Starch hydrogels: The influence of the amylose content and gelatinization method.

Gelatinization and retrogradation, influenced by amylose and amylopectin ratio, are important characteristics for starch hydrogels elaboration. The objective of this study was to evaluate the influence of amylose content and the gelatinization method on the physicochemical characteristics of native and cross-linked rice starch hydrogels. The native and cross-linked starches were gelatinized with heating or alkaline solution, added polyvinyl alcohol, frozen and then freeze-dried. The cross-linked starch had a low final viscosity (101.38 RVU), which made the heat-induced gelatinized hydrogel readily disintegrated in water. However, modified starch hydrogels obtained by alkaline-induced gelatinization resulted in a more rigid structure than the native starch hydrogels. In addition, the starch sample with high amylose content had lower water absorption (322.2%) due to the greater stiffness of the hydrogel structure that resisted swelling. The alkaline-gelatinization resulted in stiffer hydrogels with lower water absorption (322.2 to 534.8%), while the heat-gelatinized behaved as a superabsorbent (658.7 to 1068.5%). The variability of the hydrogels properties of this study can enable a range of applications due to different amylose contents and gelatinization methods.

Impact of acid and oxidative modifications, single or dual, of sorghum starch on biodegradable films.

The objective of this study was to evaluate the effects of acid and oxidation modifications on sorghum starch, as well as the effect of dual modification of starch on the physical, morphological, mechanical, and barrier properties of biodegradable films. The acid modification was performed with 3% lactic acid and the oxidation was performed with 1.5% active chlorine. For dual modification, the acid modification was performed first, followed by oxidation under the same conditions as above. Both films of the oxidized starches, single and dual, had increased stiffness, providing a higher tensile strength and lower elongation when compared to films based on native and single acid modified starches. However, the dual modification increased the water vapor permeability of the films without changing their solubility. The increase in sorghum starch concentration in the filmogenic solution increased the thickness, water vapor permeability, and elongation of the films.