High-Entropy Diborides-Silicon Carbide Composites by Reactive and Non-Reactive Spark Plasma Sintering: A Comparative Study.

The reactive spark plasma sintering (R-SPS) method was compared in this work with the two-step SHS-SPS route, based on the combination of the self-propagating high-temperature synthesis (SHS) with the SPS process, for the fabrication of dense (Hf0.2Mo0.2Ti0.2Ta0.2Nb0.2)B2-SiC and (Hf0.2Mo0.2Ti0.2Ta0.2Zr0.2)B2-SiC ceramics. A multiphase and inhomogeneous product, containing various borides, was obtained at 2000 °C/20 min by R-SPS from transition metals, B4C, and Si. In contrast, if the same precursors were first reacted by SHS and then processed by SPS under the optimized condition of 1800 °C/20 min, the desired ceramics were successfully attained. The resulting sintered samples possessed relative densities above 97% and displayed uniform microstructures with residual oxide content <2.4 wt.%. The presence of SiC made the sintering temperature milder, i.e., 150 °C below that needed by the corresponding additive-free system. The fracture toughness was also markedly improved, particularly when considering the Nb-containing system processed at 1800 °C/20 min, whereas the fracture toughness progressively decreased (from 7.35 to 5.36 MPa m1/2) as the SPS conditions became more severe. SiC addition was found to inhibit the volatilization of metal oxides like MoO3 formed during oxidation experiments, thus avoiding mass loss in the ceramics. The benefits above also likely took advantage of the fact that the two composite constituents were synthesized in parallel, according to the SHS-SPS approach, rather than being produced separately and combined subsequently, so that strong interfaces between them were formed.

Comparative toxicological analysis of two pristine carbon nanomaterials (graphene oxide and aminated graphene oxide) and their corresponding degraded forms using human in vitro models.

Despite the wide application of graphene-based materials, the information of the toxicity associated to some specific derivatives such as aminated graphene oxide is scarce. Likewise, most of these studies analyse the pristine materials, while the available data regarding the harmful effects of degraded forms is very limited. In this work, the toxicity of graphene oxide (GO), aminated graphene oxide (GO-NH2), and their respective degraded forms (dGO and dGO-NH2) obtained after being submitted to high-intensity sonication was evaluated applying in vitro assays in different models of human exposure. Viability and ROS assays were performed on A549 and HT29 cells, while their skin irritation potential was tested on a reconstructed human epidermis model. The obtained results showed that GO-NH2 and dGO-NH2 substantially decrease cell viability in the lung and gastrointestinal models, being this reduction slightly higher in the cells exposed to the degraded forms. In contrast, this parameter was not affected by GO and dGO which, conversely, showed the ability to induce higher levels of ROS than the pristine and degraded aminated forms. Furthermore, none of the materials is skin irritant. Altogether, these results provide new insights about the potential harmful effects of the selected graphene-based nanomaterials in comparison with their degraded counterparts.

Toxicological assessment of pristine and degraded forms of graphene functionalized with MnOx nanoparticles using human in vitro models representing different exposure routes.

The development of novel advanced nanomaterials (NMs) with outstanding characteristics for their use in distinct applications needs to be accompanied by the generation of knowledge on their potential toxicological impact, in particular, that derived from different occupational risk exposure routes, such as inhalation, ingestion, and skin contact. The harmful effects of novel graphene-metal oxide composites on human health are not well understood, many toxicological properties have not been investigated yet. The present study has evaluated several toxicological effects associated with graphene decorated with manganese oxide nanoparticles (GNA15), in a comparative assessment with those induced by simple graphene (G2), on human models representing inhalation (A549 cell line), ingestion (HT29 cell line) and dermal routes (3D reconstructed skin). Pristine and degraded forms of these NMs were included in the study, showing to have different physicochemical and toxicological properties. The degraded version of GNA15 (GNA15d) and G2 (G2d) exhibited clear structural differences with their pristine counterparts, as well as a higher release of metal ions. The viability of respiratory and gastrointestinal models was reduced in a dose-dependent manner in the presence of both GNA15 and G2 pristine and degraded forms. Besides this, all NMs induced the production of reactive oxygen species (ROS) in both models. However, the degraded forms showed to induce a higher cytotoxicity effect. In addition, we found that none of the materials produced irritant effects on 3D reconstructed skin when present in aqueous suspensions. These results provide novel insights into the potentially harmful effects of novel multicomponent NMs in a comprehensive manner. Furthermore, the integrity of the NMs can play a role in their toxicity, which can vary depending on their composition and the exposure route.

