Microleakage assessment of CAD-CAM Cobalt-Chrome and Zirconia abutments on a conical connection dental implant: A comparative in vitro study.

OBJECTIVE: To assess the marginal and bacterial microleakage in zirconia and CAD-CAM or cast Co-Cr implant abutments. METHODS: Sixty-four conical connection implants with their respective abutments were divided into four groups (Co-Cr (milled, laser-sintered, and cast) and Zirconia (milled)). All specimens were subjected to a chewing simulation and thermocycling. After aging process, specimens were submerged in a 0.2% methylene blue solution with Porphyromonas gingivalis (P.g) for 48 h. The marginal microleakage was measured using a 40× optical microscopy at the internal part of the implant, and when positive microleakage was observed, a DNA isolation with a polymerase chain reaction (PCR) test was used. The microbiological assessment was based on colony forming units (CFUs). RESULTS: Thirty (47%) implant-abutments presented microleakage and the PCR was performed on those specimens (1 Zirconia, 1 Co-Cr milled, 14 Co-Cr laser-sintered and 14 cast). Seven specimens (1 Co-Cr laser-sintered and six cast) presented values below the PCR detection limit (< 100 CFUs). The lowest CFUs count occurred in the Co-Cr milled group (5.17E+02 CFUs/ml) followed by zirconia (7.70E+03 CFUs/ml). The Co-Cr cast (9.39E+03 CFUs/ml) and laser-sintered (2.4E+05 CFUs/ml) groups had higher bacterial count. The CFU count comparison performed between Co-Cr cast and laser-sintered resulted in a statistically significant differences in favor of Co-CrCL (p < .05). CONCLUSIONS: The abutment material and fabrication technique affected the implant-abutment microleakage. Although the CAD-CAM abutments presented favorable results, all tested groups presented microleakage.

Survival rates of a lithium disilicate-based core ceramic for three-unit esthetic fixed partial dentures: a 10-year prospective study.

PURPOSE: The aim of this prospective study was to evaluate the clinical efficacy and long-term survival rate of three-unit fixed partial dentures (FPDs) made from lithium disilicate-based core ceramic. MATERIALS AND METHODS: Twenty-one three-unit FPDs were placed in 19 patients to replace single lost teeth in the esthetic area, following a study protocol that took clinical, esthetic, and radiologic aspects into consideration. Each case was reviewed at 1 week following placement, at 6 months, and then annually for 10 years. Statistical analysis was performed using Kaplan-Meier survival analysis. RESULTS: Out of the 19 patients, 14.3% presented reversible postoperative sensitivity. Recession was observed in 24% of dental posts, and 7.1% presented marginal discoloration. Treatment did not increase either Bleeding or Plaque Index scores at prepared teeth; secondary caries did not appear either. The restorations' survival rate at the 10-year follow-up was 71.4%; six FPDs had fractured and one debonded. CONCLUSIONS: Fracture failure rate was 28.6% after 10 years; a high percentage corresponded to connector fractures and occurred during the first 5 years. Lithium disilicate glass-ceramic FPDs present a higher risk of fracture than standard therapies (metal-ceramic) or other more recently developed ceramic materials. The prognosis for survival improves for Class I occlusion and nonparafunctional patients.