Development of nanobiosilicate, tricalcium phosphate and chlorhexidine materials for biomineralization with crystallographic similarity to hydroxyapatite and biomodified collagen.

OBJECTIVES: The aim of this work is to test experimental cements, doped with a silicate based bioactive nanoparticle (NanoBiosilicate). Methods, we synthesized a glass nanoparticle by Sol-Gel Stöber method, used to be incorporated in a dental material for endodontic uses. MATERIALS AND METHODS: We assess the mineralizing properties and biocompatibility. Besides the crystallography characterization of the resultant new crystals. Results, After analysis, and comparison with commercial materials, the material tested was similar in mechanical properties required by ISO, The ion release was effective after 2 hr. of setting and the novel material was cell compatible accepted by ISO. RESULTS: We found new formed Calcium Phosphate peaks in the spectroscopic analysis (FTIR), remarkably the crystals formed were comparable to hydroxyapatite when analyzed with a Selected Area Electron Diffractometer, with rings of 2.84 Å for 002, and the 2.77 Å is also visible for 210. The 6.83 Å and 6.88 Å, for respective 222 and 004. The incorporation of Chlorhexidine was not detrimental for this property, Significance, the features mentioned represented a progress in biomineralization field that was associated to an improved mineral structure formation with increased crystallographic similarity to natural hydroxyapatite. When chlorhexidine was added a favorable biomodification of the remaining collagen in dentinal walls and antimicrobial activity potential were also observed.

Surface Analysis of a Universal Resin Composite and Effect of Preheating on its Physicochemical Properties.

This study was aimed at analyzing the surface properties of a universal resin composite and evaluating the effect of preheating on its physicochemical properties. Two commercial resin composites were used under two conditions: Filtek Universal Restorative (UR); UR preheated (URH); Filtek Supreme (FS) and FS preheated (FSH). The film thickness (FT) test (n = 10) was done using two glass slabs under compression. Flexural strength (FLS) and modulus (FLM) were evaluated using a three-point flexion test (n = 10). Polymerization shrinkage stress (PSS) was evaluated in a universal testing machine (n = 5). Gap width (GW) between composite and mold was measured in internally polished metallic molds (n = 10). The degree of conversion (DC) was evaluated by Fourier Transform Infrared spectroscopy (n = 3). The morphology of the filler particles was checked by scanning electron microscope (SEM) and EDX analysis. Surface gloss (SG) and surface roughness (SR) were evaluated before and after mechanical brushing (n = 10). The outcomes were submitted to 2-way ANOVA and Tukey's test (α = 0.05). Lower mean values of FT were observed for the preheated groups when compared to the non-preheated groups. URH and FSH showed higher mean values of FLS and FLM when compared with UR and FS. No differences were observed between groups in the PSS test. The GW was higher for the UR and FS groups when compared with URH and FSH. The DC was higher for preheated resin composites when compared to the non-preheated groups. The SR of the UR composite was higher than the FS after mechanical brushing, while the SG was higher for the FS groups. In conclusion, the universal resin composite tested generally presented similar physicochemical properties compared with the nanofilled resin composite and either similar or slightly inferior surface properties. The preheating improved or maintained all properties evaluated.

Effect of elastomeric urethane monomer on physicochemical properties and shrinkage stress of resin composites.

This study aimed to evaluate the effect of an elastomeric urethane monomer (Exothane-24) in different concentrations on physicochemical properties, gap formation, and polymerization shrinkage stress of experimental resin composites. All experimental composites were prepared with 50 wt.% of Bis-GMA and 50 wt.% of TEGDMA, to which 0 wt.% (control), 10 wt.%, 20 wt.%, 30 wt.%, and 40 wt.% of Exothane-24 were added. Filler particles (65 wt.%) were then added to these resin matrixes. Ultimate tensile strength (UTS: n = 10), flexural strength (FS: n = 10), flexural modulus (FM: n = 10), hardness (H: n = 10), hardness reduction (HR: n = 10), degree of conversion (DC: n = 5), gap width (GW: n = 10), and polymerization shrinkage stress in Class I (SS-I: n = 10) and Class II (SS-II: n = 10) simulated configuration. All test data were analyzed using one-way ANOVA and Tukey's test (α = 0.05;  = 0.2). Exothane-24 in all concentrations decreased the H, HR, DC, GW, SS-I, and SS-II (p < 0.05) without affecting the UTS, and FS (p > 0.05). Reduction in FM was observed only in the Exothane 40% and 30% groups compared to the control (p < 0.05). Exothane-24 at concentrations 20% and 30% seems suitable since it reduced GW and polymerization SS without affecting the properties of the composite resins tested, except for H.

