Edge-On (Cellulose II) and Face-On (Cellulose I) Adsorption of Cellulose Nanocrystals at the Oil-Water Interface: A Combined Entropic and Enthalpic Process.

Nanocelluloses can be used to stabilize oil-water surfaces, forming so-called Pickering emulsions. In this work, we compare the organization of native and mercerized cellulose nanocrystals (CNC-I and CNC-II) adsorbed on the surface of hexadecane droplets dispersed in water at different CNC concentrations. Both types of CNCs have an elongated particle morphology and form a layer strongly adsorbed at the interface. However, while the layer thickness formed with CNC-I is independent of the concentration at 7 nm, CNC-II forms a layer ranging from 9 to 14 nm thick with increasing concentration, as determined using small-angle neutron scattering with contrast-matched experiments. Molecular dynamics (MD) simulations showed a preferred interacting crystallographic plane for both crystalline allomorphs that exposes the CH groups (100 and 010) and is therefore considered hydrophobic. Furthermore, this study suggests that whatever the allomorph, the migration of CNCs to the oil-water interface is spontaneous and irreversible and is driven by both enthalpic and entropic processes.

Selective radical depolymerization of cellulose to glucose induced by high frequency ultrasound.

The depolymerization of cellulose to glucose is a challenging reaction and often constitutes a scientific obstacle in the synthesis of downstream bio-based products. Here, we show that cellulose can be selectively depolymerized to glucose by ultrasonic irradiation in water at a high frequency (525 kHz). The concept of this work is based on the generation of H˙ and ˙OH radicals, formed by homolytic dissociation of water inside the cavitation bubbles, which induce the cleavage of the glycosidic bonds. The transfer of radicals on the cellulose particle surfaces prevents the side degradation of released glucose into the bulk solution, allowing maintaining the selectivity to glucose close to 100%. This work is distinguished from previous technologies in that (i) no catalyst is needed, (ii) no external source of heating is required, and (iii) the complete depolymerization of cellulose is achieved in a selective fashion. The addition of specific radical scavengers coupled to different gaseous atmospheres and ˙OH radical dosimetry experiments suggested that H˙ radicals are more likely to be responsible for the depolymerisation of cellulose.