Synthesis of novel chitosan/sodium hyaluronate/iridium hydrogel nanocomposite for wound healing application.

A novel chitosan/sodium hyaluronate/iridium (CHI/SH/Ir) hydrogel nanocomposite with a unique microstructure containing vertically aligned pores is fabricated via an electrophoresis technique. The formation of orderly vertical pores in CHI/SH/Ir hydrogel nanocomposite is due to the confinement of hydrogen bubbles produced from the water electrolysis during electrophoresis that limits their lateral movement and coalescence. In a wet state, the diameter for the vertical pores is 600-700 µm. With a thickness of 500 µm, the CHI/SH/Ir hydrogel nanocomposite exhibits a porosity of 76.7 % and a water uptake of 350 %. Its tensile strength is almost doubled to 8.7 MPa, as compared to that of counterpart without the addition of iridium. In CHI/SH/Ir hydrogel nanocomposite, the iridium nanoparticles are homogeneously distributed with an average size of 3 nm. The CHI/SH/Ir electrophoresis suspension exhibits a negligible cytotoxicity. In cell migration test using the human keratinocytes HaCaT cells, the CHI/SH/Ir hydrogel nanocomposite reveals a relative migration of 122.15 ± 9.02 % (p < 0.001) as compared to the blank sample. The presence of vertically aligned pores with the use of SH and iridium nanoparticles indicates a promising opportunity in wound healing application.

Bubble-Channeling Electrophoresis of Honeycomb-Like Chitosan Composites.

A chitosan composite with a vertical array of pore channels is fabricated via an electrophoretic deposition (EPD) technique. The composite consists of chitosan and polyethylene glycol, as well as nanoparticles of silver oxide and silver. The formation of hydrogen bubbles during EPD renders a localized increase of hydroxyl ions that engenders the precipitation of chitosan. In addition, chemical interactions among the constituents facilitate the establishment of vertical channels occupied by hydrogen bubbles that leads to the unique honeycomb-like microstructure; a composite with a porosity of 84%, channel diameter of 488 µm, and channel length of 2 mm. The chitosan composite demonstrates an impressive water uptake of 2100% and a two-stage slow release of silver. In mass transport analysis, both Disperse Red 13 and ZnO powders show a much enhanced transport rate over that of commercial gauze. Due to its excellent structural integrity and channel independence, the chitosan composite is evaluated in a passive suction mode for an adhesive force of 9.8 N (0.56 N cm-2 ). The chitosan composite is flexible and is able to maintain sufficient adhesive force toward objects with different surface curvatures.

Electrophoretic fabrication of a robust chitosan/polyethylene glycol/polydopamine composite film for UV-shielding application.

The film-forming process of chitosan composite films is an important issue because it affects their experimental design, chemicals used, and feasibility of large-scaled fabrication. In this work, electrophoresis is employed to produce chitosan composite films with significantly reduced processing time and environmentally friendly chemicals. With the addition of hydrogen peroxide and polyethylene glycol, the parasitic hydrogen bubble formation during the electrophoresis of chitosan and polydopamine is effectively inhibited that leads to the formation of a defectless chitosan/polyethylene glycol/polydopamine composite film which could be removed from the substrate readily. In addition, the chitosan/polyethylene glycol/polydopamine composite film reveals significantly improved tensile strength and a slower decomposition rate as compared to those of chitosan film and chitosan/polyethylene glycol composite film. This is attributed to the strong interaction between chitosan and polydopamine. Lastly, the chitosan/polyethylene glycol/polydopamine composite film exhibits excellent UV-shielding ability without compromising its visible transparency.

Lenvatinib Inhibits AKT/NF-κB Signaling and Induces Apoptosis Through Extrinsic/Intrinsic Pathways in Non-small Cell Lung Cancer.

