Electronic structure of methoxy-, bromo-, and nitrobenzene grafted onto Si(111).

The properties of Si(111) surfaces grafted with benzene derivatives were investigated using ultraviolet photoemission spectroscopy (UPS) and X-ray photoelectron spectroscopy (XPS). The investigated materials were nitro-, bromo-, and methoxybenzene layers (-C(6)H(4)-X, with X = NO(2), Br, O-CH(3)) deposited from diazonium salt solutions in a potentiostatic electrochemical process. The UPS spectra of the valence band region are governed by the molecular orbital density of states of the adsorbates, which is modified from the isolated state in the gas phase due to molecule-molecule and molecule-substrate interaction. Depending on the adsorbate, clearly different emission features are observed. The analysis of XPS intensities clearly proves multilayer formation for bromo- and nitrobenzene in agreement with the amount of charge transferred during the grafting process. Methoxybenzene forms only a sub-monolayer coverage. The detailed analysis of binding energy shifts of the XPS emissions for determining the band bending and the secondary electron onset in UPS spectra for determining the work function allow one to discriminate between surface dipole layers--changing the electron affinity--and band bending, affecting only the work function. Thus, complete energy band diagrams of the grafted Si(111) surfaces can be constructed. It was found that silicon surface engineering can be accomplished by the electrochemical grafting process using nitrobenzene and bromobenzene: silicon-derived interface gap states are chemically passivated, and the adsorbate-related surface dipole effects an increase of the electron affinity.

Synchrotron photoemission analysis of semiconductor/electrolyte interfaces by the frozen-electrolyte approach: interaction of HCl in 2-propanol with GaAs(100).

Perspectives of a new approach for the synchrotron photoemission spectroscopic analysis of chemical processes at solid/liquid interfaces under UHV conditions have been explored. A thin layer of HCl-2-propanol solution was frozen-in on the semiconductor GaAs(100) wafer surface by cooling the substrate to liquid nitrogen temperature after etching off the native oxide layer under N2 atmosphere. Chemical reactions induced in situ by exposure to synchrotron radiation (SR) and by stepwise heating have been monitored. Right after etching and freezing, the surface is covered by gallium chlorides with 1, 2, 3, and 4 Cl ions attached and lattice back-bonded to As atoms, as well as by elemental arsenic As0 and 2-propanol. Exposure to SR at low temperature produces surface As chlorides at the expense of As0. The GaCl3 and GaCl2 emissions diminish while GaCl is enhanced. On the other hand, heating the sample to approximately 130 K just above H2O desorption causes the thermodynamically expected reaction of AsCl3 with the substrate GaAs to form Ga chloride species and As0. Heating the sample to room temperature leaves only As0 on the surface and for gallium the content of all surface chlorides is drastically reduced. By further heating to 400 K elemental arsenic starts to desorb and the Ga chloride surface content is reduced. Using different excitation energies the depth composition of the reaction products has been monitored indicating a tendency of decreasing chlorination numbers and increasing Ga vs As chloride content toward the pristine substrate at each stage of the reaction.