RESUMO
OBJECTIVES: The aim of this study was to evaluate and compare the retentive strength of orthodontic bands cemented with amorphous calcium phosphate (ACP)-containing and conventional glass ionomer cements (GICs). MATERIALS AND METHODS: One-hundred-and-twenty mandibular third molars were embedded in acrylic resin blocks with the buccal surface of crowns perpendicular to the base of the mold. The teeth were randomly divided into four groups containing 30 teeth each. Groups 1 and 3 were cemented using conventional GIC and groups 2 and 4 were cemented using ACP-containing orthodontic cement. Groups 1 and 2 without thermocycling, and groups 3 and 4 after thermocycling (5000 cycles, 5° to 55°C) were tested for retentive strength using a universal testing machine (crosshead speed of 1mm/minute). Two-way ANOVA was performed to compare the retentive strength of the groups. RESULTS: The highest retentive strength belonged to group 1, and it was significantly higher than that of group 2 (P<0.001) and group 3 (P=0.02). The mean strength for group 2 was significantly lower than that of group 1 (P<0.001) and group 4 (P=0.04). CONCLUSIONS: Although retentive strength decreased when ACP was added to GIC, the retentive strength of the samples cemented by ACP-containing GIC was remarkably high after thermocycling. It seems that in the oral cavity, ACP-containing GIC provides sufficient strength to endure forces applied on posterior teeth.
RESUMO
BACKGROUND: Although using light-cured composites for bonding orthodontic brackets has become increasingly popular, curing light cannot penetrate the metallic bulk of brackets and polymerization of composites is limited to the edges. Limited access and poor direct sight may be a problem in the posterior teeth. Meanwhile, effectiveness of the trans-illumination technique is questionable due to increased bucco-lingual thickness of the posterior teeth. Light-emitting diode (LED) light-curing units cause less temperature rise and lower risk to the pulpal tissue. The purpose of this study was to evaluate the clinical effectiveness of trans-illumination technique in bonding metallic brackets to premolars, using different light intensities and curing times of an LED light-curing unit. METHODS: Sixty premolars were randomly divided into six groups. Bonding of brackets was done with 40- and 80-s light curing from the buccal or lingual aspect with different intensities. Shear bond strengths of brackets were measured using a universal testing machine. Data were analyzed by one-way analysis of variance test and Duncan's post hoc test. RESULTS: The highest shear bond belonged to group 2 (high intensity, 40 s, buccal) and the lowest belonged to group 3 (low intensity, 40 s, lingual). Bond strength means in control groups were significantly higher than those in experimental groups. CONCLUSIONS: In all experimental groups except group 6 (80 s, high intensity, lingual), shear bond strength was below the clinically accepted values. In clinical limitations where light curing from the same side of the bracket is not possible, doubling the curing time and increasing the light intensity during trans-illumination are recommended for achieving acceptable bond strengths.