Retention performance of alumina porous layer open-tubular column coated with γ-alumina nanoparticles in the highly volatile hydrocarbons separation.

An alumina porous layer open-tubular (Al2O3 PLOT) column coated with γ-alumina nanoparticles (20 nm) for highly volatile hydrocarbons (C1 to C5) separation was described. Relative to the coating of bulk alumina, this column was easily coated with dynamic method under 0.4 or 0.6 MPa for 0.53 mm or 0.32 mm capillary, respectively. And the thickness of coating layer could be tuned by repeating the coating process after column was dried and activated at 300 °C for 3 h. The effect of deactivation agents on the physicochemical properties of nano γ-alumina was characterized by X-ray diffraction (XRD) measurement and nitrogen adsorption-desorption isotherms. The influences of deactivation agents, film thickness, conditioning and column dimensions on the inertness, polarity, selectivity and elution order of C1 to C5 separation were investigated in detail. The crystallite structure and size of nano alumina were not affected by the deactivation agents and remained constant during the column making processes, whereas specific surface area, pore volume and average half pore width altered significantly. The specific surface area decreased to 125.4 m2 g-1 or 174.0 m2 g-1 and the average half pore size distributions decreased to 1.6-8.4 nm or 2.4-14.3 nm when it was deactivated with potassium chloride or sodium sulfate solution, respectively. The deactivation agents and its concentrations impacted significantly on the retention performance of column. The column deactivated with sodium sulfate solution exhibited stronger polarity and lower selectivity than which deactivated with potassium chloride solution although both columns showed good inertness. The length, internal diameter and film thickness of the column had less influence on the selectivity and resolution for C1 to C5 hydrocarbons separation, whereas the conditioning temperature and time had an obvious influence. The column had distinguished polarity and selectivity which was different from either bulk or commercial alumina columns. Typically, the hydrocarbons were baseline separated with resolutions ranging from 1.65 to 15.33 within 9 min under programmed temperature below 100 °C, and the tailing factors ranging from 1.02 to 1.07.

Oxidized multiwalled carbon nanotubes coated fibers for headspace solid-phase microextraction of amphetamine-type stimulants in human urine.

Carbon nanotubes (CNTs) have attracted a lot of attention as effective sorbents due to their strong sorption properties and several potential applications in many fields. In this work, the acid oxidized multiwalled carbon nanotubes (MWCNTs-COOH) was coated onto a stainless steel wire by a simple physical adhesion approach to develop solid-phase microextraction (SPME) fibers. By combination of the MWCNTs-COOH coated fiber-based headspace SPME and gas chromatography-mass spectrometry (GC-MS), the developed method demonstrates a good enhancement factor (288-651), low limits of detection (LODs, 0.2-1.3µg/L) for determination of amphetamine-type stimulant drugs (ATSs) in urine samples. The recoveries of the spiked ATSs (5, 50 and 500µg/L) were in the range of 88-107%, the calibration curve was linear for concentrations of analytes in the range from 0.5 to 1000µg/L (R=0.963-0.999). Furthermore, single fiber repeatability and fiber-to-fiber reproducibility were in the range of 2.3%-6.2% (n=6) and 5.7%-9.8% (n=3), respectively. The MWCNTs-COOH coated fiber is highly thermally stable and can be used over 150 times. The method was successfully applied to the forensic determination of amphetamine (AMP) and methamphetamine (MAMP) in human urine samples and satisfactory results were achieved.