Surface Analysis of a Universal Resin Composite and Effect of Preheating on its Physicochemical Properties

Abstract This study was aimed at analyzing the surface properties of a universal resin composite and evaluating the effect of preheating on its physicochemical properties. Two commercial resin composites were used under two conditions: Filtek Universal Restorative (UR); UR preheated (URH); Filtek Supreme (FS) and FS preheated (FSH). The film thickness (FT) test (n = 10) was done using two glass slabs under compression. Flexural strength (FLS) and modulus (FLM) were evaluated using a three-point flexion test (n = 10). Polymerization shrinkage stress (PSS) was evaluated in a universal testing machine (n = 5). Gap width (GW) between composite and mold was measured in internally polished metallic molds (n = 10). The degree of conversion (DC) was evaluated by Fourier Transform Infrared spectroscopy (n = 3). The morphology of the filler particles was checked by scanning electron microscope (SEM) and EDX analysis. Surface gloss (SG) and surface roughness (SR) were evaluated before and after mechanical brushing (n = 10). The outcomes were submitted to 2-way ANOVA and Tukey's test (α = 0.05). Lower mean values of FT were observed for the preheated groups when compared to the non-preheated groups. URH and FSH showed higher mean values of FLS and FLM when compared with UR and FS. No differences were observed between groups in the PSS test. The GW was higher for the UR and FS groups when compared with URH and FSH. The DC was higher for preheated resin composites when compared to the non-preheated groups. The SR of the UR composite was higher than the FS after mechanical brushing, while the SG was higher for the FS groups. In conclusion, the universal resin composite tested generally presented similar physicochemical properties compared with the nanofilled resin composite and either similar or slightly inferior surface properties. The preheating improved or maintained all properties evaluated.

Resumo Neste estudo avaliou-se propriedades físico-químicas e de superfície de um compósito universal pré-aquecido e comparado a um compósito convencional. Foram utilizados dois compósitos comerciais: Filtek Universal Restorative (UR); UR pré-aquecido (URH); Filtek Supreme (FS) e FS pré-aquecido (FSH). O teste de espessura de película (EP) (n = 10) foi feito usando duas placas de vidro sob compressão. A resistência à flexão (RF) e o módulo flexural (MF) foram avaliados por meio do teste de flexão de três pontos (n = 10). A tensão de contração de polimerização (TCP) foi avaliada em uma máquina de teste universal (n = 8). A largura da fenda (LF) entre o compósito e o molde foi medida em moldes metálicos polidos internamente (n = 10). O grau de conversão (GC) foi avaliado por espectroscopia de infravermelho com transformada de Fourier (n = 3). A morfologia das partículas de carga foi observada em microscopia eletrônica de varredura (MEV) e sua composição em EDX. Brilho superficial (BS) e rugosidade superficial (RS) foram avaliados antes e após escovação mecânica (n=10). Os resultados foram submetidos à ANOVA 2-fatores e as médias comparadas pelo teste de Tukey (α = 0,05). Menores valores médios de EP foram observados para os grupos pré-aquecidos quando comparados aos grupos não pré-aquecidos. URH e FSH apresentaram maiores valores médios de RF e MF quando comparados com UR e FS. Não foram observadas diferenças entre os grupos no teste TCP. A LF foi maior para os grupos UR e FS quando comparados com URH e FSH. O GC foi maior para os compósitos pré-aquecidos quando comparados aos não pré-aquecidos. A RS do compósito UR foi maior que o FS após a escovação mecânica, enquanto o BS foi maior para os grupos FS. Em conclusão, o compósito universal testado geralmente apresentou propriedades físico-químicas semelhantes em comparação ao compósito nanoparticulado e propriedades de superfície semelhantes ou ligeiramente inferiores. O pré-aquecimento melhorou ou manteve todas as propriedades avaliadas.

Effect of elastomeric urethane monomer on physicochemical properties and shrinkage stress of resin composites

Abstract This study aimed to evaluate the effect of an elastomeric urethane monomer (Exothane-24) in different concentrations on physicochemical properties, gap formation, and polymerization shrinkage stress of experimental resin composites. All experimental composites were prepared with 50 wt.% of Bis-GMA and 50 wt.% of TEGDMA, to which 0 wt.% (control), 10 wt.%, 20 wt.%, 30 wt.%, and 40 wt.% of Exothane-24 were added. Filler particles (65 wt.%) were then added to these resin matrixes. Ultimate tensile strength (UTS: n = 10), flexural strength (FS: n = 10), flexural modulus (FM: n = 10), hardness (H: n = 10), hardness reduction (HR: n = 10), degree of conversion (DC: n = 5), gap width (GW: n = 10), and polymerization shrinkage stress in Class I (SS-I: n = 10) and Class II (SS-II: n = 10) simulated configuration. All test data were analyzed using one-way ANOVA and Tukey's test (α = 0.05; β= 0.2). Exothane-24 in all concentrations decreased the H, HR, DC, GW, SS-I, and SS-II (p < 0.05) without affecting the UTS, and FS (p > 0.05). Reduction in FM was observed only in the Exothane 40% and 30% groups compared to the control (p < 0.05). Exothane-24 at concentrations 20% and 30% seems suitable since it reduced GW and polymerization SS without affecting the properties of the composite resins tested, except for H.

