Nanosponge-C3N4 composites as photocatalysts for selective partial alcohol oxidation in aqueous suspension.

A set of four composite materials was prepared, consisting of a nanosponge matrix based on ß-cyclodextrin in which carbon nitride was dispersed. The materials were characterized by the presence of diverse cross-linker units joining the cyclodextrin moieties, in order to vary the absorption/release abilities of the matrix. The composites were characterized and used as photocatalysts in aqueous medium under UV, visible and natural solar irradiation for the photodegradation of 4-nitrophenol, and for the selective partial oxidation of 5-hydroxymethylfurfural and veratryl alcohol to the corresponding aldehydes. The nanosponge-C3N4 composites showed higher activity than the pristine semiconductor, which can probably be attributed to the synergic effect of the nanosponge, capable of increasing the substrate concentration near the surface of the photocatalyst.

Supported Poly(Ionic Liquid)-Heteropolyacid Based Materials for Heterogeneous Catalytic Fructose Dehydration in Aqueous Medium.

Two sets of four different supported catalyst materials were prepared. One set was obtained by polymerization of a bis-vinylimidazolium salt, which formed a poly(ionic liquid) coating on SiO2, TiO2, boron nitride BN, and carbon nitride C3N4. The other set was, instead, obtained by immobilizing Keggin heteropolyacid H3PW12O40 onto poly-imidazolium functionalized materials. All the catalysts, including the bare supports, were subjected to physical and chemical characterization by XRD, SEM, Specific Surface Area and pore size measurements, TGA, FTIR, and acidity-basicity measurements. The catalytic activity of the materials was tested versus the fructose dehydration in water solution at two different sugar initial concentrations (0.3 and 1 M). Tests lasted 3 h with an amount of catalyst of 2 g∙L−1. The presence of the poly-imidazolium on the surface of the supports increased the catalytic conversion of fructose to 5-hydroxymethylfurfural (the most abundant compound obtained) and was further improved by the contemporary presence of the heteropolyacid, at least for the highest initial fructose concentration. In the latter conditions, the highest yield of 5-hydroxymethylfurfural (>40%) was also obtained.

Catalytic Dehydration of Fructose to 5-Hydroxymethylfurfural in Aqueous Medium over Nb2O5-Based Catalysts.

The catalytic dehydration of fructose to 5-hydroxymethylfurfural (HMF) in water was performed in the presence of pristine Nb2O5 and composites containing Nb and Ti, Ce or Zr oxides. In all experiments, fructose was converted to HMF using water as the solvent. The catalysts were characterized by powder X-ray diffraction, scanning electron microscopy, N2 physical adsorption, infrared and Raman spectroscopy and temperature-programmed desorption of NH3. Experimental parameters such as fructose initial concentration, volume of the reacting suspension, operation temperature, reaction time and amount of catalyst were tuned in order to optimize the catalytic reaction process. The highest selectivity to HMF was ca. 80% in the presence of 0.5 g·L-1 of bare Nb2O5, Nb2O5-TiO2 or Nb2O5-CeO2 with a maximum fructose conversion of ca. 70%. However, the best compromise between high conversion and high selectivity was reached by using 1 g·L-1 of pristine Nb2O5. Indeed, the best result was obtained in the presence of Nb2O5, with a fructose conversion of 76% and a selectivity to HMF of 75%, corresponding to the highest HMF yield (57%). This result was obtained at a temperature of 165° in an autoclave after three hours of reaction by using 6 mL of 1 M fructose suspension with a catalyst amount equal to 1 g·L-1.

Titania-Silica Materials for Enhanced Photocatalysis.

Mesoporous titania-organosilica nanoparticles comprised of anatase nanocrystals crosslinked with organosilica moieties have been prepared by direct co-condensation of a titania precursor, tetrabuthylortotitanate (TBOT), with two organosilica precursors, 1,4-bis(triethoxysilyl) benzene (BTEB) and 1,2-bis(triethoxysilyl) ethane (BTEE), in mild conditions and in the absence of surfactant. These hybrid materials show both high surface areas (200-360 m(2) g(-1) ) and pore volumes (0.3 cm(3) g(-1) ) even after calcination, and excellent photoactivity in the degradation of rhodamine 6G and in the partial oxidation of propene under UV irradiation, especially after the calcination of the samples. During calcination, there is a change in the Ti(IV) coordination and an increase in the content of SiOTi moieties in comparison with the uncalcined materials, which seems to be responsible for the enhanced photocatalytic activity of hybrid titania-silica materials as compared to both uncalcined samples and the control TiO2 .