RESUMO
Protective clothing standards, such as test methods published by ASTM International, play an integral role in ensuring the performance of personal protective equipment. The standard tests are not without limitations and are periodically reviewed and often updated. Some tests may not be reflective of in-use conditions. A new test cell was designed using sanitary fixtures to evaluate the effect of glove stretch on barrier performance using fluorescein solution as the challenge agent for enhanced visualization and fluorometer detection. Domed-shaped and flat screens were developed to permit and limit glove stretch within the test cell. The barrier performance of glove swatches was evaluated for both stretched and unstretched states. Latex, nitrile, and vinyl glove models of various thicknesses were evaluated. The tests were conducted following pressure and time parameters specified in ASTM F903, ASTM F1670, and ASTM F1671. Fluorescein solution movement, which may occur through penetration, was measured using a fluorometer. Glove stretch caused a reduction in glove thickness ranging from 16% to 40%. Overall, 21 sample failures were found (16.7%; n = 126) regardless of test condition. Nitrile gloves provided better barrier efficacy with the lowest failure rates (2.38%; 1 failure out of 42) compared to latex (19.4%; 7 failures out of 36) and vinyl gloves (27.1%; 13 failures out of 48). Differences in failure rates between stretched and unstretched gloves were insignificant; however, the latex material showed a 2.5 times increase in failures when stretched compared to unstretched. The new test apparatus was able to differentiate between the barrier performance of different glove materials. The use of a domed screen allowed the gloves to stretch, a condition that better represents the state of gloves when in use. Analysis of samples collected from the glove surface opposite to the exposure may provide a way to assess chemical permeation in addition to penetration.
RESUMO
The National Institute for Occupational Safety and Health recommends the use of nitrile gloves with a minimum thickness of 5.0 ± 2.0 mil [0.127 ± 0.051 millimeters] in situations where it is suspected or known that fentanyl or other illicit drugs are present. However, there is limited data available on fentanyl permeation through gloves. Current test methods used to measure fentanyl permeation do not consider the effect of glove fit and flexion. Furthermore, first responders need to have PPE readily available in the field, and storage conditions may affect the protective performance of the gloves. The objective of this study was to evaluate the effects of glove stretch and storage temperatures on glove durability and barrier performance against fentanyl. Nine nitrile glove models previously shown to be resistant to fentanyl permeation were selected for this investigation. These nine models were stretched 25% in one linear direction, to consider glove fit and flexion, and tested against fentanyl hydrochloride permeation. Additionally, four of the nine glove models were stored at 48 °C, 22 °C, and -20 °C, and evaluated for tensile strength, ultimate elongation, and puncture resistance after up to 16 wk of storage and fentanyl permeation after up to 8 wk of storage. At least one sample for six of the nine tested models had maximum permeation over the test method fail threshold when stretched. The tested storage temperatures showed no effect on glove tensile strength, ultimate elongation, and puncture resistance. The findings of this study can be used to inform PPE recommendations, with consideration to storage practices and proper sizing for first responders with potential exposure to fentanyl and other illicit drugs. The results of this study can be used to assess the need for new standard test methods to evaluate the barrier performance of gloves and shelf-life determination with consideration to glove fit.