Resumo Este estudo teve como objetivo avaliar o efeito de um monômero elastomérico de uretano (Exothane-24) em diferentes concentrações em propriedades físico-químicas, formação de fenda e tensão de contração de polimerização de resinas compostas experimentais. Todos os compósitos experimentais foram preparados com 50% em peso de Bis-GMA e 50% em peso de TEGDMA, nos quais 0% (controle), 10%, 20%, 30% e 40% em peso de Exothane-24 foram adicionados. Partículas de carga (65% em peso) foram então adicionadas as matrizes resinosas. Resistência coesiva (RC: n = 10), resistência à flexão (RF: n = 10), módulo de flexão (MF: n = 10), dureza (D: n = 10), redução de dureza (RD: n = 10), grau de conversão (GC: n = 5), largura de fenda (LF: n = 10) e tensão de contração de polimerização em simulações de cavidades Classe I (TC-I: n = 10) e Classe II (TC-II: n = 10). Todos os dados do teste foram analisados usando one-way ANOVA e teste de Tukey (α = 0,05; β = 0,2). O Exothane-24 em todas as concentrações diminuiu a D, RD, GC, LF, TC-I e TC-II (p < 0,05) sem afetar o RC e RF (p > 0,05). A redução da MF foi observada apenas nos grupos Exothane 40% e 30% em relação ao controle (p < 0,05). O Exothane-24 nas concentrações de 20% e 30% pareceu ser adequado, pois reduziu LF e TC de polimerização sem afetar as propriedades das resinas compostas testadas, exceto para D.

Patients´ satisfaction concerning direct anterior dental restoration.

The objective of this study was to observe patients' satisfaction with their in-service direct anterior dental restorations and to compare it with clinical evaluation using FDI (Federation Dental International) criteria. Patients scored their own anterior dental restorations regarding satisfaction (satisfactory /dissatisfactory). If dissatisfaction was mentioned, then, they would be interviewed about the complaint. In the same session, the dental restorations were clinically evaluated by two dentists using FDI criteria (1-5 score) concerning esthetic, functional, and biological domains. Descriptive statistics were used for frequencies of scores attributed by patients and clinicians. In order to compare patients' to clinicians' frequencies, the Chi-square test was applied (p ≤ 0.05). A total of 106 restorations were evaluated by patients and clinicians. Patients reported 52.8% of restorations satisfactory and 47.8% dissatisfactory. Overall, clinicians reported the same restorations as 82,3% satisfactory and 17,6% dissatisfactory. Patients' most frequent complaints referred to color, followed by anatomical form, fracture of material and retention, and approximal anatomical form. Comparing patients' satisfaction and dissatisfaction rates to clinicians' evaluation per criteria, there was no difference regarding esthetics. The frequency of dissatisfactory restorations by clinicians was significantly lower when functional and biological properties were compared with patients' opinions. Direct anterior dental restorations were more frequently reported as satisfactory by patients and clinicians, being the main complaints related to esthetic issues. When clinicians and patients' evaluations were compared, it was observed that the frequencies of satisfactory restoration by patients and clinicians were similar regarding esthetic properties, and significantly different regarding functional and biological properties.

Patients´ satisfaction concerning direct anterior dental restoration

Abstract The objective of this study was to observe patients' satisfaction with their in-service direct anterior dental restorations and to compare it with clinical evaluation using FDI (Federation Dental International) criteria. Patients scored their own anterior dental restorations regarding satisfaction (satisfactory /dissatisfactory). If dissatisfaction was mentioned, then, they would be interviewed about the complaint. In the same session, the dental restorations were clinically evaluated by two dentists using FDI criteria (1-5 score) concerning esthetic, functional, and biological domains. Descriptive statistics were used for frequencies of scores attributed by patients and clinicians. In order to compare patients' to clinicians' frequencies, the Chi-square test was applied (p ≤ 0.05). A total of 106 restorations were evaluated by patients and clinicians. Patients reported 52.8% of restorations satisfactory and 47.8% dissatisfactory. Overall, clinicians reported the same restorations as 82,3% satisfactory and 17,6% dissatisfactory. Patients' most frequent complaints referred to color, followed by anatomical form, fracture of material and retention, and approximal anatomical form. Comparing patients' satisfaction and dissatisfaction rates to clinicians' evaluation per criteria, there was no difference regarding esthetics. The frequency of dissatisfactory restorations by clinicians was significantly lower when functional and biological properties were compared with patients' opinions. Direct anterior dental restorations were more frequently reported as satisfactory by patients and clinicians, being the main complaints related to esthetic issues. When clinicians and patients' evaluations were compared, it was observed that the frequencies of satisfactory restoration by patients and clinicians were similar regarding esthetic properties, and significantly different regarding functional and biological properties.

