Effect of Composition and Surface Microstructure in Self-Polarized Ferroelectric Polymer Films on the Magnitude of the Surface Potential.

The values of the surface potentials of two sides of films of polyvinylidene fluoride, and its copolymers with tetrafluoroethylene and hexafluoropropylene, were measured by the Kelvin probe method. The microstructures of the chains in the surfaces on these sides were evaluated by ATR IR spectroscopy. It was found that the observed surface potentials differed in the studied films. Simultaneously, it was observed from the IR spectroscopy data that the microstructures of the chains on both sides of the films also differed. It is concluded that the formation of the surface potential in (self-polarized) ferroelectric polymers is controlled by the microstructure of the surface layer. The reasons for the formation of a different microstructure on both sides of the films are suggested on the basis of the general regularities of structure formation in flexible-chain crystallizing polymers.

Optical and Electrophysical Properties of Vinylidene Fluoride/Hexafluoropropylene Ferroelectric Copolymer Films: Effect of Doping with Porphyrin Derivatives.

Polymer films doped by different porphyrins, obtained by crystallization from the acetone solutions, differ in absorption and fluorescence spectra, which we attribute to the differences in the structuring and composition of the rotational isomers in the polymer chains. According to the infrared spectroscopy data, the crystallization of the films doped with tetraphenylporphyrin (TPP) proceeds in a mixture of α- and γ-phases with TGTG- and T3GT3G- conformations, respectively. Three bonds in the planar zigzag conformation ensures the contact of such segments with the active groups of the porphyrin macrocycle, significantly changing its electronic state. Structuring of the films in the presence of TPP leads to an increase in the low-voltage AC-conductivity and the registration of an intense Maxwell-Wagner polarization. An increased conductivity by an order of magnitude in TPP-doped films was also observed at high-voltage polarization. The introduction of TPP during the film formation promotes the displacement of the chemical attachment defects of "head-to-head" type in the monomeric units into the surface. This process is accompanied by a significant increase in the film surface roughness, which was registered by piezo-force microscopy. The latter method also revealed the appearance of hysteresis phenomena during the local piezoelectric coefficient d33 measurements.

Boosting Magnetoelectric Effect in Polymer-Based Nanocomposites.

Polymer-based magnetoelectric composite materials have attracted a lot of attention due to their high potential in various types of applications as magnetic field sensors, energy harvesting, and biomedical devices. Current researches are focused on the increase in the efficiency of magnetoelectric transformation. In this work, a new strategy of arrangement of clusters of magnetic nanoparticles by an external magnetic field in PVDF and PFVD-TrFE matrixes is proposed to increase the voltage coefficient (αME) of the magnetoelectric effect. Another strategy is the use of 3-component composites through the inclusion of piezoelectric BaTiO3 particles. Developed strategies allow us to increase the αME value from ~5 mV/cm·Oe for the composite of randomly distributed CoFe2O4 nanoparticles in PVDF matrix to ~18.5 mV/cm·Oe for a composite of magnetic particles in PVDF-TrFE matrix with 5%wt of piezoelectric particles. The applicability of such materials as bioactive surface is demonstrated on neural crest stem cell cultures.