Solid State Processing of BCZT Piezoceramics Using Ultra Low Synthesis and Sintering Temperatures.

Lead-free (Ba0.92Ca0.08) (Ti0.95 Zr0.05) O3 (BCZT) ceramics were prepared by a solid-state route (SSR) using ultra-low synthesis (700 °C/30 min and 700 °C/2 h) and sintering temperatures (from 1150 °C to 1280 °C), due to prior activation and homogenization by attrition milling of the starting high purity raw materials for 6 h before the synthesis and of the calcined powders for 3 h before the sintering. The comparison of the thermal analysis of the mixture of the starting raw materials and the same mixture after 6 h attrition milling allowed to evidence the mechanisms of activation, resulting in a significant decrease of the perovskite formation temperature (from 854 °C down to 582 °C). The secondary phases that limit the functional properties of the ceramic and their evolution with the sintering conditions were analyzed by X-ray diffraction (XRD) and scanning electron microscopy (SEM), which allowed the design of a two-step sintering method to eliminate them. A pure tetragonal BCZT perovskite phase (P4mm, c/a = 1.004) and homogeneous ceramic microstructure was obtained for synthesis at 700 °C for 2 h and sintering with the use of a two-step sintering treatment (900 °C for 3 h and 1280 °C for 6 h). The best electromechanical properties achieved were d33 = 455 pC/N, kp = 35%, Qm = 155.

Mechanochemical effects underlying the mechanically activated catalytic hydrogenation of carbon monoxide.

In this work, we highlight and measure the intensity of mechanochemical effects at work in the hydrogenation of carbon monoxide by comparing the activity of a supported Co-Fe catalyst subjected, respectively, to ball milling and simple powder agitation. Paying due regard to the discontinuous nature of ball milling, we show that mechanochemical hydrogenation proceeds at significantly higher rate and disclose its connection with individual impacts. Experimental evidence suggests that the enhanced catalytic activity we observe can be ascribed to local processes affecting the amount of powder that gets involved in individual impacts.

Harnessing Molecular Fluorophores in the Carbon Dots Matrix: The Case of Safranin O.

The origin of fluorescence in carbon dots (C-dots) is still a puzzling phenomenon. The emission is, in most of the cases, due to molecular fluorophores formed in situ during the synthesis. The carbonization during C-dots processing does not allow, however, a fine control of the properties and makes finding the source of the fluorescence a challenging task. In this work, we present a strategy to embed a pre-formed fluorescent molecule, safranin O dye, into an amorphous carbonaceous dot obtained by citric acid carbonization. The dye is introduced in the melted solution of citric acid and after pyrolysis remains incorporated in a carbonaceous matrix to form red-emitting C-dots that are strongly resistant to photobleaching. Embedding dyes in amorphous C-dots represents an alternative method to optimize the emission in the whole visible spectrum.

Chemical effects induced by the mechanical processing of granite powder.

Starting from 1970s, the use of mechanical forces to induce chemical transformations has radically changed vast areas of metallurgy and materials science. More recently, mechanochemistry has expanded to core sectors of chemistry, showing the promise to deeply innovate chemical industry while enhancing its sustainability and competitiveness. We are still far, however, from unveiling the full potential of mechanical activation. This study marks a step forward in this direction focusing on the chemical effects induced on the surrounding gaseous phase by the mechanical processing of granite. We show that fracturing granite blocks in oxygen can result in the generation of ozone. The refinement of coarse granite particles and the friction between fine ones are also effective in this regard. Combining experimental evidence related to the crushing of large granite samples by uniaxial compression and the ball milling of coarse and fine granite powders, we develop a model that relates mechanochemical ozone generation to the surface area effectively affected by fracture and frictional events taking place during individual impacts. We also extend the investigation to gaseous phases involving methane, oxygen, benzene and water, revealing that chemical transformations occur as well.

Improving the Photocatalytic Activity of Mesoporous Titania Films through the Formation of WS2/TiO2 Nano-Heterostructures.

Heterostructures formed by anatase nanotitania and bidimensional semiconducting materials are expected to become the next-generation photocatalytic materials with an extended operating range and higher performances. The capability of fabricating optically transparent photocatalytic thin films is also a highly demanded technological issue, and increasing the performances of such devices would significantly impact several applications, from self-cleaning surfaces to photovoltaic systems. To improve the performances of such devices, WS2/TiO2 heterostructures obtained by incorporating two-dimensional transition metal dichalcogenides layers into titania mesoporous ordered thin films have been fabricated. The self-assembly process has been carefully controlled to avoid disruption of the order during film fabrication. WS2 nanosheets of different sizes have been exfoliated by sonication and incorporated in the mesoporous films via one-pot processing. The WS2 nanosheets result as well-dispersed within the titania anatase mesoporous film that retains a mesoporous ordered structure. An enhanced photocatalytic response due to an interparticle electron transfer effect has been observed. The structural characterization of the heterostructure has revealed a tight interplay between the matrix and nanosheets rather than a simple additive co-catalyst effect.

