Neutron-mapping polymer flow: scattering, flow visualization, and molecular theory.

Flows of complex fluids need to be understood at both macroscopic and molecular scales, because it is the macroscopic response that controls the fluid behavior, but the molecular scale that ultimately gives rise to rheological and solid-state properties. Here the flow field of an entangled polymer melt through an extended contraction, typical of many polymer processes, is imaged optically and by small-angle neutron scattering. The dual-probe technique samples both the macroscopic stress field in the flow and the microscopic configuration of the polymer molecules at selected points. The results are compared with a recent "tube model" molecular theory of entangled melt flow that is able to calculate both the stress and the single-chain structure factor from first principles. The combined action of the three fundamental entangled processes of reptation, contour length fluctuation, and convective constraint release is essential to account quantitatively for the rich rheological behavior. The multiscale approach unearths a new feature: Orientation at the length scale of the entire chain decays considerably more slowly than at the smaller entanglement length.

Film thickness effects on the distribution of high-molecular-weight heterotelechelic polymers.

High-molecular-weight heterotelechelic deuteriopolystyrene, NDPSF, possessing an amine functional group at one end of the chain and a fluorocarbon group at the other was tethered to a silicon substrate by its amine functional group. These layers were coated with an unfunctionalised polystyrene matrix, HPS, such that the total film thickness covered a range from 2.2 to 9 times the radius of gyration of NDPSF. The detailed distribution of the polymers after annealing for times much greater than the reptation period of either of the components, was obtained using neutron reflectometry. No evidence for bridging of the two interfaces was found for the thicker films, but the finite concentration of the NDPSF polymer observed for the thinnest films may be due to bridging since the energy gain of the fluorocarbon end is just greater than the loss due to configurational entropy losses. A linear increase in the ellipsometric thickness of the excess of NDPSF at the substrate was discovered and we attribute this to the NDPSF slowly being leached out of the layer initially at the substrate followed by diffusion into the bulk of the film. The concentration profiles obtained are consistent with hindered relaxation of the large NDPSF molecules, when they are tethered at the substrate or at the vacuum surface.