Resumo O objetivo deste estudo foi observar a satisfação dos pacientes com suas restaurações dentárias anteriores diretas e compará-las com a avaliação clínica do dentista usando os critérios FDI (Federation Dental International). Os pacientes pontuaram suas restaurações dentárias (n=106) anteriores em relação à satisfação (satisfatória / insatisfatória). Quando insatisfatória, ele foi entrevistado sobre a queixa. Na mesma sessão, as restaurações dentárias foram avaliadas clinicamente por dois dentistas utilizando os critérios FDI (escore 1-5) quanto aos aspectos estéticos, funcionais e biológicos. Estatística descritiva foi usada para frequências de escores atribuídos por pacientes e clínicos. Para comparar as frequências dos pacientes e dos clínicos, foi aplicado o teste Qui-quadrado (p ≤ 0,05). Os pacientes relataram suas restaurações como 52,8% satisfatórias e 47,8% insatisfatórias. Os clínicos reportaram as mesmas restaurações, 82,3% satisfatória e 17,6% insatisfatória. As queixas mais frequentes dos pacientes referiam-se à cor, seguida da forma anatômica, fratura e retenção do material e forma anatômica proximal. Comparando os índices de satisfação e insatisfação dos pacientes com os clínicos, não houve diferença em relação à estética. A frequência de restaurações insatisfatórias por dentistas foi significativamente menor quando as propriedades funcionais e biológicas foram comparadas com as opiniões dos pacientes. As restaurações foram mais frequentemente relatadas como satisfatórias pelos pacientes, sendo as principais queixas relacionadas a questões estéticas. Quando as avaliações dos clínicos e dos pacientes foram comparadas, observou-se que as frequências de restaurações satisfatórias por pacientes e clínicos foram semelhantes em relação às propriedades estéticas e significativamente diferentes em relação às propriedades funcionais e biológicas.

Effect of preheating on mechanical properties of a resin-based composite containing elastomeric urethane monomer.

This study investigated the effect of preheating an elastomeric urethane monomer (Exothane-24) experimental resin composite on its physicochemical properties. Two resin matrices were formulated: (a) 50 wt% Bisphenol-glycidyl methacrylate (Bis-GMA) and 50 wt% triethylene glycol dimethacrylate (TEGDMA); and (b) 20 wt% Exothane-24, 40 wt% Bis-GMA and 40 wt% TEGDMA. A photoinitiator system (0.25 wt% camphorquinone and 0.50 wt% ethyl-4-dimethylamino benzoate) and 65 wt% of the inorganic filler (20 wt% 0.05 µm silica and 80 wt% 0.7 µm BaBSiO2 glass) were added to both matrices. These formulations were then assigned to four groups: Exothane-24 (E); Exothane-24 plus preheating (EH); no Exothane-24 (NE); and no Exothane-24 plus preheating (NEH). NEH and EH were preheated at 69 °C. The dependent variables were as follows: film thickness (FT); polymerization shrinkage stress (PSS); gap width (GW); maximum rate of polymerization (Rpmax); and degree of conversion (DC). Data were statistically analyzed by two-way ANOVA and Tukey's test (α = 0.05). Preheating reduced FT for both composites. PSS and GW were significantly lower for EH, when compared with E. The DC for EH and NEH and the Rpmax for EH increased significantly. Preheating improved most of the physicochemical properties (FT, PSS, GW, and DC) of the experimental resin composite containing Exothane-24.

Tunable Release of Calcium from Chitosan-Coated Bioglass.

Bioglass presents a standard biomaterial for regeneration of hard tissues in orthopedics and dentistry. The notable osteo-inductive properties of bioglass are largely due to the release of calcium ions from it. However, this release is not easily controllable and can often be excessive, especially during the initial interaction of the biomaterial with the surrounding tissues. Consequently, this excessive release can deplete the calcium content of the bioglass, ultimately reducing its overall bioactivity. In this study, we have tested if applying biopolymer chitosan coatings of different thicknesses would be able to mitigate and regulate the calcium ion release from monodisperse bioglass nanoparticles. Calcium release was assessed for four different chitosan coating thicknesses at different time points over the period of 28 days using a fluorescence quencher. Expectedly, chitosan-coated particles released less calcium as the concentration of chitosan in the coating solution increased, presumably due to the increased thickness of the chitosan coating around the bioglass particles. The mechanism of release remained constant for each coating thickness, corresponding to anomalous, non-Fickian diffusion, but the degree of anomalousness increased with the deposition of chitosan. Zeta potential testing showed an expected increase in the positive double layer charge following the deposition of the chitosan coating due to the surface exposure of the amine groups of chitosan. Less intuitively, the zeta potential became less positive as thickness of the chitosan coating increased, attesting to the lower density of the surface charges within thicker coatings than within the thinner ones. Overall, the findings of this study demonstrate that chitosan coating efficiently prevents the early release of calcium from bioglass. This coating procedure also allows for the tuning of the calcium release kinetics by controlling the chitosan concentration in the parent solution.

Effect of a polymerization inhibitor on the chemomechanical properties and consistency of experimental resin composites

