Unveiling the Antifouling Performance of Different Marine Surfaces and Their Effect on the Development and Structure of Cyanobacterial Biofilms.

Since biofilm formation by microfoulers significantly contributes to the fouling process, it is important to evaluate the performance of marine surfaces to prevent biofilm formation, as well as understand their interactions with microfoulers and how these affect biofilm development and structure. In this study, the long-term performance of five surface materials-glass, perspex, polystyrene, epoxy-coated glass, and a silicone hydrogel coating-in inhibiting biofilm formation by cyanobacteria was evaluated. For this purpose, cyanobacterial biofilms were developed under controlled hydrodynamic conditions typically found in marine environments, and the biofilm cell number, wet weight, chlorophyll a content, and biofilm thickness and structure were assessed after 49 days. In order to obtain more insight into the effect of surface properties on biofilm formation, they were characterized concerning their hydrophobicity and roughness. Results demonstrated that silicone hydrogel surfaces were effective in inhibiting cyanobacterial biofilm formation. In fact, biofilms formed on these surfaces showed a lower number of biofilm cells, chlorophyll a content, biofilm thickness, and percentage and size of biofilm empty spaces compared to remaining surfaces. Additionally, our results demonstrated that the surface properties, together with the features of the fouling microorganisms, have a considerable impact on marine biofouling potential.

Kinetics and Chemorheological Analysis of Cross-Linking Reactions in Humins.

Humins is a biomass-derived material, co-product of the acid-catalyzed conversion of cellulose and hemicellulose to platform chemicals. This work presents a thorough study concerning the crosslinking kinetics of humins by chemorheological analysis and model-free kinetics under isothermal and non-isothermal curing. Humins can auto-crosslink under the effect of temperature, and the reaction can be fastener when adding an acidic initiator. Thus, the effect of P-Toluenesulfonic acid monohydrate (pTSA) on the crosslinking kinetics was also studied. The dependencies of the effective activation energy (Eα-dependencies) were determined by an advanced isoconversional method and correlated with the variation of complex viscosity during curing. It is shown that humins curing involves multi-step complex reactions and that the use of an acidic initiator allows faster crosslinking at lower temperatures, involving lower Eα. The shift from chemical to diffusion control was also estimated.