Transition metal dichalcogenide heterobilayers feature strong moiré potentials with multiple local minima, which can spatially trap interlayer excitons at different locations within one moiré unit cell (dubbed moiré locales). However, current studies mainly focus on moiré excitons trapped at a single moiré locale. Exploring interlayer excitons trapped at different moiré locales is highly desirable for building polarized light-emitter arrays and studying multiorbital correlated and topological physics. Here, via enhancing the interlayer coupling and engineering the heterointerface, we report the observation and modulation of high-temperature interlayer excitons trapped at separate moiré locales in WS2/WSe2 heterobilayers. These moiré-locale excitons are identified by two emission peaks with an energy separation of â¼60 meV, exhibiting opposite circular polarizations due to their distinct local stacking registries. With the increase of temperature, two momentum-indirect moiré-locale excitons are observed, which show a distinct strain dependence with the momentum-direct one. The emission of these moiré-locale excitons can be controlled via engineering the heterointerface with different phonon scattering, while their emission energy can be further modulated via strain engineering. Our reported highly tunable interlayer excitons provide important information on understanding moiré excitonic physics, with possible applications in building high-temperature excitonic devices.
RESUMO
Doping is an important technique for semiconductor materials and devices, yet effective and controllable doping of organic-inorganic halide perovskites is still a challenge. Here, we demonstrate a facile way to dope two-dimensional Sn-based perovskite (PEA)2SnI4 by incorporating SnI4 in the precursor solutions. It is observed that Sn4+ produces p-doping effect on the perovskite, which increases the electrical conductivity by 105 times. The dopant SnI4 is also found to improve the film morphology of (PEA)2SnI4, leading to reduced trap states. This doping technique allows us to improve the room temperature mobility of (PEA)2SnI4 field-effect transistors from 0.25 to 0.68 cm2 V-1 s-1 thanks to reduced trapping effects in the doped devices. Moreover, the doping technique enables the characterization and improvement of the thermoelectric performance of (PEA)2SnI4 films, which show a high power factor of 3.92 µW m-1 K-2 at doping ratio of 5 mol %.
RESUMO
Doping is an important technique for semiconductor materials, yet effective and controllable doping of organic-inorganic halide perovskites is still a challenge. Here, we present a protocol to dope 2D perovskite (PEA)2SnI4 by incorporating SnI4 in the precursor solutions. We detail steps for preparation of field-effect transistors (FETs) and thermoelectric devices (TEs) based on SnI4-doped (PEA)2SnI4 films. We further describe characterization via conductivity measurement using the four-point probe method, FETs performance, and TEs performance measurements. For complete details on the use and execution of this protocol, please refer to Liu et al. (2022).1.