Abstract This study investigated the effect of butylated hydroxytoluene (BHT) inhibitor on degree of conversion (DC), flexural strength (FS), flexural modulus (FM), Knoop microhardness (KH), microhardness reduction (HR), and consistency of experimental resin composites at different BHT concentrations: C0 (control-0%); C0.01 (0.01%); C0.025 (0.025%); C0.05 (0.05%); C0.1 (0.1%); and C0.5 (0.5%). For the consistency, the composites were tested immediately after being exposed to a dental chair headlight (0, 20, 40 and 60 s). Data concerning DC, FS, FM, KH, and HR were submitted to one-way ANOVA, while the consistency data was submitted to 2-way ANOVA; mean values were then compared (Tukey's test; α=0.05). The KH, FS and FM analyses showed no significant difference among the composites tested. For DC, C0 showed the highest mean value (74.2%) and differed only from C0.5 (67.2%). For HR, C0.5 showed the lowest mean (13.09%) value and differed from C0 (26.4%) and C0.01 (24.87). The consistency analysis showed no difference among C0.05, C0.1 and C0.5, considering 0 and 20 s of light exposure, while C0 (14.07 mm), C0.01 (13.97 mm), and C0.025 (14.18 mm) showed higher mean values at 0 s when compared to 20 s (12.67, 12.77 and 13.05 mm, respectivelly). Polymerization occurred within 40 s of light exposure for C0, C0.01, C0.025, and C0.05 and within 60 s for C0.1. In conclusion, the BHT concentrations had no significant influence on FS, FM and KH. The higher the BHT concentration, the longer was its handling time under light, with a significant improvement in the HR, but a decrease in DC. Therefore, BHT at 0.1% showed the best outcomes concerning all the BHT concentrations tested.

Resumo O objetivo foi investigar o efeito do inibidor de polimerização BHT no grau de conversão (GC), resistência à flexão (RF), módulo de flexão (MF), microdureza Knoop (KH) e redução da microdureza (RKH), e consistência de um compósito experimental contendo diferentes concentrações de BHT (% em peso): C0 - controle (0%); C0,01 (0,01%); C0,025 (0,025%); C0,05 (0,05%); C0,1 (0,1%); e C0,5 (0,5%). Para o teste de consistência, os compósitos foram testados imediatamente após serem expostos à luz de um refletor odontológico por 0, 20, 40 e 60 s. Os dados relativos a GC, RF, MF, KH e RKH foram submetidos a one-way ANOVA, enquanto os dados de consistência foram submetidos a two-way ANOVA; os valores médios foram comparados (teste de Tukey; α = 0,05). As análises de KH, RF e MF não mostraram diferença significativa entre os compósitos testados. Para GC, C0 apresentou o maior valor médio e diferiu apenas de C0,5. Para a RKH, C0,5 apresentou o menor valor médio e diferiu de C0 e C0,01. A análise de consistência não mostrou diferença entre C0,05, C0,1 e C0,5, considerando-se 0 e 20 s de exposição à luz, enquanto C0, C0,01 e C0,025 apresentaram maiores valores médios a 0 s quando comparados a 20 s. A polimerização ocorreu dentro de 40 s de exposição à luz para C0, C0.01, C0.025 e C0.05 e dentro de 60 s para C0.1. Em conclusão, as concentrações de BHT não tiveram influência significativa sobre RF, MF e KH. Quanto maior a concentração de BHT, maior o tempo de manuseio sob luz, com melhora significativa da RKH, mas diminuição da GC. Portanto, o compósito contendo 0,1 % de BHT apresentou os melhores resultados entre as demais concentrações testadas.

Effect of a polymerization inhibitor on the chemomechanical properties and consistency of experimental resin composites.

This study investigated the effect of butylated hydroxytoluene (BHT) inhibitor on degree of conversion (DC), flexural strength (FS), flexural modulus (FM), Knoop microhardness (KH), microhardness reduction (HR), and consistency of experimental resin composites at different BHT concentrations: C0 (control-0%); C0.01 (0.01%); C0.025 (0.025%); C0.05 (0.05%); C0.1 (0.1%); and C0.5 (0.5%). For the consistency, the composites were tested immediately after being exposed to a dental chair headlight (0, 20, 40 and 60 s). Data concerning DC, FS, FM, KH, and HR were submitted to one-way ANOVA, while the consistency data was submitted to 2-way ANOVA; mean values were then compared (Tukey's test; α=0.05). The KH, FS and FM analyses showed no significant difference among the composites tested. For DC, C0 showed the highest mean value (74.2%) and differed only from C0.5 (67.2%). For HR, C0.5 showed the lowest mean (13.09%) value and differed from C0 (26.4%) and C0.01 (24.87). The consistency analysis showed no difference among C0.05, C0.1 and C0.5, considering 0 and 20 s of light exposure, while C0 (14.07 mm), C0.01 (13.97 mm), and C0.025 (14.18 mm) showed higher mean values at 0 s when compared to 20 s (12.67, 12.77 and 13.05 mm, respectivelly). Polymerization occurred within 40 s of light exposure for C0, C0.01, C0.025, and C0.05 and within 60 s for C0.1. In conclusion, the BHT concentrations had no significant influence on FS, FM and KH. The higher the BHT concentration, the longer was its handling time under light, with a significant improvement in the HR, but a decrease in DC. Therefore, BHT at 0.1% showed the best outcomes concerning all the BHT concentrations tested.

Effect of Incorporation of Bioactive Glass-Ceramic into Self-etch Adhesives.

