RESUMO
This study develops a composite bone graft of CaO-MgO-SiO2 glass-ceramic and CaSO4 [abbreviated as (CMS)3-x(CS)x] via the sponge replication technique with weight fractions of x = 0, 1, 1.5, 2, and 3. The (CMS)1.5(CS)1.5 composite displays a superior degradability and, a suitable compressive strength of â¼3 MPa, and excellent cell proliferation and differentiation. The in vivo rat femur test in the hybrid-pore (CMS)1.5(CS)1.5 composite granules achieves a higher rate of bone formation, which is â¼2.7 times better than that of the commercial HAP/ß-TCP at 12 weeks. Improved expressions of osteocyte and mature osteocyte marker genes, namely (Spp1, Dmp1, and Fgf23), were observed in the (CMS)1.5(CS)1.5 group, indicating a faster differentiation into mature bone tissue. The ions release of (CMS)1.5(CS)1.5 through the ERK1/2 signaling pathway promotes osteogenic differentiation. The high bone generation rate can be attributed to faster active ions release and modified surface topography. This work highlights an excellent bone graft candidate for clinical applications in orthopedic surgery.
Assuntos
Cerâmica , Osteogênese , Cerâmica/química , Animais , Osteogênese/efeitos dos fármacos , Ratos , Diferenciação Celular/efeitos dos fármacos , Compostos de Cálcio/química , Ratos Sprague-Dawley , Proliferação de Células/efeitos dos fármacos , Óxidos/química , Dióxido de Silício/química , Masculino , Substitutos Ósseos/química , Substitutos Ósseos/farmacologia , Transplante Ósseo/métodos , Óxido de Magnésio/química , Propriedades de Superfície , FêmurRESUMO
This work reports a new CaO-MgO-SiO2 (CMS) bioactive glass-ceramic, using ZrO2 as a nucleus to modulate the ratios of glass and ceramic phases as a function of sintering temperature. Mg-rich bioactive CMS glass-ceramics exhibit advantages regarding mechanical strength (flexural strength ~190 MPa and compressive strength ~555 MPa), in-vitro and in-vivo biocompatibilities, and bone ingrowth. The high mechanical strengths could be attributed to the CaMgSi2O6 glass-ceramic and lower porosity. X-ray absorption spectra indicate an increased SiO covalent bond via the development of CaMgSi2O6 glass-ceramics. From the in-vitro cytotoxicity and BMSC differentiation assays, the CMS samples sintered above 800 °C exhibited better cell attachment and differentiation, possibly due to structural stability, appropriate pore, and ion release to boost osteogenesis. Compared to hydroxyapatite (HA) ceramics, the CMS glass-ceramics display higher mechanical strengths, biocompatibility, and osteoconductivity. An in-vivo experiment demonstrated a fine bone-ingrowth profile around the CMS implant. This study may further the application of CMS glass-ceramics in bone implants.
Assuntos
Óxido de Magnésio , Dióxido de Silício , Cerâmica , Durapatita , VidroRESUMO
In this study, a photoresist template with well-defined contact hole array was fabricated, to which radio frequency magnetron sputtering process was then applied to deposit an alloyed Zr55Cu30Al10Ni5 target, and finally resulted in ordered metallic glass nanotube (MGNT) arrays after removal of the photoresist template. The thickness of the MGNT walls increased from 98 to 126nm upon increasing the deposition time from 225 to 675s. The wall thickness of the MGNT arrays also increased while the dimensions of MGNT reduced under the same deposition condition. The MGNT could be filled with biomacromolecules to change the effective refractive index. The air fraction of the medium layer were evaluated through static water contact angle measurements and, thereby, the effective refractive indices the transverse magnetic (TM) and transverse electric (TE) polarized modes were calculated. A standard biotin-streptavidin affinity model was tested using the MGNT arrays and the fundamental response of the system was investigated. Results show that filling the MGNT with streptavidin altered the effective refractive index of the layer, the angle of reflectance and color changes identified by an L*a*b* color space and color circle on an a*b* chromaticity diagram. The limit of detection (LOD) of the MGNT arrays for detection of streptavidin was estimated as 25nM, with a detection time of 10min. Thus, the MGNT arrays may be used as a versatile platform for high-sensitive label-free optical biosensing.
Assuntos
Técnicas Biossensoriais/instrumentação , Vidro/química , Metais/química , Análise em Microsséries/instrumentação , Nanotubos/química , Técnicas Biossensoriais/métodos , Biotina/química , Desenho de Equipamento , Limite de Detecção , Análise em Microsséries/métodos , Nanotecnologia , Nanotubos/ultraestrutura , Refratometria , Silício/química , Estreptavidina/análiseRESUMO
Electrode material for low-temperature co-fired diopside glass-ceramic used for microwave dielectrics was investigated in the present work. Diffusion of silver from the electrode to diopside glass-ceramics degrades the performance of the microwave dielectrics. Two approaches were adopted to resolve the problem of silver diffusion. Firstly, silicon-oxide (SiO2) powder was employed and secondly crystalline phases were chosen to modify the sintering behavior and inhibit silver ions diffusion. Nanoscale amorphous SiO2 powder turns to the quartz phase uniformly in dielectric material during the sintering process, and prevents the silver from diffusion. The chosen crystalline phase mixing into the glass-ceramics enhances crystallinity of the material and inhibits silver diffusion as well. The result provides a method to decrease the diffusivity of silver ions by adding the appropriate amount of SiO2 and appropriate crystalline ceramics in diopside glass-ceramic dielectric materials. Finally, we used IEEE 802.11a 5.8 GHz as target specification to manufacture LTCC antenna and the results show that a good broadband antenna was made using CaMgSi2O6 with 4 wt % silicon oxide.