Highly Electron-Doped TaON Single-Crystal Growth by a High-Pressure Flux Method.

Transition-metal oxynitrides have a variety of functions such as visible light-responsive catalysts and dielectric materials, but acquiring single crystals necessary to understand inherent properties is difficult and is limited to relatively small sizes (<10 µm) because they easily decompose at high temperatures. Here, we have succeeded in growing platelet single crystals of TaON with a typical size of 50 × 100 × 10 µm3 under a high pressure and high temperature (6 GPa and 1400 °C) using a LiCl flux. Such a harsh condition, in contrast to powder samples synthesized under mild conditions, resulted in the introduction of a large amount of oxygen vacancies (x = 0.06 in TaO1-xN) into the crystal, providing a metallic behavior with a large anisotropy of ρc/ρab ∼ 103. Low-temperature oxygen annealing allows for a single-crystal-to-single-crystal transformation to obtain fully oxidized TaON (yellow) crystals. Needle-like crystals can be obtained when NH4Cl is used as a flux. Furthermore, black Hf2ON2 single crystals are also grown, suggesting that the high-pressure flux method is widely applicable to other transition-metal oxynitrides, with extensive carrier control.

Spin Frustration in Double Perovskite Oxides and Oxynitrides: Enhanced Frustration in La2MnTaO5N with a Large Octahedral Rotation.

The B-site sublattice in the double perovskite oxides A2BB'O6 (B: magnetic cation; B': nonmagnetic cation) causes spin frustration, but the relationship between the structure and spin frustration remains unclear although a number of compounds have been studied. The present study systematically investigated A2MnIIB'O6 (S = 5/2) and found that the frustration factor, defined by f = |θW|/TN (θW: Weiss temperature; TN: Néel temperature), scales linearly with the tolerance factor t, i.e., octahedral rotation. Unexpectedly, La2MnTaO5N (space group: P21/n) synthesized under high pressure is more frustrated (f = 6) than oxides with similar t values, despite the large octahedral rotation due to the small t value of 0.914. Structural analysis suggests that the enhanced frustration can be attributed to the site preference of nitride anions at the equatorial positions, which reduces the variance of neighboring Mn-Mn distances. Our findings provide a new guide to control and improve spin frustration in double perovskites with multiple anions.

High-Pressure Synthesis of Non-Stoichiometric Li x WO3 (0.5 ≤ x ≤ 1.0) with LiNbO3 Structure.

Compounds with the LiNbO3-type structure are important for a variety of applications, such as piezoelectric sensors, while recent attention has been paid to magnetic and electronic properties. However, all the materials reported are stoichiometric. This work reports on the high-pressure synthesis of lithium tungsten bronze Li x WO3 with the LiNbO3-type structure, with a substantial non-stoichiometry (0.5 ≤ x ≤ 1). Li0.8WO3 exhibit a metallic conductivity. This phase is related to an ambient-pressure perovskite phase (0 ≤ x ≤ 0.5) by the octahedral tilting switching between a-a-a- and a+a+a+.