Erratum: Elshazli et al. Laser Surface Modification of TC21 (α/ß) Titanium Alloy Using a Direct Energy Deposition (DED) Process. Micromachines 2021, 12, 739.

In the original article [...].

Laser Surface Modification of TC21 (α/ß) Titanium Alloy Using a Direct Energy Deposition (DED) Process.

The TC21 alloy (Ti-6Al-3Mo-1.9Nb-2.2Sn-2.2Zr-1.5Cr) is considered a new titanium alloy that replaced the commercial Ti-6Al-4V alloy in aerospace applications due to its higher operating temperatures. Recently, direct energy deposition was usually applied to enhance the hardness, tribological properties, and corrosion resistance for many alloys. Consequently, this study was performed by utilizing direct energy deposition (DED) on TC21 (α/ß) titanium alloy to improve their mechanical properties by depositing a mixture powder of stellite-6 (Co-based alloy) and tungsten carbides particles (WC). Different WC percentages were applied to the surfaces of TC21 using a 4 kW continuous-wave fiber-coupled diode laser at a constant powder feeding rate. This study aimed to obtain a uniform distribution of hard surfaces containing undissolved WC particles that were dispersed in a Co-based alloy matrix to enhance the wear resistance of such alloys. Scanning electron microscopy, energy dispersive X-ray analysis (EDAX), and X-ray diffractometry (XRD) were used to characterize the deposited layers. New constituents and intermetallic compounds were found in the deposited layers. The microhardness was measured for all deposited layers and wear resistance was evaluated at room temperature using a dry sliding ball during a disk abrasion test. The results showed that the microstructure of the deposited layer consisted of a hypereutectic structure and undissolved tungsten carbide dispersed in the matrix of the Co-based alloy that depended on the WC weight fraction. The microhardness values increased with increasing WC weight fraction in the deposited powder by more than threefold as compared with the as-cast samples. A notable enhancement of wear resistance of the deposited layers was thus achieved.

Laser Powder Cladding of Ti-6Al-4V α/ß Alloy.

Laser cladding process was performed on a commercial Ti-6Al-4V (α + ß) titanium alloy by means of tungsten carbide-nickel based alloy powder blend. Nd:YAG laser with a 2.2-KW continuous wave was used with coaxial jet nozzle coupled with a standard powder feeding system. Four-track deposition of a blended powder consisting of 60 wt % tungsten carbide (WC) and 40 wt % NiCrBSi was successfully made on the alloy. The high content of the hard WC particles is intended to enhance the abrasion resistance of the titanium alloy. The goal was to create a uniform distribution of hard WC particles that is crack-free and nonporous to enhance the wear resistance of such alloy. This was achieved by changing the laser cladding parameters to reach the optimum conditions for favorable mechanical properties. The laser cladding samples were subjected to thorough microstructure examinations, microhardness and abrasion tests. Phase identification was obtained by X-ray diffraction (XRD). The obtained results revealed that the best clad layers were achieved at a specific heat input value of 59.5 J·mm-2. An increase by more than three folds in the microhardness values of the clad layers was achieved and the wear resistance was improved by values reaching 400 times.