PURPOSE: This study evaluated the effect of incorporating different concentrations of biosilicate in an experimental self-etch adhesive (SE). MATERIALS AND METHODS: Biosilicate microparticles (0, 2, 5, and 10 wt%) were incorporated into the primer, and degree of conversion (DC) and wettability were tested (one-way ANOVA, Tukey's test, p < 0.05). The two best concentrations were selected (2% and 5%) for µTBS evaluation. Sound human molars (n=20) were sectioned into quarters and randomly assigned to 4 experimental groups: 1. experimental SE + 0% biosilicate (Exp0%; negative control); 2. experimental SE + 2% biosilicate (Exp2%); 3. experimental SE + 5% biosilicate (Exp5%); 4. AdheSE (Ivoclar Vivadent, positive control). After adhesive application, Filtek Z350 (3M Oral Care) composite was built up incrementally to 5 mm. Each quarter tooth was sectioned into sticks (0.9 mm2) and stored in distilled water (37°C) for 24 h, 6 months, or 1 year. After storage, sticks were submitted to µTBS (0.75 mm/min). The Ca:P ratio was analyzed using scanning electron microscopy (SEM) and energy-dispersive x-ray spectroscopy (EDS). Data were analyzed using two-way ANOVA with Bonferroni's correction, with statistical siginificance set at p < 0.05. Fracture patterns were observed under a digital microscope and adhesive interfaces with transmission electron microscopy (TEM). RESULTS: Exp2% presented the highest DC (p < 0.05), Exp5% exhibited the lowest µTBS (p < 0.05), and adhesive failures were predominant in all groups. TEM suggested remineralized areas in Exp2% and to a lesser degree in Exp5%. Exp2% and Exp5% showed a higher Ca:P ratio after aging (p < 0.05). CONCLUSION: The incorporation of biosilicate microparticles can improve the properties of self-etch adhesives. It increased the DC of the experimental adhesive as well as mineral deposition. However, the adhesive properties are concentration dependent, as a higher concentration of microparticles can adversely affect the mechanical properties of an adhesive.

Effect of an elastomeric urethane monomer on BisGMA-free resin composites containing different co-initiators.

OBJECTIVES: The aim of this study was to investigate the mechanical, chemical, optical, and adhesive properties of BisGMA-free experimental resin composites containing Exothane-24-an elastomeric urethane monomer-and different co-initiators. MATERIALS AND METHODS: A blend of urethane dimethacrylate (UDMA), extended dimethacrylate urethane (PEG 400), triethylene glycol dimethacrylate (TEGDMA), and camphorquinone was prepared. Two different co-initiators-dimethyl aminoethyl methacrylate (DMAEMA) or 4-N alcohol, N-dimethylamine phenylethyl (DMPOH)-were added to the blend. Exothane-24 monomer was added to the blend for each co-initiator and four groups were established as follows: DMAEMA; DMAEMA + Exothane; DMPOH; and DMPOH + Exothane. Specimens were photo-activated using a multi-wave LED light-curing unit (VALO; 954 mW/cm2 of irradiance). Mechanical (ultimate tensile strength, flexural strength, flexural modulus and hardness), chemical (degree of conversion, hardness reduction, water sorption and solubility), optical (color change), and adhesive (microtensile bond strength) properties were analyzed. Data were submitted to two-way ANOVA and Tukey's test (α = 0.05). RESULTS: The resin composite containing DMPOH and Exothane-24 showed similar or superior performance to those of the other experimental composites for mechanical and chemical properties, except for flexural strength. It also showed less color change and greater micro-tensile bond strength. CONCLUSIONS: Among the combinations tested, the BisGMA-free resin composite containing Exothane-24 combined with the DMPOH co-initiator showed the best mechanical, chemical, optical, and adhesive properties. Clinical relevance Exothane-24 monomer and DMPOH co-initiator could be useful in the formulation of BisGMA-free resin composites in order to minimize exposure to BPA.

Clinical decision-making in anterior resin composite restorations: a multicenter evaluation.

OBJECTIVE: This study investigated whether a sample of anterior resin composite restorations could be differently evaluated in different centers of evaluation by clinical and lay evaluators. METHODS: Anterior resin composite restorations on high-quality intraoral digital photography were evaluated using FDI criteria (1-5 score) by pairs of clinical and lay evaluators in Brazil (BR), France (FR), Peru (PE), and the United States of America (USA). Scores were allocated as maintenance (1, 2, 3), repair (4) and replacement (5) when comparing clinical evaluators and, as acceptable (1, 2, 3) and unacceptable (4, 5) when comparing clinical vs. lay evaluators and lay vs. lay evaluators. The Chi-square test compared the frequencies of scores among the centers. RESULTS: The frequencies of maintaining, repairing, or replacing anterior resin composite restorations given by clinical evaluators varied depending on the evaluation center. BR and PE showed the highest frequencies for repair and replacement, while FR and USA showed the highest frequencies for maintenance. The comparison of frequencies of anterior resin composite restorations accepted or unaccepted by the clinical vs lay evaluators in the same centers showed a significantly higher frequency of acceptable dental restorations coming from clinical evaluators. Comparison between lay evaluators from different centers showed significant higher frequency of unacceptable dental restorations by BR, compared to other centers. CONCLUSIONS: In the evaluation of anterior resin composite restorations, the maintenance, repair, or replacement trends can vary among different centers. The unacceptable rate came more frequently from lay than from clinical evaluators. Lay evaluators from different centers differed significantly. CLINICAL SIGNIFICANCE: Clinical and lay evaluators in distant evaluation centers can present different trends when assessing anterior resin composite restoration. Multicenter evaluations can help to understand such differences and it is important because clinical decision-making based on scientific evidence comes from clinical studies done in different research centers.

