Cryo-FIB-nanotomography for quantitative analysis of particle structures in cement suspensions.

Cryo-FIB-nanotomography is a novel high-resolution 3D-microscopy technique, which opens new possibilities for the quantitative microstructural analysis of complex suspensions. In this paper, we describe the microstructural changes associated with dissolution and precipitation processes occurring in a fresh cement paste, which has high alumina and sulphate contents. During the first 6 min, precipitation of ettringite leads to a general decrease of the particle size distribution. In the unhydrated cement paste almost no particles smaller than 500 nm are present, whereas after 6 min this size class already represents 9 vol%. The precipitation of ettringite also leads to a significant increase of the particle number density from 0.294*10(9)/mm(3) at t(0min) to 20.55*10(9)/mm(3) at t(6min). Correspondingly the surface area increases from 0.75 m(2)/g at t(0min) to 2.13 m(2)/g at t(6min). The small ettringite particles tend to form agglomerates, which strongly influence the rheological properties. The particular strength of cryo-FIB-nt is the potential to quantify particle structures in suspension and thereby also to describe higher-order topological features such as the particle-particle interfaces, which is important for the study of agglomeration processes.

Three-dimensional analysis of porous BaTiO3 ceramics using FIB nanotomography.

Three-dimensional (3D) data represent the basis for reliable quantification of complex microstructures. Therefore, the development of high-resolution tomography techniques is of major importance for many materials science disciplines. In this paper, we present a novel serial sectioning procedure for 3D analysis using a dual-beam FIB (focused ion beam). A very narrow and reproducible spacing between the individual imaging planes is achieved by using drift correction algorithms in the automated slicing procedure. The spacing between the planes is nearly of the same magnitude as the pixel resolution on scanning electron microscopy images. Consequently, the acquired stack of images can be transformed directly into a 3D data volume with a voxel resolution of 6 x 7 x 17 nm. To demonstrate the capabilities of FIB nanotomography, a BaTiO3 ceramic with a high volume fraction of fine porosity was investigated using the method as a basis for computational microstructure analysis and the results compared with conventional physical measurements. Significant differences between the particle size distributions as measured by nanotomography and laser granulometry indicate that the latter analysis is skewed by particle agglomeration/aggregation in the raw powder and by uncertainties related to calculation assumptions. Significant differences are also observed between the results from mercury intrusion porosimetry (MIP) and 3D pore space analysis. There is strong evidence that the ink-bottle effect leads to an overestimation of the frequency of small pores in MIP. FIB nanotomography thus reveals quantitative information of structural features smaller than 100 nm in size which cannot be acquired easily by other methods.