Characteristics Analysis of Plasticized Polyvinyl Chloride Gel-Based Microlens at Different Temperatures.

Temperature plays a crucial role in the preparation of polyvinyl chloride (PVC) gels for optical applications. Incorrect temperature selection can lead to various issues such as poor surface roughness, inadequate light transmission, and insufficient solution for optical devices. To address this challenge, this study focuses on the preparation of PVC gel samples by combining PVC powder (n = 3000), eco-friendly dibutyl adipate, and tetrahydrofuran at different stirring temperatures ranging from 40 to 70 °C. The PVC gel preparation process is categorized into four groups (T40, T50, T60, and T70) based on the mixing temperatures, employing a controlled test method with specific temperature conditions. The prepared PVC gel samples are then subjected to analysis to evaluate various properties including surface morphology, tensile strength, light transmittance, and electrical response time. Among the samples, the PVC gel prepared at 60 °C (referred to as T60) exhibits excellent optical properties, with a transmittance of 91.2% and a tensile strength of 2.07 MPa. These results indicate that 60 °C is an optimal reaction temperature. Notably, the PVC gel microlenses produced at this temperature achieve their maximum focal length (ranging from -8 to -20 mm) within approximately 60 s, and they recover their initial state within around 80 s after the power is switched off. This focal length achievement is twice as fast as reported in previous studies on microlenses. It is observed that the reaction temperature significantly influences the solubility of the resin-based raw materials and the homogeneity of the gel. Consequently, these findings open up possibilities for utilizing PVC gel microlenses in novel commercial optics applications, thanks to their desirable properties.

Analysis of the Performance of a Gel Actuator Made of Plasticized Polyvinyl Chloride/Carboxylated Cellulose Nanocrystals.

Recently, polyvinyl chloride (PVC) gel materials appeared promising for developing actuators, artificial muscles, and sensors. However, their energized response time and recovery limitations restrict their broader applications. Herein, a novel soft composite gel was prepared by mixing functionalized carboxylated cellulose nanocrystals (CCNs) and plasticized PVC. The surface morphology of the plasticized PVC/CCNs composite gel was characterized by scanning electronic microscopy (SEM). The prepared PVC/CCNs gel composites have increased polarity and electrical actuation with a fast response time. Experimental results demonstrated good response characteristics within the actuator model with a multilayer electrode structure when stimulated with a specified DC voltage (1000 V), with deformation of approximately 36.7%. Moreover, this PVC/CCNs gel has excellent tensile elongation, and the elongation at break of the PVC/CCNs gel is greater than the elongation at break of the pure PVC gel under the same thickness conditions. However, these PVC/CCNs composite gels showed excellent properties and development potential and are directed for broad applications in actuators, soft-robotics, and biomedical applications.