Incorporation of Arginine to Commercial Orthodontic Light-Cured Resin Cements-Physical, Adhesive, and Antibacterial Properties.

(1) Background: The amino acid arginine is now receiving great attention due to its potential anti-caries benefits. The purpose of this in vitro study was to evaluate the shear bond strength (SBS), ultimate tensile strength (UTS), and antimicrobial potential (CFU) of two arginine-containing orthodontic resin cements. (2) Methods: Forty bovine incisors were separated into four groups (n = 10): Orthocem, Orthocem + arginine (2.5 wt%), Transbond XT, and Transbond XT + arginine (2.5 wt%). The brackets were fixed to the flat surface of the enamel, and after 24 h the SBS was evaluated using the universal testing machine (Instron). For the UTS test, hourglass samples (n = 10) were made and tested in a mini-testing machine (OM-100, Odeme). For the antibacterial test (colony forming unit-CFU), six cement discs from each group were made and exposed to Streptococcus mutans UA159 biofilm for 7 days. The microbiological experiment was performed by serial and triplicate dilutions. The data from each test were statistically analyzed using a two-way ANOVA, followed by Tukey's test (α = 0.05). (3) Results: The enamel SBS mean values of Transbond XT were statistically higher than those of Orthocem, both with and without arginine (p = 0.02033). There was no significant difference in the SBS mean values between the orthodontic resin cements, either with or without arginine (p = 0.29869). The UTS of the Transbond XT was statistically higher than the Orthocem, but the addition of arginine at 2.5 wt% did not influence the UTS for either resin cement. The Orthocem + arginine orthodontic resin cement was able to significantly reduce S. mutans growth, but no difference was observed for the Transbond XT (p = 0.03439). (4) Conclusion: The incorporation of arginine to commercial orthodontic resin cements may be an efficient preventive strategy to reduce bacterial growth without compromising their adhesive and mechanical properties.

Electric current effects on bond strength, nanoleakage, degree of conversion and dentinal infiltration of adhesive systems.

To evaluate the effect of three adhesive systems applied under electric current on microtensile bond strength (µTBS) and degree of conversion (DC). Molar teeth were restored with the aid of three adhesive systems (Adper Single Bond 2-SB2; Clearfil SE Bond-CSE; and Single Bond Universal-SBU) under different electric current intensities (0 µA; 25 µA; and 50 µA). Composite resin blocks were built up in increments (2 mm) and sectioned into 1 × 1 mm beams. The µTBS was tested after 24 h and 1 y distilled water storages. Samples (n = 10) from 24 h to 1 y storages were immersed in a 50% ammoniacal silver nitrate solution and submitted to scanning electron microscopy. The silver nitrate in the hybrid layer was quantified (ImageJ software). The adhesive systems' dentinal infiltration was analyzed using confocal laser scanning microscopy. Fourier transform near infrared spectroscopy was used to measure the DC. The µTBS data were submitted to two-way ANOVA (time vs. electric current) and Bonferroni's test (α = 0.05). Quantitative nanoleakage data were submitted to two-way ANOVA (electric current vs. adhesive) and Bonferroni's test (α = 0.05). DC data were submitted to one-way ANOVA and Tukey's test (α = 0.05) for each adhesive system. The electric current statistically increased the µTBS for SB2 and CSE in 24 h storage, as well as for SB2, CSE and SBU in 1 y storage. No significant difference was observed between storage time for CSE and SBU. When compared to the control, electric currents (25 µA and 50 µA) showed significantly higher DC mean values for SB2 and SBU, and had no effect on CSE. The electric currents (25 µA and 50 µA) reduced the adhesive system's nanoleakage after 1-year storage, and improved the infiltration of SB2 and CSE. Both electric current intensities improved dentinal interface stability.

The ability of a nanobioglass-doped self-etching adhesive to re-mineralize and bond to artificially demineralized dentin.

OBJECTIVE: To a self-etch adhesive doped with nano-bioglass and evaluate its ability to bond and re-mineralize artificially demineralized dentin. METHODS: Experimental Si, Ca, Na and PO4 based nanobioglass particles were synthesized, doped into experimental self-etch adhesives, and divided into 3 groups: Clearfi SE2 (CSE2), experimental (EXC), and experimental doped with 10% of nanobioglass (ExNB). The adhesives were applied onto the caries-affected dentin (chemically simulated), and evaluated after 24 h and 28 days of immersion in simulated body fluid. The remineralization process was assessed using optical coherence tomography, nanoindentation, in situ zymography, transmission electron microscopy, confocal laser scanning microscopy, µ-tensile bond strength, and pH buffer. RESULTS: The addition of nanobioglass particles into the experimental self-etch adhesives altered the µTBS in the short-term jeopardizing dentin bonding properties, when compared to the non-doped self-etch adhesive. The remineralization recovered the nanohardness, and volume lost by caries lesion (p = 0.02). Moreover, reduced the enzymatic activity (p = 1.24E-4) and formed new crystals within of the hybrid layer. CONCLUSION: The use of nanobioglass was efficient to recover the properties of a caries affected dentin. Furthermore, the adhesive properties were not hampered and the probabilistic reliability increased.

