Continuous drying of a protein-type drug using scaled-up fiber formation with HP-ß-CD matrix resulting in a directly compressible powder for tableting.

The goals of this work were to evaluate if high-speed electrospinning can be used as a gentle and continuous drying technology to produce protein-containing cyclodextrin-based fibers from an aqueous solution and to convert the produced protein-cyclodextrin fibers into a directly compressible powder. A 400 mL/h feeding rate was used during the electrospinning experiments, corresponding to a ~270 g/h production rate of the dried material. The produced fibers were collected in a cyclone. The fibers were found grindable without secondary drying, and the ground powder was mixed with tableting excipients and was successfully tableted by direct compression. The model protein-type drug (ß-galactosidase) remained stable during each of the processing steps (electrospinning, grinding, tableting) and after 6 months of storage at room temperature in the tablets. The obtained results demonstrate that high speed electrospinning can be a gentle alternative to traditional drying methods used for protein-type drugs, and that tablet formulation is achievable from the electrospun material prepared this way.

Scaled-Up Production and Tableting of Grindable Electrospun Fibers Containing a Protein-Type Drug.

The aims of this work were to develop a processable, electrospun formulation of a model biopharmaceutical drug, ß-galactosidase, and to demonstrate that higher production rates of biopharmaceutical-containing fibers can be achieved by using high-speed electrospinning compared to traditional electrospinning techniques. An aqueous solution of 7.6 w/w% polyvinyl alcohol, 0.6 w/w% polyethylene oxide, 9.9 w/w% mannitol, and 5.4 w/w% ß-galactosidase was successfully electrospun with a 30 mL/h feeding rate, which is about 30 times higher than the feeding rate usually attained with single-needle electrospinning. According to X-ray diffraction measurements, polyvinyl alcohol, polyethylene oxide, and ß-galactosidase were in an amorphous state in the fibers, whereas mannitol was crystalline (δ-polymorph). The presence of crystalline mannitol and the low water content enabled appropriate grinding of the fibrous sample without secondary drying. The ground powder was mixed with excipients commonly used during the preparation of pharmaceutical tablets and was successfully compressed into tablets. ß-galactosidase remained stable during each of the processing steps (electrospinning, grinding, and tableting) and after one year of storage at room temperature in the tablets. The obtained results demonstrate that high-speed electrospinning is a viable alternative to traditional biopharmaceutical drying methods, especially for heat sensitive molecules, and tablet formulation is achievable from the electrospun material prepared this way.