Unveiling redox mechanism at the iron centers in the mechanochemically activated conversion of CO2 in the presence of olivine.

The transformation of olivine during the conversion of CO2 to light hydrocarbons activated by mechanochemical treatments at different impact frequencies was studied by a combination of several complementary characterization methods including X-ray diffraction, Raman and 57Fe Mössbauer spectroscopy. Several olivine samples were studied as a function of the milling time, indicating the gradual transformation of FeII-containing olivine into new FeIII-containing weathering products including iron oxides, magnesium iron carbonates and silicates. The results presented here complement those of a previous study on the weathering process of olivine promoted by mechanochemical activation, by demonstrating the role of the redox activity of the iron species during the activation process. These additional spectroscopic results allow us to thoroughly understand the complex weathering mechanism and to correlate it with the efficiency of the CO2 conversion and storage properties of mechanochemically activated olivine. Supplementary Information: The online version contains supplementary material available at 10.1007/s10853-022-06962-x.

Comparative Evaluation of Graphene Nanostructures in GERS Platforms for Pesticide Detection.

Graphene-enhanced Raman scattering (GERS) produces enhancement of the Raman signal, which is based on chemical rather than electromagnetic mechanism such as in the surface-enhanced Raman scattering. Graphene oxide, amino- and guanidine-functionalized graphene oxide, exfoliated graphene, and commercial graphene nanoplatelets have been used to investigate the GERS response with the change of graphene properties. Different graphene nanostructures have been embedded into organic-inorganic microporous films to build a platform for the fast and sensitive detection of pesticides in water. The graphene nanostructures vary in the number of layers, lateral size, degree of oxidation, and surface functionalization. The GERS performances of the graphene nanostructures cast on silicon substrates and embedded in the nanocomposite films have been comparatively evaluated. After casting a few droplets of the pesticide aqueous solution on the graphene nanostructures, the Raman band enhancements of the analytes have been measured. In the nanocomposite films, the characteristic Raman bands originating from pesticides such as paraoxon, parathion, and glyphosate could be traced at concentrations below 10-7, 10-5, and 10-4 M, respectively. The results show that the surface functionalization reduces the GERS effect because it increases the ratio between the sp3 carbon and sp2 carbon. On the other hand, the comparison among different types of graphenes shows that the monolayers are more efficient than the few-layer nanostructures in enhancing the Raman signal.

Processing Optimization and Toxicological Evaluation of "Lead-Free" Piezoceramics: A KNN-Based Case Study.

Due to the ever-increasing limitations of the use of lead-based materials, the manufacturing of lead-free piezoceramics with competitive piezoelectric properties and established nontoxicity is considered a priority for the scientific and industrial community. In this work, a lead-free system based on sodium potassium niobate (KNN), opportunely modified with MgNb2O6 (MN), was prepared through a combination of a mechanochemical activation method and air sintering, and its toxicity was evaluated. The effect of the mechanical processing on the microstructure refinement of the processed powders was established by X-ray diffraction and the average crystallite size content of the Nb2O5 species was evaluated. The experimental evidence was rationalized using a phenomenological model which permitted us to obtain the amount of powder processed at each collision and to optimize the activation step of the pre-calcined reagents. This influenced the final density and piezoresponse of the as-sintered pellets, which showed optimal properties compared with other KNN systems. Their toxicological potential was evaluated through exposure experiments to the pulverized KNN-based pellets, employing two widely used human and environmental cellular models. The in vitro assays proved, under the selected conditions, the absence of cytotoxicity of KNN-bases systems here studied.

MgNb2 O6 Modified K0.5 Na0.5 NbO3 Eco-Piezoceramics: Scalable Processing, Structural Distortion and Complex Impedance at Resonance.

