Mapping Temperature Heterogeneities during Catalytic CO2 Methanation with Operando Luminescence Thermometry.

Controlling and understanding reaction temperature variations in catalytic processes are crucial for assessing the performance of a catalyst material. Local temperature measurements are challenging, however. Luminescence thermometry is a promising remote-sensing tool, but it is cross-sensitive to the optical properties of a sample and other external parameters. In this work, we measure spatial variations in the local temperature on the micrometer length scale during carbon dioxide (CO2) methanation over a TiO2-supported Ni catalyst and link them to variations in catalytic performance. We extract local temperatures from the temperature-dependent emission of Y2O3:Nd3+ particles, which are mixed with the CO2 methanation catalyst. Scanning, where a near-infrared laser locally excites the emitting Nd3+ ions, produces a temperature map with a micrometer pixel size. We first designed the Y2O3:Nd3+ particles for optimal temperature precision and characterized cross-sensitivity of the measured signal to parameters other than temperature, such as light absorption by the blackened sample due to coke deposition at elevated temperatures. Introducing reaction gases causes a local temperature increase of the catalyst of on average 6-25 K, increasing with the reactor set temperature in the range of 550-640 K. Pixel-to-pixel variations in the temperature increase show a standard deviation of up to 1.5 K, which are attributed to local variations in the catalytic reaction rate. Mapping and understanding such temperature variations are crucial for the optimization of overall catalyst performance on the nano- and macroscopic scale.

Sub-Second Time-Resolved Surface-Enhanced Raman Spectroscopy Reveals Dynamic CO Intermediates during Electrochemical CO2 Reduction on Copper.

The electrocatalytic carbon dioxide (CO2 ) reduction reaction (CO2 RR) into hydrocarbons is a promising approach for greenhouse gas mitigation, but many details of this dynamic reaction remain elusive. Here, time-resolved surface-enhanced Raman spectroscopy (TR-SERS) is employed to successfully monitor the dynamics of CO2 RR intermediates and Cu surfaces with sub-second time resolution. Anodic treatment at 1.55 V vs. RHE and subsequent surface oxide reduction (below -0.4 V vs. RHE) induced roughening of the Cu electrode surface, which resulted in hotspots for TR-SERS, enhanced time resolution (down to ≈0.7 s) and fourfold improved CO2 RR efficiency toward ethylene. With TR-SERS, the initial restructuring of the Cu surface was followed (<7 s), after which a stable surface surrounded by increased local alkalinity was formed. Our measurements revealed that a highly dynamic CO intermediate, with a characteristic vibration below 2060 cm-1 , is related to C-C coupling and ethylene production (-0.9 V vs. RHE), whereas lower cathodic bias (-0.7 V vs. RHE) resulted in gaseous CO production from isolated and static CO surface species with a distinct vibration at 2092 cm-1 .