BACKGROUND/AIM: Non-small cell lung cancer (NSCLC) is a serious disease and the leading cause of death globally. Overexpression of protein kinase B/nuclear factor-kappa B (NF-κB) signaling transduction of NSCLC cells was recognized as a potential therapeutic target. Lenvatinib is a multiple kinase inhibitor against vascular endothelial growth factor receptor family. However, whether lenvatinib may affect AKT/NF-κB in NSCLC remains unknown. MATERIALS AND METHODS: MTT assay, NF-κB reporter gene assay, flow cytometry, tranwell migration/invasion analysis and western blotting were used to identify the alteration of cell viability, NF-κB activation, apoptosis effect, migration/invasion potential and AKT/NF-κB related protein expression, respectively, in CL-1-5-F4 cells after lenvatinib treatment. RESULTS: The cell viability and NF-κB activity were suppressed by lenvatinib. Extrinsic and intrinsic apoptosis were activated by lenvatinib. Additionally, the metastatic potential of CL-1-5-F4 cells was also suppressed by lenvatinib. CONCLUSION: Altogether, lenvatinib induced extrinsic/intrinsic apoptosis and suppressed migration/invasion ability of NSCLC cells that was associated with AKT/NF-κB signaling inactivation.

Leveraging the water electrolysis reaction in bipolar electrophoresis to form robust and defectless chitosan films.

Electrophoresis of chitosan and its composites are widely used to form a coating on selective substrates, but the parasitic water electrolysis causes structural defects that weaken the resulting film. In this work, we demonstrate a bipolar electrophoresis technique that leverages the water electrolysis to produce a chitosan film with less porosity and surface cavities. The process involves a negative bias to deposit the protonated chitosan molecules from the solution, followed by a positive bias to remove the entrapped hydrogen bubbles via the re-protonation of chitosan deposit. Since water electrolysis occurs for both positive and negative bias, the bipolar profile is designed to engender pH changeup near the electrode for "surface conditioning" of chitosan film. The bipolar electrophoresis route demonstrates better coulomb efficiency than that of conventional potentiostatic electrophoresis, resulting in a free-standing chitosan film with sufficient mechanical strength and large area.

Associations of region-specific visceral adiposity with subclinical atrial dysfunction and outcomes of heart failure.

AIMS: Excessive visceral adiposity (VAT) plays an essential role in metabolic derangements with those close to heart further mediates myocardial homeostasis. The disparate biological links between region-specific VAT and cardiometabolic profiles as mediators influencing atrial kinetics remain unexplored. METHODS AND RESULTS: Among 1326 asymptomatic individuals, region-specific VAT including peri-aortic root fat (PARF) and total pericardial fat (PCF) of cardiac region, together with thoracic peri-aortic adipose tissue (TAT), was assessed using multiple-detector computed tomography. VAT measures were related to functional left atrial (LA) metrics assessed by speckle-tracking algorithm and clinical outcomes of atrial fibrillation (AF) and heart failure (HF). Multivariate linear regression models incorporating body fat, metabolic syndrome, and E/TDI-e' consistently demonstrated independent associations of larger PARF/PCF with peak atrial longitudinal systolic strain (PALS) reduction, higher LA stiffness, and worsened strain rate components; instead, TAT was independently associated with cardiometabolic profiles. PARF rather than PCF or TAT conferred independent prognostic values for incident AF/HF by multivariate Cox regression (adjusted hazard ratio: 1.56, 95% confidence interval: 1.17-2.08, P = 0.002) during a median of 1790 days (interquartile range: 25th to 75th: 1440-1927 days) of follow-up, with subjects categorized into worst PALS and largest VAT tertiles demonstrating highest events (all log-rank P < 0.001). Mediation analysis showed that higher triglyceride and lower high-density lipoproteins may serve as intermediary factors for effects between VAT and LA functional metrics, with lesser role by glucose level. CONCLUSIONS: Visceral adiposity surrounding atrial region was tightly associated with subclinical atrial dysfunction and incident AF or HF beyond metabolic factors. Instead, peri-aortic adiposity may mediate their toxic effects mainly through circulating cardiometabolic profiles.

Formation of Free-Standing Inverse Opals with Gradient Pores.

