Temperature-Driven Transformation of the Crystal and Magnetic Structures of BiFe0.7Mn0.3O3 Ceramics.

The compound BiFe0.7Mn0.3O3 consisting at room temperature of coexistent anti-polar orthorhombic and polar rhombohedral phases has a metastable structural state, which has been studied by laboratory X-ray, synchrotron and neutron diffraction, magnetometry, differential thermal analysis, and differential scanning calorimetry. Thermal annealing of the sample at temperatures above the temperature-driven phase transition into the single phase rhombohedral structure (~700 K) causes an increase of the volume fraction of the rhombohedral phase at room temperature from ~10% up to ~30%, which is accompanied by the modification of the magnetic state, leading to strengthening of a ferromagnetic component. A strong external magnetic field (~5 T) applied to the sample notably changes its magnetic properties, as well as provides a reinforcement of the ferromagnetic component, thus leading to an interaction between two magnetic subsystems formed by the antiferromagnetic matrix with non-collinear alignment of magnetic moments and the nanoscale ferromagnetic clusters coexisting within it. The modification of the structural state and magnetic properties of the compounds and a correlation between different structural and magnetic phases are discussed focusing on the effect of thermal annealing and the impact of an external magnetic field.

Structural and Magnetic Phase Transitions in BiFe1 - xMnxO3 Solid Solution Driven by Temperature.

The crystal structure and magnetic state of the (1 − x)BiFeO3-(x)BiMnO3 solid solution has been analyzed by X-ray diffraction using lab-based and synchrotron radiation facilities, magnetization measurements, differential thermal analysis, and differential scanning calorimetry. Dopant concentration increases lead to the room-temperature structural transitions from the polar-active rhombohedral phase to the antipolar orthorhombic phase, and then to the monoclinic phase accompanied by the formation of two-phase regions consisting of the adjacent structural phases in the concentration ranges 0.25 < x1 < 0.30 and 0.50 ≤ x2 < 0.65, respectively. The accompanied changes in the magnetic structure refer to the magnetic transitions from the modulated antiferromagnetic structure to the non-colinear antiferromagnetic structure, and then to the orbitally ordered ferromagnetic structure. The compounds with a two-phase structural state at room temperature are characterized by irreversible temperature-driven structural transitions, which favor the stabilization of high-temperature structural phases. The magnetic structure of the compounds also exhibits an irreversible temperature-induced transition, resulting in an increase of the contribution from the magnetic phase associated with the high-temperature structural phase. The relationship between the structural parameters and the magnetic state of the compounds with a metastable structure is studied and discussed depending on the chemical composition and heating prehistory.

Crystal Structure and Concentration-Driven Phase Transitions in Lu(1-x)ScxFeO3 (0 ≤ x ≤ 1) Prepared by the Sol-Gel Method.

The structural state and crystal structure of Lu(1-x)ScxFeO3 (0 ≤ x ≤ 1) compounds prepared by a chemical route based on a modified sol-gel method were investigated using X-ray diffraction, Raman spectroscopy, as well as scanning electron microscopy. It was observed that chemical doping with Sc ions led to a structural phase transition from the orthorhombic structure to the hexagonal structure via a wide two-phase concentration region of 0.1 < x < 0.45. An increase in scandium content above 80 mole% led to the stabilization of the non-perovskite bixbyite phase specific for the compound ScFeO3. The concentration stability of the different structural phases, as well as grain morphology, were studied depending on the chemical composition and synthesis conditions. Based on the data obtained for the analyzed samples, a composition-dependent phase diagram was constructed.

Crystal and Magnetic Structure Transitions in BiMnO3+δ Ceramics Driven by Cation Vacancies and Temperature.

The crystal structure of BiMnO3+δ ceramics has been studied as a function of nominal oxygen excess and temperature using synchrotron and neutron powder diffraction, magnetometry and differential scanning calorimetry. Increase in oxygen excess leads to the structural transformations from the monoclinic structure (C2/c) to another monoclinic (P21/c), and then to the orthorhombic (Pnma) structure through the two-phase regions. The sequence of the structural transformations is accompanied by a modification of the orbital ordering followed by its disruption. Modification of the orbital order leads to a rearrangement of the magnetic structure of the compounds from the long-range ferromagnetic to a mixed magnetic state with antiferromagnetic clusters coexistent in a ferromagnetic matrix followed by a frustration of the long-range magnetic order. Temperature increase causes the structural transition to the nonpolar orthorhombic phase regardless of the structural state at room temperature; the orbital order is destroyed in compounds BiMnO3+δ (δ ≤ 0.14) at temperatures above 470 °C.

Mesoscopic theory of defect ordering-disordering transitions in thin oxide films.

Ordering of mobile defects in functional materials can give rise to fundamentally new phases possessing ferroic and multiferroic functionalities. Here we develop the Landau theory for strain induced ordering of defects (e.g. oxygen vacancies) in thin oxide films, considering both the ordering and wavelength of possible instabilities. Using derived analytical expressions for the energies of various defect-ordered states, we calculated and analyzed phase diagrams dependence on the film-substrate mismatch strain, concentration of defects, and Vegard coefficients. Obtained results open possibilities to create and control superstructures of ordered defects in thin oxide films by selecting the appropriate substrate and defect concentration.

A Facile Synthesis and Characterization of Highly Crystalline Submicro-Sized BiFeO3.

