Severe Crowding Associated with Lower Canine Premature Resorption: Interceptive Treatment with Clear Aligners-A Pilot Study.

BACKGROUND: Early mixed dentition represents a critical phase since crowding conditions can occur. The interceptive resolution of dental crowding allows favorable arch and occlusal development. The aim of the present investigation was to evaluate dentoalveolar changes of clear aligner treatment planned to manage lower incisor crowding, loss of arch length, and midline deviation in early mixed dentition. METHODS: A total of 13 patients (7 females, 6 males, 9.4 ± 1.2 age) treated with clear aligners were selected. Arch dimensions and incisor inclinations were evaluated before (T0) and at the end of interceptive treatment (T1). A paired t-test was chosen to compare T1-T0 changes. The level of significance was set at 5%. RESULTS: The greatest significant increase in mandibular width was observed at the level of the first deciduous molars (+2.44 ± 1.4 mm), followed by the second permanent molars (+2.16 ± 1.4 mm). Lower arch length and arch depth showed a statistically relevant increase (2 ± 0.6 mm and 4.5 ± 1.6 mm, respectively). The mean lower dental midline changes were statistically significant (1.42 ± 0.73 mm). CONCLUSIONS: Early treatment with clear aligners, including the combination of transversal arch development, maintenance of leeway space, and guidance of eruption, represents a valid treatment strategy in early mixed dentition to manage arch crowding and occlusion development.

Friction and wear behavior of a mechanical oscillating strip system used for interproximal enamel reduction: a quantitative and qualitative scanning electronic microscope evaluation.

OBJECTIVES: To evaluate wear and friction properties of oscillating strips in order to validate the importance of a standardized interproximal enamel reduction (IPR) sequence to preserve their efficiency and lifetime. MATERIALS AND METHODS: Fifteen complete oscillating IPR sequences were tested by means of tribological tests (Linear Reciprocating Tribometer, C.S.M. Instruments, Peseaux, Switzerland). Fifteen single 0.2-mm metallic strips underwent a long continuous cycle of 240 minutes. Strip surface roughness and waviness measurements were assessed by means of a contact probe surface profiler (TalySurf CLI 2000; Taylor Hobson, Leicester, UK) and TayMap software. Statistical analysis was performed with independent-samples t-test. Significance was at the P < .05 level. Scanning electronic microscopy analysis of strip surfaces was conducted with an FEI Quanta 200 (Hillsboro, Ore) in high vacuum at 30.00 kV. RESULTS: Resin strips revealed a significant reduction in surface roughness (Ra, Rt, RDq) and a significant increase in waviness parameters (Wa, Wt). Rt and RDq values significantly decreased upon use of the metallic strips. Significantly higher values of Wa (+ 2.84 µm) and Wt (+0.1 µm) were observed only for the 0.2-mm metallic strips. Higher friction values were observed when the metallic strips were tested singularly rather than within the entire sequence. Lower Ra and Rt values were revealed when 0.2-mm metallic strips were tested up to 240 minutes. CONCLUSIONS: The application of a standardized oscillating sequence allows for more efficient wear performance of the strips with a significant impact on their abrasive power and lifetime.