Bonding performance and mechanical properties of flowable bulk-fill and traditional composites in high c-factor cavity models.

OBJECTIVES: The aim of this study is to evaluate bond strength (BS), shrinkage stress (SS), flexural strength (FS), and elastic modulus (E) of three flowable bulk fill in comparison with conventional composites. MATERIALS AND METHODS: Three bulk fill (Filtek Bulk Fill Flow, Surefil SDR, X-tra Base) and three conventional composites (Filtek Z250 XT, Grandioso, Dentsply TPH3) were used. For BS, conical cavities (n = 10) were prepared in bovine dentine and restored with materials and were analyzed through push-out test in a universal testing machine (UTM). For FS/EM, 60 (n = 10) bar specimens (7 mm × 2 mm × 1 mm) were prepared and evaluated with a UTM. SS was measured in UTM coupled to an extensometer (n = 5). The data were statistically evaluated using one-way ANOVA/Tukey tests (P < 0.05). RESULTS: Conventional composites showed higher E when compared to bulk-fill composites. Regarding FS, they showed similar results, except for (XBF) Xtra Bulk Fill that was inferior. SS and BS of bulk-fill composites were significantly lower and higher than conventional composites, respectively, except for XBF, which showed similar BS to conventional ones. CONCLUSIONS: Flowable bulk-fill composites, except XBF, showed higher BS, lower SS, similar FS, and lower E when compared to conventional ones.

Chlorhexidine-modified nanotubes and their effects on the polymerization and bonding performance of a dental adhesive.

OBJECTIVES: The purpose of this study was to synthesize chlorhexidine (CHX)-encapsulated aluminosilicate clay nanotubes (Halloysite®, HNTs) and to incorporate them into the primer/adhesive components of an etch-and-rinse adhesive system (SBMP; Scotchbond Multipurpose, 3M ESPE) and to test their effects on degree of conversion, viscosity, immediate and long-term bonding to dentin. METHODS: CHX-modified HNTs were synthesized using 10% or 20% CHX solutions. The primer and the adhesive components of SBMP were incorporated with 15wt.% of the CHX-encapsulated HNTs. Degree of conversion (DC) and viscosity analyses were performed to characterize the modified primers/adhesives. For bond strength testing, acid-etched dentin was treated with one of the following: SBMP (control); 0.2%CHX solution before SBMP; CHX-modified primers+SBMP adhesive; SBMP primer+CHX-modified adhesives; and SBMP primer+CHX-free HNT-modified adhesive. The microtensile bond strength test was performed after immediate (24h) and long-term (6 months) of water storage. Data were analyzed using ANOVA and Tukey (α=5%) and the Weibull analysis. RESULTS: DC was greater for the CHX-free HNT-modified adhesive, whereas the other experimental adhesives showed similar DC as compared with the control. Primers were less viscous than the adhesives, without significant differences within the respective materials. At 24h, all groups showed similar bonding performance and structural reliability; whereas at the 6-month period, groups treated with the 0.2%CHX solution prior bonding or with the CHX-modified primers resulted in greater bond strength than the control and superior reliability. SIGNIFICANCE: The modification of a primer or adhesive with CHX-encapsulated HNTs was an advantageous approach that did not impair the polymerization, viscosity and bonding performance of the materials, showing a promising long-term effect on resin-dentin bonds.

Influence of Pre-Heating Regular Resin Composites and Flowable Composites on Luting Ceramic Veneers with Different Thicknesses.

The aim of this study was to evaluate of pre-heating, filler contents and ceramic thickness on film thickness, microshear bond strength, degree of conversion and color change on ceramic veneers. Two experimental composites were prepared (Bis-GMA/UDMA/BisEMA/ TEGDMA), with different amounts of filler (65% or 50%wt) simulating a conventional and a flowable composite. The flowable (F) was used at room temperature and, the conventional either at room temperature (C) or pre-heated (CPH). Disk-shaped ceramics with different thickness (0.4 mm, 0.8 mm, 1.5 mm) were prepared. The film thickness was evaluated according to the ISO 4049 (n=10). The microshear bond strength (n=10) was evaluated in enamel using tubing specimens light-cured through the ceramic veneer. The degree of conversion was evaluated using Raman spectroscopy. The color change of the ceramic restorations (n=10) was evaluated by spectrophotometry. The results were submitted to 2-way ANOVA and Tukey's post hoc test (a=5%). For the film thickness 1-way ANOVA was used (a=5%). The C presented the thicker film thickness; the CPH produced a similar film thickness in comparison to the F. All composites showed similar microshear bond strength. The degree of conversion of the F was higher than the C and CPH. The degree of conversion of the composites photo-activated through a 0.4 mm was higher than the composites photo-activated through thicker ceramics. The C showed the highest color change, while the CPH showed similar color change to the F. In conclusion, pre-heated conventional composites seem to be a potential alternative to lute ceramic veneers such as the flowable composites.