In this study, a highly crystalline bismuth ferrite (BFO) powder was synthesized using a novel, very simple, and cost-effective synthetic approach. It was demonstrated that the optimal annealing temperature for the preparation of highly-pure BFO is 650 °C. At lower or higher temperatures, the formation of neighboring crystal phases was observed. The thermal behavior of BFO precursor gel was investigated by thermogravimetric and differential scanning calorimetry (TG-DSC) measurements. X-ray diffraction (XRD) analysis and Mössbauer spectroscopy were employed for the investigation of structural properties. Scanning electron microscopy (SEM) was used to evaluate morphological features of the synthesized materials. The obtained powders were also characterized by magnetization measurements, which showed antiferromagnetic behavior of BFO powders.

Investigation of Local Conduction Mechanisms in Ca and Ti-Doped BiFeO3 Using Scanning Probe Microscopy Approach.

In this work we demonstrate the role of grain boundaries and domain walls in the local transport properties of n- and p-doped bismuth ferrites, including the influence of these singularities on the space charge imbalance of the energy band structure. This is mainly due to the charge accumulation at domain walls, which is recognized as the main mechanism responsible for the electrical conductivity in polar thin films and single crystals, while there is an obvious gap in the understanding of the precise mechanism of conductivity in ferroelectric ceramics. The conductivity of the Bi0.95Ca0.05Fe1-xTixO3-δ (x = 0, 0.05, 0.1; δ = (0.05 - x)/2) samples was studied using a scanning probe microscopy approach at the nanoscale level as a function of bias voltage and chemical composition. The obtained results reveal a distinct correlation between electrical properties and the type of charged defects when the anion-deficient (x = 0) compound exhibits a three order of magnitude increase in conductivity as compared with the charge-balanced (x = 0.05) and cation-deficient (x = 0.1) samples, which is well described within the band diagram representation. The data provide an approach to control the transport properties of multiferroic bismuth ferrites through aliovalent chemical substitution.

Peculiarities of the Crystal Structure Evolution of BiFeO3-BaTiO3 Ceramics across Structural Phase Transitions.

Evolution of the crystal structure of ceramics BiFeO3-BaTiO3 across the morphotropic phase boundary was analyzed using the results of macroscopic measuring techniques such as X-ray diffraction, differential scanning calorimetry, and differential thermal analysis, as well as the data obtained by local scale methods of scanning probe microscopy. The obtained results allowed to specify the concentration and temperature regions of the single phase and phase coexistent regions as well as to clarify a modification of the structural parameters across the rhombohedral-cubic phase boundary. The structural data show unexpected strengthening of structural distortion specific for the rhombohedral phase, which occurs upon dopant concentration and temperature-driven phase transitions to the cubic phase. The obtained results point to the non-monotonous character of the phase evolution, which is specific for metastable phases. The compounds with metastable structural state are characterized by enhanced sensitivity to external stimuli, which significantly expands the perspectives of their particular use.

Functional Magnetic Composites Based on Hexaferrites: Correlation of the Composition, Magnetic and High-Frequency Properties.

The paper describes preparation features of functional composites based on ferrites, such as "Ba(Fe1-xGax)12O19/epoxy," and the results of studying their systems; namely, the correlation between structure, magnetic properties and electromagnetic absorption characteristics. We demonstrated the strong mutual influence of the chemical compositions of magnetic fillers (Ba(Fe1-xGax)12O19 0.01 < x < 0.1 solid solutions), and the main magnetic (coercivity, magnetization, anisotropy field and the first anisotropy constant) and microwave (resonant frequency and amplitude) characteristics of functional composites with 30 wt.% of hexaferrite. The paper presents a correlation between the chemical compositions of composites and amplitude-frequency characteristics. Increase of Ga-content from x = 0 to 0.1 in Ba(Fe1-xGax)12O19/epoxy composites leads to increase of the resonant frequency from 51 to 54 GHz and absorption amplitude from -1.5 to -10.5 dB/mm. The ability to control the electromagnetic properties in these types of composites opens great prospects for their practical applications due to high absorption efficiency, and lower cost in comparison with pure ceramics oxides.

Ferromagnetic-like behavior of Bi0.9La0.1FeO3-KBr nanocomposites.

We studied magnetostatic response of the Bi0.9La0.1FeO3- KBr composites (BLFO-KBr) consisting of nanosized (≈100 nm) ferrite Bi0.9La0.1FeO3 (BLFO) conjugated with fine grinded ionic conducting KBr. When the fraction of KBr is rather small (less than 15 wt%) the magnetic response of the composite is very weak and similar to that observed for the BLFO (pure KBr matrix without Bi1-xLaxFeO3 has no magnetic response as anticipated). However, when the fraction of KBr increases above 15%, the magnetic response of the composite changes substantially and the field dependence of magnetization reveals ferromagnetic-like hysteresis loop with a remanent magnetization about 0.14 emu/g and coercive field about 1.8 Tesla (at room temperature). Nothing similar to the ferromagnetic-like hysteresis loop can be observed in Bi1-zLazFeO3 ceramics with z ≤ 0.15, which magnetization quasi-linearly increases with magnetic field. Different physical mechanisms were considered to explain the unusual experimental results for BLFO-KBr nanocomposites, but only those among them, which are highly sensitive to the interaction of antiferromagnetic Bi0.9La0.1FeO3 with ionic conductor KBr, can be relevant.