Magnetic Nanocomposite Materials Based on Fe3O4 Nanoparticles with Iron and Silica Glycerolates Shell: Synthesis and Characterization.

Novel magnetic nanocomposite materials based on Fe3O4 nanoparticles coated with iron and silica glycerolates (MNP@Fe(III)Glyc and MNP@Fe(III)/SiGlyc) were obtained. The synthesized nanocomposites were characterized using TEM, XRD, TGA, VMS, Mössbauer and IR spectroscopy. The amount of iron and silica glycerolates in the nanocomposites was calculated from the Mössbauer spectroscopy, ICP AES and C,H-elemental analysis. Thus, it has been shown that the distribution of Fe in the shell and core for MNP@Fe(III)Glyc and MNP@Fe(III)/SiGlyc is 27:73 and 32:68, respectively. The synthesized nanocomposites had high specific magnetization values and a high magnetic response to the alternating magnetic field. The hydrolysis of shells based on Fe(III)Glyc and Fe(III)/SiGlyc in aqueous media has been studied. It has been demonstrated that, while the iron glycerolates shell of MNP@Fe(III)Glyc is resistant to hydrolysis, the silica glycerolates shell of MNP@Fe(III)/SiGlyc is rather labile and hydrolyzed by 76.4% in 24 h at 25 °C. The synthesized materials did not show cytotoxicity in in vitro experiments (MTT-assay). The data obtained can be used in the design of materials for controlled-release drug delivery.

Coagulation removal of nickel (II) ions by ferric chloride: Efficiency and mechanism.

Removal of heavy metal ions, in particular, divalent nickel ions from natural and wastewater, is of great importance for the environment. Nickel (II) ions are very toxic and provoke many diseases. The purpose of this work was to study the possibility of removing toxic nickel (II) ions from polluted water using an iron (III) chloride (FeCl3) coagulant. It is shown that the removal of nickel ions from aqueous solution by iron (III) hydroxide precipitate formed during the coagulation process at pH 7 and 8 is described with satisfactory accuracy by the classical adsorption isotherms of Freundlich, Langmuir, and Dubinin-Radushkevich. The studies performed with the use of X-ray powder diffraction and thermal analyses, IR, Raman, and Mössbauer spectroscopy have shown that the uptake of nickel ions by iron (III) hydroxide precipitate is due to simple physical adsorption and is not accompanied by the formation of mixed iron and nickel compounds. No alloying of the formed iron (III) hydroxide precipitate with nickel ions takes place either. The formed iron (III) hydroxide precipitate is a two-line ferrihydrite having the gross formula Fe2 O3 × 3H2 O. Its sorption capacity for nickel ions is almost an order of magnitude higher than that of some mineral and carbon sorbents, and at pH 7 and 8, it is 60.5 and 141.9 mg/g, respectively. PRACTITIONER POINTS: Coagulant FeCl3 cleans contaminated solutions from Ni(II) ions. Iron (III) hydroxide precipitated at pH 7 and 8 is a two-line ferrihydrite Fe2 O3  × 3H2 O. Removing of Ni(II) ions is described by classical adsorption isotherms. The most complete removal of Ni(II) ions occurs at pH = 8.

Individual iron(iii) glycerolate: synthesis and characterisation.

Iron(ii) and iron(iii) salts of strong acids form iron glycerolates on heating at 180 °C with glycerol in the presence of an equivalent amount of alkali. Individual iron(iii) glycerolate was obtained for the first time. When Fe3O4 magnetic nanoparticles were heated with glycerol, an iron(iii) glycerolate shell was formed on their surface.