RESUMO
OBJECTIVE: White spot lesion (WSL) is one of the most important complications of fixed orthodontic treatment. Many methods have been studied to prevent this problem. This study is aimed to investigate the effect of high concentration nano-hydroxyapatite (nHAP) on shear bond strength (SBS) of metal brackets and Adhesive Remnant Index (ARI) score in different preparation methods. MATERIAL AND METHODS: Sixty human premolars, which were extracted for orthodontic reasons were included in this in vitro study. The teeth were randomly divided into 4 groups of 15 each: one control group and three nHAP groups. After applying nHAP for 2 to 3 minutes daily for 10 days, the groups 2 to 4 underwent sandblasting using 50µm aluminium oxide and 30 seconds etching, 60 and 30 seconds etching, respectively, and the brackets were then bonded to the teeth. After debonding, SBS and ARI scores were recorded. Data were analysed using the ANOVA test and posthoc test for pairwise comparisons. RESULTS: No significant difference was observed in SBS between the control group and the nHAP groups. The sandblasted teeth showed significantly higher SBS than the 30 seconds etching after nHAP application (P=0.02). The teeth etched for 60 seconds showed a significantly higher ARI score than the 30 seconds etched teeth with (P=0.003) or without (P<0.001) nHAP application. CONCLUSIONS: The use of nHAP before bracket bonding can be considered as a caries preventive method since it did not compromise the SBS. Sixty seconds etching is recommended for less likely damage to the enamel after debonding.