We demonstrate the fabrication of free-standing inverse opals with gradient pores via a combination of electrophoresis and electroplating techniques. Our processing scheme starts with the preparation of multilayer colloidal crystals by conducting sequential electrophoresis with polystyrene (PS) microspheres in different sizes (300, 600, and 1000 nm). The critical factors affecting the stacking of individual colloidal crystals are discussed and relevant electrophoresis parameters are identified so the larger PS microspheres are assembled successively atop of smaller ones in an orderly manner. In total, we construct multilayer colloidal crystals with vertical stacking of microspheres in 300/600, 300/1000, and 300/600/1000 nm sequences. The inverse opals with gradient pores are produced by galvanostatic plating of Ni, followed by the selective removal of colloidal template. Images from scanning electron microscopy exhibit ideal multilayer close-packed structures with well-defined boundaries among different layers. Results from porometer analysis reveal the size of bottlenecks consistent with those of interconnected pore channels from inverse opals of smallest PS microspheres. Mechanical properties determined by nanoindentation tests indicate significant improvements for multilayer inverse opals as compared to those of conventional single-layer inverse opals.

Use of a tolerance interval approach as a statistical quality control tool for traditional Chinese medicine.

Raw materials for traditional Chinese medicine (TCM) are often from different resources and its final product may also be made by different sites. Therefore, variabilities from different resources such as site-to-site or within site component-to-component may be expected. Consequently, test for consistency in raw materials, in-process materials, and/or final product has become an important issue in the quality control (QC) process in TCM development. In this paper, a statistical QC process for raw materials and/or the final product of TCM is proposed based on a two sided [Formula: see text]-content, [Formula: see text]-confidence tolerance interval. More specifically, we construct the tolerance interval for a random-effects model to assess the QC of TCM products from different regions and possibly different product batches. The products can be claimed to be consistency when the constructed tolerance interval is within the permitted range. Given the region and batch effects, sample sizes can also be calculated to ensure the desired measure of goodness. An example is presented to illustrate the proposed approach.

Surface-Enhanced Raman Scattering and Fluorescence on Gold Nanogratings.

Surface-enhanced Raman scattering (SERS) spectroscopy is a sensitive sensing technique. It is desirable to have an easy method to produce SERS-active substrate with reproducible and robust signals. We propose a simple method to fabricate SERS-active substrates with high structural homogeneity and signal reproducibility using electron beam (E-beam) lithography without the problematic photoresist (PR) lift-off process. The substrate was fabricated by using E-beam to define nanograting patterns on the photoresist and subsequently coat a layer of gold thin film on top of it. Efficient and stable SERS signals were observed on the substrates. In order to investigate the enhancement mechanism, we compared the signals from this substrate with those with photoresist lifted-off, which are essentially discontinuous gold stripes. While both structures showed significant grating-period-dependent fluorescence enhancement, no SERS signal was observed on the photoresist lifted-off gratings. Only transverse magnetic (TM)-polarized excitation exhibited strong enhancement, which revealed its plasmonic attribution. The fluorescence enhancement showed distinct periodic dependence for the two structures, which is due to the different enhancement mechanism. We demonstrate using this substrate for specific protein binding detection. Similar periodicity dependence was observed. Detailed theoretical and experimental studies were performed to investigate the observed phenomena. We conclude that the excitation of surface plasmon polaritons on the continuous gold thin film is essential for the stable and efficient SERS effects.

Structural characterization of colloidal crystals and inverse opals using transmission X-ray microscopy.

A nondestructive tomographic technique was used to determine the crystallographic information of colloidal crystals comprising of polystyrene (PS) microspheres, as well as their silver inverse opals. The properties of the colloidal crystals, such as defects, grain size, grain boundaries, stacking sequence, and grain orientation, were determined using the full field transmission X-ray microscopy (TXM) with a spatial resolution of 50 nm. The PS microspheres (500-750 nm) which underwent a vertical electrophoresis process to form a face-centered cubic (fcc) close-packed structure with an ABCABC packing sequence. In addition, the colloidal crystal exhibited multiple grains, and an orientation variation of 6.1° in the stacking direction between two neighboring grains.