Inactivation of Bacteriophage ɸ6 and SARS-CoV-2 in Antimicrobial Surface Tests.

Due to the COVID-19 pandemic, researchers have focused on new preventive measures to limit the spread of SARS-CoV-2. One promising application is the usage of antimicrobial materials on often-touched surfaces to reduce the load of infectious virus particles. Since tests with in vitro-propagated SARS-CoV-2 require biosafety level 3 (BSL-3) laboratories with limited capacities and high costs, experiments with an appropriate surrogate like the bacteriophage ɸ6 are preferred in most studies. The aim of this study was to compare ɸ6 and SARS-CoV-2 within antiviral surface tests. Different concentrations of copper coatings on polyethylene terephthalate (PET) were used to determine their neutralizing activity against ɸ6 and SARS-CoV-2. The incubation on the different specimens led to similar inactivation of both SARS-CoV-2 and ɸ6. After 24 h, no infectious virus particles were evident on any of the tested samples. Shorter incubation periods on specimens with high copper concentrations also showed a complete inactivation. In contrast, the uncoated PET foils resulted only in a negligible reduced inactivation during the one-hour incubation. The similar reduction rate for ɸ6 and SARS-CoV-2 in our experiments provide further evidence that the bacteriophage ɸ6 is an adequate model organism for SARS-CoV-2 for this type of testing.

Antimicrobial Activity of a Novel Cu(NO3)2-Containing Sol-Gel Surface under Different Testing Conditions.

In this study, assessment of the antimicrobial activity of a novel, plasma-cured 2.5% (w/v) Cu(NO3)2-containing sol-gel surface was performed. In contrast to state-of-the-art sol-gel coatings, the plasma curing led to a gradient in cross-linking with the highest values at the top of the coating. As a result, the coating behaved simultaneously hard, scratch-resistant, and tough, the latter due to the more flexible bulk of the coating toward the substrate. Further, the diffusion and permeation through the coating also increased toward the substrate. In our study, tests according to ISO 22196 showed antibacterial activity of the 2.5% (w/v) Cu(NO3)2-containing sol-gel surface against all bacterial strains tested, and we expanded the testing further using a "dry" evaluation without an aqueous contact phase, which confirmed the antimicrobial efficacy of the 2.5% (w/v) Cu(NO3)2-containing sol-gel surface. However, further investigation under exposure to soiling with the addition of 0.3% albumin, used to simulate organic load, led to a significant impairment in the antibacterial effect under both tested conditions. Furthermore, re-testing of the surface after disinfection with 70% ethanol led to a total loss of antibacterial activity. Our results showed that besides the mere application of an antimicrobial agent to a surface coating, it is also necessary to consider the future use of these surfaces in the experimental phase combining industry and science. Therefore, a number of tests corresponding to the utilization of the surface should be obligative on the basis of this assessment.