In this work, piezoceramics of the lead-free composition K0.5 Na0.5 NbO3 with an increasing amount of MgNb2 O6 (0, 0.5, 1, 2 wt.%) were prepared through conventional solid-state synthesis and sintered in air atmosphere at 1100 °C. The effect of magnesium niobate addition on structure, microstructure and piezoelectric properties was evaluated. The ceramics maintain the orthorhombic Amm2 phase for all compositions, while an orthorhombic Pbcm secondary phase was found for increasing the concentration of MgNb2 O6 . Our results show that densification of these ceramics can be significantly improved up to 94.9 % of theoretical density by adding a small amount of magnesium-based oxide (1 wt.%). Scanning electron microscopy morphology of the 1 wt.% system reveals a well-packed structure with homogeneous grain size of ∼2.72 µm. Dielectric and piezoelectric properties become optimal for 0.5-1.0 wt.% of MgNb2 O6 that shows, with respect to the unmodified composition, either higher piezoelectric coefficients, lower anisotropy and relatively low piezoelectric losses (d33 =97 pC N-1 ; d31 =-36.99 pC N-1 and g31 =-14.04×10-3  mV N-1 ; Qp (d31 )=76 and Qp (g31 )=69) or enhanced electromechanical coupling factors (kp =29.06 % and k31 =17.25 %).

Boron Nitride-Titania Mesoporous Film Heterostructures.

The fabrication of optically active heterostructures in the shape of mesostructured thin films is a highly challenging task. It requires an integrated process to allow in one-step incorporating the two-dimensional materials within the mesoporous ordered host without disrupting the pore organization. Hexagonal boron nitride (BN) nanosheets have been successfully introduced into titania mesoporous films using a template-assisted sol-gel synthesis and evaporation-induced self-assembly. Two types of BN sheets have been used, with and without defects, to investigate the role of defects in heterostructure properties. It has been found that the defects increase the ultraviolet radiation A (UVA) absorbance and enhance the photocatalytic response of the film. The BN sheets are optically transparent and do not exhibit any photocatalytic property but contribute to anatase crystallization via heterogeneous nucleation.

A Simple Ball Milling and Thermal Oxidation Method for Synthesis of ZnO Nanowires Decorated with Cubic ZnO2 Nanoparticles.

In this work, we propose the synthesis of ZnO nanostructures through the thermal oxidation of ball-milled powders with the introduction of Mg and Sn doping species at the preliminary step of milling. We investigate the advantages and challenges of this two steps process for the production and fabrication of highly crystalline ZnO nanowires. This simple method allows us to fabricate ZnO nanowires with a higher quality core crystal at a much lower temperature and for a shorter processing time than the state-of-the-art, and decorated with by ZnO2 nanoparticles as determined via TEM analysis. The main findings will show that the crystalline core of the nanowires is of hexagonal ZnO while the nanoparticles on the surface are ZnO2 cubic type. Generally, the method proves to be suitable for applications that require a high surface-to-volume ratio, for example, catalysis phenomena, in which the presence of zinc oxides species can play an important role.

In situ synchrotron radiation investigation of V2O5-Nb2O5 metastable compounds: transformational kinetics at high temperatures with a new structural solution for the orthorhombic V4Nb20O60 phase.

Due to the considerable interest in vanadium niobium oxides as a lithium storage material, the kinetics and transformation processes of the V2O5-5Nb2O5 system have been investigated by in situ synchrotron powder X-ray diffraction. The diffraction data after the thermal treatments selected with a view on the most significant features were supplemented with specific ex situ experiments conducted using a laboratory rotating anode X-ray diffractometer. The morphological changes of the mixed powders assuming an amorphous and nanocrystalline solid solution structure as a function of the temperature were inspected by scanning electron microscopy observations. The structural solution of the powder diffraction pattern of the phase recorded in situ at a temperature of about 700 °C was compatible with an orthorhombic crystal structure with the space group Amm2. The obtained lattice parameters for this structure were a = 3.965 Å; b = 17.395 Å, c = 17.742 Å, and the cell composition was V4Nb20O60, Pearson symbol oA84, and density = 4.10 g cm-3. In this structure, while the niobium atoms may be four-, five-, and six-fold coordinated by oxygen atoms, the vanadium atoms were six-fold or seven-fold coordinated. At the temperature of 800 °C and just above, the selected 1 : 2 and 1 : 3 V2O5-Nb2O5 compositions, respectively, returned mostly a tetragonal VNb9O25 phase, in line with earlier observations conducted for determination of the stability phase diagram of such quasi-binary systems.

Study of the Effects Induced by Ball Milling Treatment on Different Types of Hydrocolloids in a Corn Starch-Rice Flour System.

