH-super activated carbon from biomass waste: Insights into the paracetamol adsorption mechanism and thermal regeneration cycles.

A super activated carbon (SAC) was produced by KOH-activation of a biomass waste for paracetamol (PCT) adsorption from aqueous solution and for adsorption-thermal regeneration cycles. The SAC and the regenerated SAC after five adsorption-regeneration cycles (RSAC-5th) were fully characterized by several techniques. The N2 physisorption showed that the SBET values of the SAC and RSAC-5th are remarkably different, being 2794 m² g-1 and 889 m² g-1, respectively. The XPS analysis demonstrated that the SAC surface is composed by oxygen containing-groups, whilst the RSAC-5th also presents nitrogen ones, provenient from the PCT molecules. The adsorption studies revealed that the maximum adsorption capacity (Qm) for the SAC (356.22 mg g-1) is higher than that for RSAC-5th (113.69 mg g-1). Also, the results demonstrated that the PCT adsorption is governed by both physisorption and chemisorption and the ab initio calculations showed the chemisorption mainly occurs in carboxylic groups.