Monolithic Magneto-Optical Nanocomposites of Barium Hexaferrite Platelets in PMMA.

The incorporation of magnetic barium hexaferrite nanoparticles in a transparent polymer matrix of poly(methyl methacrylate) (PMMA) is reported for the first time. The barium hexaferrite nanoplatelets doped with Sc(3+), i.e., BaSc0.5Fe11.5O12 (BaHF), having diameters in the range 20 to 130 nm and thicknesses of approximately 5 nm, are synthesized hydrothermally and stabilized in 1-butanol with dodecylbenzenesulfonic acid. This method enables the preparation of monolithic nanocomposites by admixing the BaHF suspension into a liquid monomer, followed by in-situ, bulk free-radical polymerization. The PMMA retains its transparency for loadings of BaHF nanoparticles up to 0.27 wt.%, meaning that magnetically and optically anisotropic, monolithic nanocomposites can be synthesized when the polymerization is carried out in a magnetic field. The excellent dispersion of the magnetic nanoparticles, coupled with a reasonable control over the magnetic properties achieved in this investigation, is encouraging for the magneto-optical applications of these materials.

Nanocomposite foams from iron oxide stabilized dicyclopentadiene high internal phase emulsions: preparation and bromination.

Nanocomposite polyHIPE foams with open-cellular morphology were obtained using nanoparticles (γFe2O3/Fe3O4), surfactant (Pluronic L121) or nanoparticle/surfactant stabilized dicyclopentadiene high internal phase emulsions (DCPD HIPEs). Upon curing, cavity sizes were found to vary drastically between 950 ± 360 µm down to 7 ±3 µm depending on the HIPE formulations. As-obtained nanocomposite polyHIPE foams were functionalized using elemental bromine in THF. Upon bromination the nanoparticles are moved from the cavities surfaces into the bulk phase of the polymer scaffold, which affects the inductive-heating capability of the magnetic nanocomposite foams decreasing it by the factor of 2.

Synthesis of chromium-nickel nanoparticles prepared by a microemulsion method and mechanical milling.

A chemical and a physical method have been applied for the preparation of chromium-nickel alloy nanoparticles. These particles were designed to be used for controlled magnetic hyperthermia applications. Microemulsions with Ni2+ and Cr3+ and/or NaBH4 as precursors were prepared using the isooctane/CTAB, n-butanol/H2O system. The samples of CrxNi1-x nanoparticles with the desired composition were obtained after the reduction of their salts with NaBH4 and afterwards heat treated in a TGA in a N2 atmosphere at various temperatures. The CrxNi1-x materials were also prepared by mechanical milling. Utilizing a ball-to-powder mass ratio of 20 : 1 and selecting the proper alloy compositions we were able to obtain nanocrystalline CrxNi1-x particles. Thermal demagnetization in the vicinity of the Curie temperature of the nanoparticles was studied using a modified TGA-SDTA method. The alloy's phase composition, size and morphology were determined with XRD measurements and TEM analyses.

A facile route to the synthesis of coated maghemite nanocomposites for hyperthermia applications.

CM-dextran-covered maghemite particles for applications in magnetic hyperthermia treatments were synthesized and their physical, magnetic and morphological properties were examined. Magnetic fluids were prepared and their heating properties in an alternating magnetic field were studied. The results reveal that the particle size and the thickness of the carboxy-methyl-dextran (CM-dextran) coatings have a decisive influence on the heating properties: specific absorption rate (SAR). The majority of the magnetic dissipation comes from the Neel relaxation, while the Brown contribution is small. A thermal steady state at the selected temperature (42 °C) can be achieved using synthesized maghemite particles with proper particle morphology and by controlling the magnetic field intensity or the frequency.