The effects of ball milling treatment on both the structure and properties of guar gum (GG), tara gum (TG), and methylcellulose (MC) were analyzed prior to assessing their potential interactions with starch components when they are used alone or in blends in a corn starch-rice flour system. X-ray diffraction profiles showed that the ball milling caused a reduction in the crystallin domain and, in turn, a diminished viscosity of the GG aqueous solutions. Despite an increase in its viscosity properties, effects on TG were minimal, while the milled MC exhibited reduced crystallinity, but similar viscosity. When both milled and un-milled hydrocolloids were individually added to the starch-flour system, the pasting properties of the resulting mixtures seemed to be affected by the type of hydrocolloid added rather than the structural changes induced by the treatment. All hydrocolloids increased the peak viscosity of the binary blends (especially pure GG), but only milled and un-milled MC showed values of setback and final viscosity similar to those of the individual starch. Ball milling seemed to be more effective when two combined hydrocolloids (milled GG and MC) were simultaneously used. No significant differences were observed in the viscoelastic properties of the blends, except for un-milled GG/starch, milled TG/starch, and milled MC/milled TG/starch gels.

Integrating sol-gel and carbon dots chemistry for the fabrication of fluorescent hybrid organic-inorganic films.

Highly fluorescent blue and green-emitting carbon dots have been designed to be integrated into sol-gel processing of hybrid organic-inorganic materials through surface modification with an organosilane, 3-(aminopropyl)triethoxysilane (APTES). The carbon dots have been synthesised using citric acid and urea as precursors; the intense fluorescence exhibited by the nanoparticles, among the highest reported in the scientific literature, has been stabilised against quenching by APTES. When the modification is carried out in an aqueous solution, it leads to the formation of silica around the C-dots and an increase of luminescence, but also to the formation of large clusters which do not allow the deposition of optically transparent films. On the contrary, when the C-dots are modified in ethanol, the APTES improves the stability in the precursor sol even if any passivating thin silica shell does not form. Hybrid films containing APTES-functionalized C-dots are transparent with no traces of C-dots aggregation and show an intense luminescence in the blue and green range.

Enhanced Stability of Li-RHC Embedded in an Adaptive TPX™ Polymer Scaffold.

In this work, the possibility of creating a polymer-based adaptive scaffold for improving the hydrogen storage properties of the system 2LiH+MgB2+7.5(3TiCl3·AlCl3) was studied. Because of its chemical stability toward the hydrogen storage material, poly(4-methyl-1-pentene) or in-short TPXTM was chosen as the candidate for the scaffolding structure. The composite system was obtained after ball milling of 2LiH+MgB2+7.5(3TiCl3·AlCl3) and a solution of TPXTM in cyclohexane. The investigations carried out over the span of ten hydrogenation/de-hydrogenation cycles indicate that the material containing TPXTM possesses a higher degree of hydrogen storage stability.

Carbon Dots from Citric Acid and its Intermediates Formed by Thermal Decomposition.

Thermal decomposition of citric acid is one of the most common synthesis methods for fluorescent carbon dots; the reaction pathway is, however, quite complex and the details are still far from being understood. For instance, several intermediates form during the process and they also give rise to fluorescent species. In the present work, the formation of fluorescent C-dots from citric acid has been studied as a function of reaction time by coupling infrared analysis, X-ray photoelectron spectroscopy, liquid chromatography/mass spectroscopy (LC/MS) with the change of the optical properties, absorption and emission. The reaction intermediates, which have been identified at different stages, produce two main emissive species, in the green and blue, as also indicated by the decay time analysis. C-dots formed from the intermediates have also been synthesised by thermal decomposition, which gave an emission maximum around 450 nm. The citric acid C-dots in water show short temporal stability, but their functionalisation with 3-aminopropyltriethoxysilane reduces the quenching. The understanding of the citric acid thermal decomposition reaction is expected to improve the control and reproducibility of C-dots synthesis.

A mechanochemical route for the synthesis of VNbO5 and its structural re-investigation using structure solution from powder diffraction data.

A new and solvent-free synthesis route has been adopted and optimized to prepare crystalline VNbO5 from the mechanochemical reaction between Nb2O5 and V2O5 as starting reagents. The substantially amorphous mixture of equimolar pentoxide V and Nb metals observed after extended mechanical treatment transforms into a crystalline powder following calcination under mild conditions at 710 K. The structure solution of the X-ray diffraction pattern using a global optimization approach, combined with Rietveld refinement, points to a space group P212121 (no. 19) different from Pnma (no. 62) previously proposed in the literature assuming it to be isostructural to VTaO5. The new space group helps to describe weak peaks that remained previously unaccounted for and allows more reliable determination of atomic fractional coordinates and interatomic distance distribution. The as-prepared VNbO5 has been tested as a dopant (5 wt%) for the purpose of solid state hydrogen storage, decreasing significantly the release of hydrogen of MgH2/Mg (620 K) and further enhancing the hydrogen sorption kinetic properties.