RESUMO
Fluorescence correlation spectroscopy was used to show that the temperature-dependent diffusion coefficient of poly(ethylene oxide) (PEO) adsorbed on polystyrene and different poly(alkyl methacrylate) (PAMA) films in aqueous solution exhibited a maximum close to (but below) the surface glass transition temperature, Tgs, of the film. This elevated diffusion was observed over a small range of temperatures below Tgs for these surfaces, and at other temperatures, the diffusion was similar to that on silicon, although the diffusion coefficient for PEO on polystyrene at temperatures above Tgs did not completely decrease to that on silicon, in contrast to the PAMA surfaces. It is concluded that the enhanced surface mobility of the films near the surface glass transition temperature induces conformational changes in the adsorbed PEO. The origin of this narrow and dramatic increase in diffusion coefficient is not clear, but it is proposed that it is caused by a coupling of a dominant capillary mode in the liquid surface layer with the polymer. Friction force microscopy experiments also demonstrate an unexpected increase in friction at the same temperature as the increase in diffusion coefficient.
RESUMO
Collagen-based scaffolds are extensively used in biomaterials and tissue engineering applications. These scaffolds have shown great biocompatibility and versatility, but their relatively low mechanical properties may limit use in orthopaedic load-bearing applications. Moreover, terminal sterilization with gamma irradiation, as is commonly performed with commercial devices, presents concerns over structural integrity and enzymatic stability. Therefore, the goal of this study was to test the hypothesis that EDC/NHS cross-linking (10 mM/5 mM) can protect collagen-hyaluronan sponges from the damaging effects of gamma irradiation. Specifically, we evaluated compressive and tensile mechanical properties, enzymatic stability, porosity and pore size, and swelling ratio. Ultimate tensile strength and elastic modulus exhibited increases (168.5 and 245.8%, respectively) following irradiation, and exhibited over tenfold increases (1049.2 and 1270.6%, respectively) following cross-linking. Irradiation affected pore size (38.4% decrease), but cross-linking prior to irradiation resulted in only a 17.8% decrease. Cross-linking also showed an offsetting effect on the equilibrium modulus, enzymatic stability, and swelling ratio of sponges. These results suggest that carbodiimide cross-linking of collagen-hyaluronan sponges can mitigate the structural damage typically experienced during gamma irradiation, warranting their use in tissue engineering applications.