RESUMO
The complete atomic structure of a five-monolayer film of LaAlO3 on SrTiO3 has been determined for the first time by surface x-ray diffraction in conjunction with the coherent Bragg rod analysis phase-retrieval method and further structural refinement. Cationic mixing at the interface results in dilatory distortions and the formation of metallic La(1-x)SrxTiO3. By invoking electrostatic potential minimization, the ratio of Ti{4+}/Ti{3+} across the interface was determined, from which the lattice dilation could be quantitatively explained using ionic radii considerations. The correctness of this model is supported by density functional theory calculations. Thus, the formation of a quasi-two-dimensional electron gas in this system is explained, based on structural considerations.
RESUMO
We report the first complete determination, using surface x-ray diffraction, of the surface structure of TiO2-terminated SrTiO3(001), both at room temperature in vacuum, and also hot, under typical conditions used for thin film growth. The cold structure consists of a mixture of a (1x1) relaxation and (2x1) and (2x2) reconstructions. The latter disappear over several minutes upon heating. The structures are best modeled by a TiO2-rich surface similar to that proposed by Erdman et al. [Nature (London) 419, 55 (2002).10.1038/nature01010]. Both reconstructions have been shown by density functional theory to be energetically favorable. The calculated (1x1) surface energy is higher, indicating that it may be a disordered mixture of the reconstructions. Atomic displacements are significant down to three unit cells, which may have important implications on possible surface ferroelectric phenomena in SrTiO3.
RESUMO
A novel energetic smoothing mechanism in the growth of complex metal-oxide thin films is reported from in situ kinetic studies of pulsed laser deposition of on , using x-ray reflectivity. Below 50% monolayer coverage, prompt insertion of energetic impinging species into small-diameter islands causes them to break up to form daughter islands. This smoothing mechanism therefore inhibits the formation of large-diameter 2D islands and the seeding of 3D growth. Above 50% coverage, islands begin to coalesce and their breakup is thereby suppressed. The energy of the incident flux is instead rechanneled into enhanced surface diffusion, which leads to an increase in the effective surface temperature of DeltaT approximately 500 K. These results have important implications on optimal conditions for nanoscale device fabrication using these materials.
RESUMO
The use of an area detector in grazing-incidence X-ray experiments lends many advantages in terms of both speed and reliability. Here a discussion is given of the procedures established using the PILATUS pixel detector developed at the Swiss Light Source for optimizing data acquisition and analysis of surface diffraction data at the Materials Science beamline, especially with regard to reflectivity measurements, crystal truncation and fractional order rods, and grazing-incidence diffraction experiments.