Introduction: The patient satisfaction questionnaires in literature are according to the community pharmacies services in the authors' countries and not all have psychometric reports to support the results. We designed a questionnaire specific to the services of community pharmacies in Romania to evaluate the level of patient satisfaction. Methods: We carried out a cross-sectional study on voluntary patients. The questionnaire consisted of 22 items, grouped into three domains corresponding to patient satisfaction with pharmacies, pharmaceutical staff and medication availability, and four subdomains related to pharmaceutical staff skills. The 5-point Likert scale was used. Statistical analysis was done in SPSS 27.0. Results: The Cronbach's Alpha was 0.861. The Inter-rater Agreement was 72.0%, the Item Content Validity was 97.6% and the completeness index was 100%. The factor analysis indicated 6 factors (Eigen values >1.0). The 809 patients had a median of overall satisfaction score of 3.77; the median was 4.0 regarding satisfaction score with pharmaceutical staff skills. Respondents characteristics varied the patient's satisfaction level (p ≤ 0.05). Conclusions: The reliability and validity of the questionnaire have been demonstrated. Overall patient satisfaction with community pharmacy services had a moderate level, but the attitude and confidence in the pharmacist had a high level of satisfaction.

Investigations on the Degradation Behavior of Processed FeMnSi-xCu Shape Memory Alloys.

A new functional Fe-30Mn-5Si-xCu (x = 1.5 and 2 wt%) biomaterial was obtained from the levitation induction melting process and evaluated as a biodegradable material. The degradation characteristics were assessed in vitro using immersion tests in simulated body fluid (SBF) at 37 ± 1 °C, evaluating mass loss, pH variation that occurred in the solution, open circuit potential (OCP), linear and cyclic potentiometry (LP and CP), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and nano-FTIR. To obtain plates as samples, the cast materials were thermo-mechanically processed by hot rolling. Dynamic mechanical analysis (DMA) was employed to evaluate the thermal properties of the smart material. Atomic force microscopy (AFM) was used to show the nanometric and microstructural changes during the hot rolling process and DMA solicitations. The type of corrosion identified was generalized corrosion, and over the first 3-5 days, an increase in mass was observed, caused by the compounds formed at the metal-solution interface. The formed compounds were identified mainly as oxides that passed into the immersion liquid. The degradation rate (DR) was obtained as a function of mass loss, sample surface area and immersion duration. The dynamic mechanical behavior and dimensions of the sample were evaluated after 14 days of immersion. The nanocompounds found on the surface after atmospheric corrosion and immersion in SBF were investigated with the Neaspec system using the nano-FTIR technique.