Ni0.4Cu0.2Zn0.4TbxFe2-xO4 nanospinel ferrites: Ultrasonic synthesis and physical properties.

The Fe3+ ions were replace with Tb3+ ions as highly paramagnetic rare earth element within the structure of Ni0.4Cu0.2Zn0.4Fe2O4 nano-spinel ferrites (NSFs). The structural, magnetic, spectroscopic and optic properties have been studied in details. All products have been synthesized via ultrasonic approach via Qsonica ultrasonic homogenizer, frequency: 20 kHz and power: 70 W for 60 min. No annealing or calcination process was applied for any product. The microstructural analysis of products has been done via X-ray powder diffractometry (XRD) which presented the cubic spinel structure with nanosized distribution of all. The cubic morphology of all products were confirmed by both HR-TEM and FE-SEM. Optical band gap (Eg) values were assessed by applying %DR (percent diffuse reflectance) analysis and Kubelka-Munk theory. The Tauc schemes showed that Eg values are in a narrow range (1.87-1.98 eV). The quadrupole splitting, line width, hyperfine magnetic field, isomer shift values and cation distribution have been determined from 57Fe Mossbauer analysis. The magnetic properties of various nanoparticles have been obtained from VSM (vibration sample magnetometer) measurements at 10 and 300 K (RT). The magnetic results revealed superparamagnetic and soft ferromagnetic traits at 10 and 300 K, respectively. Ms (saturation magnetization) and Mr (remanence) initially increase with increasing Tb3+ substituting level up to x = 0.06 then diminish for further x values. Hc (coercivity) shows an opposite variation tendency of Ms and Mr. The observed magnetic traits are deeply discussed in relation with the structure, morphology, magnetic moments and cation distributions.

Magnetic Attributes of NiFe2O4 Nanoparticles: Influence of Dysprosium Ions (Dy3+) Substitution.

This paper reports the influence of dysprosium ion (Dy3+) substitution on the structural and magnetic properties of NiDyxFe2-xO4 (0.0 ≤ x ≤ 0.1) nanoparticles (NPs) prepared using a hydrothermal method. The structure and morphology of the as-synthesized NPs were characterized via X-ray diffraction (XRD), scanning and transmission electron microscope (SEM, and TEM) analyses. 57Fe Mössbauer spectra were recorded to determine the Dy3+ content dependent variation in the line width, isomer shift, quadrupole splitting, and hyperfine magnetic fields. Furthermore, the magnetic properties of the prepared NPs were also investigated by zero-field cooled (ZFC) and field cooled (FC) magnetizations and AC susceptibility measurements. The MZFC (T) results showed a blocking temperature (TB). Below TB, the products behave as ferromagnetic (FM) and act superparamagnetic (SPM) above TB. The MFC (T) curves indicated the existence of super-spin glass (SSG) behavior below Ts (spin-glass freezing temperature). The AC susceptibility measurements confirmed the existence of the two transition temperatures (i.e., TB and Ts). Numerous models, e.g., Neel-Arrhenius (N-A), Vogel-Fulcher (V-F), and critical slowing down (CSD), were used to investigate the dynamics of the systems. It was found that the Dy substitution enhanced the magnetic interactions.

Impact of La3+ and Y3+ ion substitutions on structural, magnetic and microwave properties of Ni0.3Cu0.3Zn0.4Fe2O4 nanospinel ferrites synthesized via sonochemical route.

In the current study, Ni0.4Cu0.2Zn0.4La x Y x Fe2-x O4 (x = 0.00 - 0.10) nanospinel ferrites (NSFs) were fabricated via an ultrasonic irradiation route. The creation of single phase of spinel nanoferrites (NSFs) was investigated by X-ray powder diffractometry (XRD) and selected area diffraction pattern (SAED). The cubic morphology of all samples was confirmed by scanning and transmission electron microscopies (SEM and TEM) respectively. The UV-Vis investigations provided the direct optical energy band gap values in a narrow photon energy interval of 1.87-1.92 eV. The 57Fe Mössbauer spectroscopy analysis explained that the hyperfine magnetic fields of Octahedral (Oh) and Tetrahedral (Td) sites decreased with substitution. The paramagnetic properties of NPs decrease with increase of content of doped ions. Investigations of magnetic properties reveal a superparamagnetic nature at 300 K and soft ferromagnetic trait at 10 K. The M s (saturation magnetization) and M r (remanence) decrease and the H c (coercivity) increases slightly with La3+ and Y3+ substitution. The observed magnetic traits are deeply discussed in relation with the morphology, structure, magnetic moments and cation distributions. The microwave characterization of the prepared NSFs showed that, dissipation (i.e., absorption) of incoming microwave energy occurs at a single frequency, for each sample, lying between 7 and 10.5 GHz. The reflection losses (RL) at these frequencies range from -30 to -40 dB and the mechanism of which is explained in the framework of dipolar relaxation and spin rotation. The best microwave properties were obtained with a LaY concentration of x = 0.08 having an RL of -40 dB @ 10.5 GHz and an absorption bandwidth of 8.4 GHz @ -10 dB. With these high values of RL and absorbing bandwidth, LaY doped NiCuZn NSF products would be promising candidates for radar absorbing materials in the X-band.